Search

Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) remains the most investigated conjugated polymer in bioelectronics, due to its biocompatibility, high conductivity, and commercial availability. Despite these advantages, it suffers from structural and electronic instability, associated with the PSS component. Here, a graft copolymer based on ionised sulfonic modified PEDOT, poly(EDOTS- g -EDOT), was electrochemically synthesised with demonstrated structural and electronic stability and enhanced electrochemical performance. The graft copolymer was insoluble in water without crosslinking, and exhibited enhanced ion diffusion upon electrochemical switching, as revealed by its volumetric capacitance (159 ± 8 F cm -3 ), which was significantly higher than that of spin-coated PEDOT:PSS films (41 ± 5 F cm -3 ). Similarly, its performance as an active channel material in organic electrochemical transistors (OECTs) was superior to the spin-coated PEDOT:PSS, as shown for instance by its high normalised transconductance (273 ± 79 S cm -1 ) and a significantly high I ON / I OFF ratio (19 345 ± 1205). Its short- and long-term electronic stability were also confirmed with no drop in its output drain current, despite its high swelling degree. In contrast, the spin-coated PEDOT:PSS experienced a significant deterioration in its performance over the same operational time. The facile synthesis and improved performance of poly(EDOTS- g -EDOT) highlight the importance of innovative material design in overcoming existing operational shortcomings in electronic devices.

In the field of tissue engineering and regenerative medicine, developing cytocompatible 3D conductive scaffolds that mimic the native extracellular matrix is crucial for the engineering of excitable cells and tissues. In this study, a custom cryogenic extrusion 3D printer was developed, which afforded control over both the ink and printing surface temperatures. Using this approach, aqueous inks were printed into well-defined layers with high precision. A conductive hydrogel ink was developed from chitosan (CS) and edge-functionalised expanded graphene (EFXG). Different EFXG:CS ratios (between 60:40 and 80:20) were evaluated to determine both conductivity and printability. Using the novel customized cryogenic 3D printer, conductive structures of between 2 and 20 layers were produced, with feature sizes as small as 200 μm. The printed structures are mechanically robust and are electrically conducting. The highest Young's modulus and conductivity in a hydrated state were 2.6 MPa and ∼45 S/m, respectively. Cytocompatibility experiments reveal that the developed material supports NSC-34 mouse motor neuron-like cells in terms of viability, attachment, and proliferation. The distinctive mechanical and electrical properties of the 3D-printed structures would make them good candidates for the engineering of 3D-structured excitable cells. Moreover, this novel printing setup can be used to print other hydrogel-based inks with high precision and resolution., Competing Interests: No competing financial interests exist., (Copyright 2024, Mary Ann Liebert, Inc., publishers.)