Search

In the present study, the capacity of two commercial NiTi and NiTiCu shape memory alloy (SMA) wires to develop work-generating (WG) and constrained-recovery (CR) shape memory effects (SMEs), as well as the capacity of a commercial NiTiFe super-elastic wire to act as cold-shape restoring element, have been investigated. Using differential scanning calorimetry (DSC), the reversible martensitic transformation to austenite of the three NiTi-based wires under study was emphasized by means of an endothermic minimum of the heat flow variation with temperature. NiTi and NiTiCu wire fragments were further tested for both WG-SME and CR-SME developed during the heating, from room temperature (RT) to different maximum temperatures selected from the DSC thermograms. The former tests revealed the capacity to repetitively lift various loads during repetitive heating, while the latter tests disclosed the repetitive development of shrinkage stresses during the repetitive heating of elongated wires. The tensile behavior of the three NiTi-based SMA wires was analyzed by failure and loading–unloading tests. The study disclosed the actuation capacity of NiTi and NiTiCu shape memory wires, which were able to develop work while being heated, as well as the resetting capacity of NiTiFe super-elastic wires, which can restore the initial undeformed shape of shape memory wires which soften while being cooled down. These features enable the design of a robotic gripper based on the development of NiTi-based actuators with repetitive action. [ABSTRACT FROM AUTHOR]

One of the useful features of 3D-printed specimens of recycled polyethylene terephthalate glycol (R-PETG) is the ability to repetitively develop free recovery as well as the work-generating, shape-memory effect. This behavior is enabled by the R-PETG's capacity to stiffen during cooling, thus allowing for a new temporary shape to be induced. Aiming to devise an explanation for the polymer's stiffening, in this study, the variation in some of the R-PETG's parameters during cooling are emphasized and discussed. The evolution of an R-PETG filament's shape was monitored during room-temperature-bending heating–cooling cycles. Straight-shape recovery and the complete loss of stiffness were observed at the start and the end of heating, respectively, followed by the forced straightening of the filament, performed by the operator, around 40 °C, during cooling. The tests performed by dynamic mechanical analysis disclosed the rise of the storage modulus (E') after 100 °C heating followed by either liquid-nitrogen- or air-cooling to room temperature, in such a way that E' was always larger after cooling than initially. Static tests emphasized a peculiar stress variation during a heating–cooling cycle applied in air, within the heating chamber of the tensile testing machine. Tensile-failure tests were performed at −10 °C at a rate of 100 mm/min, with specimens printed at various deposition directions between 10 and 40° to the transversal direction. The specimens printed at 40°, which had the largest ultimate strains, were broken with tensile rates between 100 and 500 mm/min. Deformation rate increase favored the shift from crazing to delamination failure modes. The correlation between the structural changes, the sharp E' increase on heating, and the stiffening induced by cooling represents a novel approach that enables the use of 3D-printed R-PETG for the fabrication of the active parts of low-priced lightweight resettable actuators. [ABSTRACT FROM AUTHOR]