Highly transparent 10 at.% Yb:GdxY3−xAl5O12 (x = 0.3, 0.5, and 0.7) ceramics were successfully fabricated by vacuum solid‐state reactive sintering at 1800°C for 20 h combined with hot isostatic pressing posttreatment at 1700°C for 3 h under 176 MPa pressure in Ar atmosphere. The in‐line transmittances of these ceramics with the thickness of 2.5 mm are 84.4%, 84.0%, and 83.5% at 1100 nm for x = 0.3, 0.5, and 0.7, respectively. The relationships of the Gd3+ content among the phase, microstructures, spectral, and laser properties of the Yb:GdxY3−xAl5O12 ceramics were elucidated in detail. The introduction of Gd3+ has a little influence on the crystal field strength of the Yb3+ sites in GdxY3−xAl5O12. The absorption, emission spectra, and fluorescence lifetime of the Yb3+ in these ceramics are similar, close to 10 at.% Yb:YAG ceramics. Quasi‐continuous wave laser outputs of the ceramics were also achieved. The maximum laser output powers are 7.8, 7.7, and 6.6 W with the corresponding slope efficiency as 46.2%, 44.7%, and 39.2% for x = 0.3, 0.5, and 0.7, respectively. The 7.8 W laser output power is the highest value achieved so far for the Yb:GdYAG ceramics, to the best of our knowledge. The previous discussions show that not all the mixed garnets could enhance full width at half maximum of absorption and emission peaks for the active ions; however, the Yb:GdYAG ceramics are still excellent laser gain media. [ABSTRACT FROM AUTHOR]

In this work, 5at.% Yb:Lu2O3 transparent ceramics were air‐annealed at different temperatures to eliminate oxygen vacancies for laser performance improvement. The influence of annealing temperature on microstructures, optical quality, and laser performance was investigated comprehensively. The ceramics HIP (Hot isostatic pressing) post‐treated at 1750°C and annealed above 1100°C show a significant optical quality decrease due to residual pore expansion, and the ceramic sample annealed at 900°C shows better laser performance than others. The maximum output of 2.88 W was obtained at 1033.3 nm with a slope efficiency of 37.4% under a quasi‐continuous wave (QCW) mode. Note that 5at.% Yb:Lu2O3 transparent ceramics HIP post‐treated at 1550°C still keep good transparency even when being annealed at 1300°C due to less residual compressed pores. The highest slope efficiency is about 73.8% with a maximum output power of 2.84 W under QCW. Fine‐grained and dense Yb:Lu2O3 transparent ceramics could be annealed at higher temperatures to eliminate oxygen vacancies more thoroughly to improve laser performance. [ABSTRACT FROM AUTHOR]