Lithium–sulfur batteries (LiSBs) offer high energy density, cost-effectiveness, and eco-friendliness, making them promising for future energy storage. This study explores using BiFeO3 (BFO) nanoparticles (NPs) to tackle challenges such as lithium polysulfides (LiPs) and shuttle issues in LiSBs. It employs a solid-state melt diffusion technique, encapsulates sulfur in single-walled carbon nanotubes (SCNTs), and utilizes BFO for effective polysulfide control. Herein, composite cathodes of sulfur (S)/SCNTs (abbr. SCNT) were fabricated, and cells were designed using a BFO-coated separator (SCNT-BFS). In addition, a cathode modification was performed with composite S/SCNTs/BFO (SCNT-BF), and a comparative analysis was conducted to assess the effectiveness of the BFO in the separator and the cathode. Cyclic voltammetry measurements revealed that the increased current peak intensity at lower reduction potential in SCNT-BF and SCNT-BFS indicated control of higher-order LiPs (Li2Sx, where 4 ≤ x ≤ 8), resulting in the generation of more stable lower-order products (Li2S2/Li2S). The charge/discharge analysis revealed controlled LiPs, resulting in high-capacity retention in SCNT-BF (∼75%) and SCNT-BFS (∼88%) over 200 cycles, which yielded capacities of 526 and 700 mAh/g at C/8 (1C = 1675 mA/g). These promising results suggest that incorporating BFO into the cathode and separator can advance the commercialization of durable LiSBs. [ABSTRACT FROM AUTHOR]

Large area single and bilayer graphene are grown on Pt/Ti/SiO2 substrates by hot filament chemical vapor deposition (HFCVD) with and without the assistance of Cu foil. The quality and number of graphene layers deposited on the substrate are assessed by Raman Spectroscopy. Atomic Force Microscopy (AFM) is used for assessing the surface topography of the graphene films grown on the Pt/Ti/SiO2 substrates. The microstructure and elemental analyses are performed by Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS). The results show that bilayer graphene growth is facilitated by a copper foil placed nearby Pt/Ti/SiO2 substrate and by a high filament temperature in the HFCVD reactor. Monolayer graphene grows only when no copper foil is placed near the Pt/Ti/SiO2 substrate at a low filament temperature. The approach paves a novel pathway towards the layer‐controlled growth of graphene on Pt/Ti/SiO2 substrates by HFCVD for frontier applications. [ABSTRACT FROM AUTHOR]