Search

Photocatalysts of TiO2–CuO coupled with 30% graphene oxide (GO) were hydrothermally fabricated, which varied the TiO2 to CuO weight ratios to 1:4, 1:2, 1:1, 2:1 and 4:1 and reduced to form TiO2–CuO/reduced graphene oxide (rGO) photocatalysts. They were characterized using XRD, TEM, SEM, XPS, Raman, and DRS technologies. TiO2–CuO composites and TiO2–CuO/GO degrade methylene blue when persulfate ions are present. Persulfate concentration ranged from 1, 2, 4 to 8 mmol/dm−3 in which the highest activity of 4.4 × 10–2 and 7.35 × 10–2 min−1 was obtained with 4 mmol/dm−3 for TiO2–CuO (1:4) and TiO2–CuO/GO (1:1), respectively. The presence of EDTA and isopropyl alcohol reduced the photodegradation. TiO2–CuO coupled with rGO coagulates methylene blue in the presence of persulfate ions and such coagulation is independent of light. The catalyst dosage and the concentration of the dye were varied for the best-performing samples. The antibacterial activity of the synthesized samples was evaluated against the growth of Escherichia coli, Staphylococcus aureus, Pseudomonas aeruginosa and Klebsiella pneumonia. Ti:Cu (1:2)-GO and Ti:Cu (1:4)-GO had the highest antibacterial activity against K. pneumoniae (16.08 ± 0.14 mm), P. aeruginosa (22.33 ± 0.58 mm), E. coli (16.17 ± 0.29 mm) and S. aureus (16.08 ± 0.88). [ABSTRACT FROM AUTHOR]

Polyethyleneglycol-coated biocompatible CuO–ZnO nanocomposites were fabricated hydrothermally varying Zn:Cu ratios as 1:1, 2:1, and 1:2, and their antibacterial activity was determined through the well diffusion method against the Gram-negative Escherichia coli, Pseudomonas aeruginosa, Klebsiella pneumoniae, and the Gram-positive Staphylococcus aureus. The minimum inhibitory concentration and the minimum bactericidal concentration values of the synthesized samples were determined. Subsequently, the time synergy kill assay was performed to elucidate the nature of the overall inhibitory effect against the aforementioned bacterial species. The mean zone of inhibition values for all four samples are presented. The inhibitory effect increased with increasing concentration of the nanocomposite (20, 40 and 60 mg/ml) on all the bacterial species except for S. aureus. According to the MBC/MIC ratio, ZnO was found to be bacteriostatic for E. coli and P. aeruginosa, and bactericidal for S. aureus and K. pneumoniae. Zn:Cu 2:1 was bactericidal on all bacterial species. A bacteriostatic effect was observed on E. coli and P. aeruginosa in the presence of Zn:Cu 1:1 whereas, it showed a bactericidal effect on S. aureus and K. pneumoniae. Zn:Cu 1:2 exhibited a bacteriostatic effect on E. coli while a bactericidal effect was observed for E. coli, P. aeruginosa, and K. pneumoniae. The metal oxide nanocomposites were found to be more sensitive towards the Gram-positive strain than the Gram-negative strains. Further, all the nanocomposites possess anti-oxidant activity as shown by the DPPH assay. [ABSTRACT FROM AUTHOR]

Photocatalysts of TiO 2 -CuO coupled with 30% graphene oxide (GO) were hydrothermally fabricated, which varied the TiO 2 to CuO weight ratios to 1:4, 1:2, 1:1, 2:1 and 4:1 and reduced to form TiO 2 -CuO/reduced graphene oxide (rGO) photocatalysts. They were characterized using XRD, TEM, SEM, XPS, Raman, and DRS technologies. TiO 2 -CuO composites and TiO 2 -CuO/GO degrade methylene blue when persulfate ions are present. Persulfate concentration ranged from 1, 2, 4 to 8 mmol/dm -3 in which the highest activity of 4.4 × 10 -2 and 7.35 × 10 -2  min -1 was obtained with 4 mmol/dm -3 for TiO 2 -CuO (1:4) and TiO 2 -CuO/GO (1:1), respectively. The presence of EDTA and isopropyl alcohol reduced the photodegradation. TiO 2 -CuO coupled with rGO coagulates methylene blue in the presence of persulfate ions and such coagulation is independent of light. The catalyst dosage and the concentration of the dye were varied for the best-performing samples. The antibacterial activity of the synthesized samples was evaluated against the growth of Escherichia coli, Staphylococcus aureus, Pseudomonas aeruginosa and Klebsiella pneumonia. Ti:Cu (1:2)-GO and Ti:Cu (1:4)-GO had the highest antibacterial activity against K. pneumoniae (16.08 ± 0.14 mm), P. aeruginosa (22.33 ± 0.58 mm), E. coli (16.17 ± 0.29 mm) and S. aureus (16.08 ± 0.88)., (© 2024. The Author(s).)