Search

In this study, the localized corrosion susceptibility of AA2050‐T84, AA2198‐T851, and AA2024‐T3 alloys was compared by immersion in three test solutions, specifically sodium chloride solution (3.5% NaCl), EXCO solution, according to ASTM G34‐18, and a solution for intergranular corrosion (IGC) test recommended by ASTM G110‐15 and via scanning vibrating electrode technique (SVET). The results showed higher susceptibility of AA2050‐T84 alloy to all types of corrosion tested compared to the other studied 2XXX series alloys. Corrosion penetration was deeper in the AA2050‐T84 due to its microstructural characteristics as a difference in the micrometric Cu‐Rich intermetallic particle distribution on the surface and related to the distribution of the T1 (Al2CuLi) phase. [ABSTRACT FROM AUTHOR]

This study evaluated two distinct cryo-fracturing techniques using liquid nitrogen (LN2). The evaluation included tests for peak compression strength, acoustic emission, and energy absorption. The experiments compared single-exposure freezing time (FT) and multiple-exposure freezing–thawing cycle (FTC) processes on dried specimens. The outcomes indicated that FTC experiments demonstrated lower uniaxial compression stress (UCS) values compared to FT experiments because, during the thawing phase, the ice inside the pores reverts to liquid as the temperature rises. The difference between average baseline experiments versus FT180 and FTC6 indicated a reduction in stress of 14.5% and 38.5%, respectively. The standard error of our experiments ranged from 0.58% for FT60 to 5.35% for FTC6. The damage factor follows a downward trend in both FT and FTC experiments as the time of LN2 treatment augments. The amount of energy that can be absorbed in elastic or plastic deformation before failure is less for FTC specimens with the same total LN2 exposure time. Samples undergoing the freezing time process demonstrate a greater and denser quantity of acoustic emissions in comparison to freezing–thawing cycle processes, suggesting a positive correlation with uniaxial compressive strength outcomes. The large network of fractures formed by the FTC and PFTC techniques indicated that they have the greatest potential as stimulation approaches. The engineering results were improved by adding the geological context, which is essential to apply these findings to coals that have comparable origins. [ABSTRACT FROM AUTHOR]

Updated understanding on the effect of biofouling on corrosion rate is needed to protect marine structures as climate change is altering seawater physiochemistry and biofouling organism distribution. Multi-disciplinary techniques can improve understanding of biofouling development and associated corrosion rates on metals immersed in natural seawater (NSW). In this study, the development of biofouling and corrosion on welded Nickel Aluminium Bronze (NAB) was investigated through long-term immersion tests in NSW, simulated seawater (SSW) and air. Biofouling was affected by geographic location within the marina and influenced corrosion extent. The corrosion rate of NAB was accelerated in the initial months of exposure in NSW (1.27 mm.yr−1) and then settled to 0.11 mm.yr−1 (annual average). This was significantly higher than the 0.06 mm.yr−1 corrosion rate measured in SSW, which matched published rates. The results suggest that corrosion rates for cast NAB should be revised to take account of biofouling and updated seawater physiochemistry. [ABSTRACT FROM AUTHOR]

This study evaluated two distinct cryo-fracturing techniques using liquid nitrogen (LN2). The evaluation included tests for peak compression strength, acoustic emission, and energy absorption. The experiments compared single-exposure freezing time (FT) and multiple-exposure freezing–thawing cycle (FTC) processes on dried specimens. The outcomes indicated that FTC experiments demonstrated lower uniaxial compression stress (UCS) values compared to FT experiments because, during the thawing phase, the ice inside the pores reverts to liquid as the temperature rises. The difference between average baseline experiments versus FT180 and FTC6 indicated a reduction in stress of 14.5% and 38.5%, respectively. The standard error of our experiments ranged from 0.58% for FT60 to 5.35% for FTC6. The damage factor follows a downward trend in both FT and FTC experiments as the time of LN2 treatment augments. The amount of energy that can be absorbed in elastic or plastic deformation before failure is less for FTC specimens with the same total LN2 exposure time. Samples undergoing the freezing time process demonstrate a greater and denser quantity of acoustic emissions in comparison to freezing–thawing cycle processes, suggesting a positive correlation with uniaxial compressive strength outcomes. The large network of fractures formed by the FTC and PFTC techniques indicated that they have the greatest potential as stimulation approaches. The engineering results were improved by adding the geological context, which is essential to apply these findings to coals that have comparable origins.