Search

The direct discharge of boron mud poses significant environmental hazards to soil and groundwater. Despite extensive research efforts, the reprocessing of boron mud has not yielded significant advancements. Recently, the development of magnesium cement has spurred interest in the reutilization of boron mud. However, the direct treatment of boron mud remains challenging, necessitating pre-treatment in most studies to achieve substantial results. Consequently, research on the direct incorporation of untreated boron mud is scarce. This study explores the feasibility of using uncalcined boron mud as a base material in basic magnesium sulfate cement (BMSC), composed of lightly calcined magnesia and magnesium sulfate heptahydrate. The effects of varying boron mud content on the compressive strength of the BMSC system were investigated. The results indicate that the 5·1·7 phase is the primary strength phase of BMSC. When the boron mud content is 30%, the uncalcined boron mud has a minimal impact on the formation of the 5·1·7 phase. Additionally, the 28 days compressive strength of BMSC-B30 showed a slight difference compared to the control group BMSC-C, registering at 66.7 MPa. TG-DSC analysis revealed that the presence of a small amount of boron mud inhibits the micro-expansion trend of the BMSC structure. Furthermore, XRD and SEM analyses confirmed that the addition of uncalcined boron mud does not significantly alter the phase structure of the 5·1·7 phase in BMSC. This study provides a foundational basis for the long-term development of direct boron mud treatment. [ABSTRACT FROM AUTHOR]

Triple‐negative breast cancer (TNBC) is often considered one of the most aggressive subtypes of breast cancer, characterized by a high recurrence rate and low overall survival (OS). It is notorious for posing challenges related to drug resistance. While there has been progress in TNBC research, the mechanisms underlying chemotherapy resistance in TNBC remain largely elusive. We collect single‐cell RNA sequencing (scRNA‐seq) data from five TNBC patients susceptible to chemotherapy and five resistant cases. Comprehensive analyses involving copy number variation (CNV), pseudotime trajectory, cell–cell interactions, pseudospace analysis, as well as transcription factor and functional enrichment are conducted specifically on macrophages and malignant cells. Furthermore, we performed validation experiments on clinical samples using multiplex immunofluorescence. We identified a subset of SPP1+ macrophages that secrete SPP1 signals interacting with CD44 on malignant cell surfaces, potentially activating the PDE3B pathway within malignant cells via the integrin pathway, leading to chemotherapy resistance. The abnormally enhanced SPP1 signal between macrophages and malignant cells may serve as a factor promoting chemotherapy resistance in TNBC patients. Therefore, SPP1+ macrophages could potentially serve as a therapeutic target to reduce chemotherapy resistance. [ABSTRACT FROM AUTHOR]

This study investigated the effects of lithium slag and iron tailings on the hydration mechanism of Basic Oxygen Furnace (BOF) slag cement paste with the addition of 0.06% diethanol-isopropanolamine (DEIPA). This study examined the fluidity, compressive strength, pore solution pH, and hydration products of BOF slag-based composite cementitious materials. The results showed that DEIPA facilitated the conversion from ettringite (AFt) to monosulphate (AFm) and improved the early compressive strength of the BOF slag–cement mortar. Incorporating lithium slag into the DEIPA-containing BOF slag–cement system promoted AFt formation, increased calcium-silicate-hydrate production, and enhanced the microstructure. BOF slag, lithium slag, and iron tailings exhibit synergistic effects in cement pastes. BOF slag and lithium slag provided the reactive components SiO2 and Al2O3. In the early hydration stages, the iron tailings primarily served as fillers, accelerating the system's reactions. [ABSTRACT FROM AUTHOR]

The preparation of cement-based supplementary cementitious materials is an important method for the efficient use of iron tailings and the reduction in CO2 emissions. The aim of this study is to improve the reactivity of iron tailings by mixing them with steel slag, slag, and fly ash through orthogonal tests to solve the problem that iron tailings cannot be utilised on a large scale. The compressive strength, hydration products, and microstructure of the iron tailings–cement-based supplementary cementitious materials were investigated using ICP-OES, XRD, TG, FTIR, and SEM. The results revealed that each solid waste raw material played a distinct role in the hydration reaction. In the iron tailings–cement-based supplementary cementitious materials system, steel slag provided Ca2+, OH−, and Si4+ ions, slag provided Ca2+ and Al3+ ions, fly ash contributed a significant amount of Ca2+ and Al3+ ions, and iron tailings offered more nucleation sites and some Si4+ ions for the hydration products. Moreover, there was a synergistic effect among these four materials, promoting the formation of hydration products such as ettringite, C-(A)-S-H gels, and others. When the proportion of IOTs:SS:FA:SL was 9:8:8:2, the highest 7 d compressive strength of cementitious material was 24.8 MPa. When the proportion of IOTs:SS:FA:SL was 9:6:8:4, the highest 28 d compressive strength of cementitious material was 35.0 MPa. This study provides a comprehensive solution for the utilisation of iron tailings and contributes to the high-value green utilisation of solid waste. [ABSTRACT FROM AUTHOR]

Utilizing a variety of solid wastes to prepare alkali-activated cementitious materials is one of the principal trends in the development of cementitious materials. Commonly used alkali activation precursors such as granulated blast furnace slag (GBFS) and fly ash (FA) will be less available due to resource pressures. Supply limitation is an important reason to research alternative precursors. To realize the high value-added utilization of copper–molybdenum tailings (CMTs), this study adopted the modified sodium silicate solution as an alkaline activator to activate GBFS-FA-CMTs cementitious system to prepare alkali-activated cementitious materials. The influence of CMTs content on the compressive strength of GBFS-FA-CMTs cementitious system was analyzed, and the mechanism of GBFS-FA-CMTs cementitious system was also analyzed through hydration product types, physical phase composition, and microscopic morphology. The results indicated that a paste with the incorporation of CMTs, S50F30C20 (50% GBFS, 30% FA, 20% CMTs), achieved the highest compressive strength of 79.14 MPa, which was due to the filling effect of the CMTs and the degree of participation in the reaction. Pastes with different contents of CMTs, while maintaining a constant CBFS content, exhibited similar strength development. Excessive amounts of CMTs could result in reduced compressive strength. Microstructural analysis revealed that the hydration products were structurally altered by the addition of CMTs. In addition to ettringite, quartz, C(-N)-S-H gel, and calcite, gaylussite was also formed; moreover, the mass of chemically bound water increased, and the microstructure of reaction products became denser. An excess of CMTs may restrict the growth of the hydration gel, leading to more microstructural defects. The study suggests that CMTs could enhance the compressive strength of hardened paste within an alkali-activated slag-fly ash system, possibly due to a filling effect and participation in the chemical reaction. This research confirms the feasibility of using CMTs in alkali-activated cementitious materials. [ABSTRACT FROM AUTHOR]

The primary aim of this study was to conduct a methodical examination and assessment of the prognostic efficacy exhibited by magnetic resonance imaging (MRI)-derived radiomic models concerning the preoperative prediction of lymph-vascular space infiltration (LVSI) in cervical cancer cases. A comprehensive and thorough exploration of pertinent academic literature was undertaken by two investigators, employing the resources of the Embase, PubMed, Web of Science, and Cochrane Library databases. The scope of this research was bounded by a publication cutoff date of May 15, 2023. The inclusion criteria encompassed studies that utilized radiomic models based on MRI to prognosticate the accuracy of preoperative LVSI estimation in instances of cervical cancer. The Diagnostic Accuracy Studies-2 framework and the Radiomic Quality Score metric were employed. This investigation included nine distinct research studies, enrolling a total of 1,406 patients. The diagnostic performance metrics of MRI-based radiomic models in the prediction of preoperative LVSI among cervical cancer patients were determined as follows: sensitivity of 83% (95% confidence interval [CI]=77%-87%), specificity of 74% (95% CI=69%-79%), and a corresponding AUC of summary receiver operating characteristic measuring 0.86 (95% CI=0.82-0.88). The results of the synthesized meta-analysis did not reveal substantial heterogeneity.This meta-analysis suggests the robust diagnostic proficiency of the MRI-based radiomic model in the prognostication of preoperative LVSI within the cohort of cervical cancer patients. In the future, radiomics holds the potential to emerge as a widely applicable noninvasive modality for the early detection of LVSI in the context of cervical cancer., Competing Interests: No potential conflict of interest relevant to this article was reported., (© 2025. Asian Society of Gynecologic Oncology, Korean Society of Gynecologic Oncology, and Japan Society of Gynecologic Oncology.)