Search

CsPbBr3 exhibits strong green emission, but its toxicity limits its widespread application. Lead-free perovskites exhibit excellent optoelectronic properties while eliminating the toxicity of lead; at the same time, doping substitution is an effective means to further optimize the optoelectronic performance of perovskites. In this work, zinc(II) is chosen to achieve heterovalent substitution in the copper(I) based perovskite Cs3Cu2Cl5 and obtain strong green luminescence. The photoluminescence quantum yield (PLQY) reached 70.19% at an optimal doping concentration, which is twice the PLQY of undoped Cs3Cu2Cl5 and much higher than that of most doped lead-free perovskites. Furthermore, a white light emitting diode (WLED) was fabricated with doped Cs3Cu2Cl5:0.20 Zn2+ as a green phosphor, commercial blue phosphor Sr(PO4)Cl:Eu+, and commercial red phosphor CaAlSiN3:Eu2+. The color rendering index (CRI) is 95.8, while the correlated color temperature (CCT) is 4573 K, which is much better than that of the WLED fabricated with CsPbBr3. This research provides important guidance on the fabrication of green light emission Zn-doped Cs3Cu2Cl5 instead of toxic CsPbBr3 and has potential in WLED lighting. [ABSTRACT FROM AUTHOR]

A novel Mn2+ doped ScTaO4 phosphor was synthesized through a high temperature solid state method and its photoluminescence properties were systematically investigated. The ScTaO4:Mn2+ phosphor exhibited two emission bands centered at 478 nm and 661 nm under UV excitation, attributed to the self-activated emission of the host and the 4T1 → 6A1 transition emission from doped Mn2+ ions, respectively. Through optimizing the concentration of doped Mn2+ ions, white light emission was achieved. Meanwhile, the temperature-dependent luminescence spectra of the ScTaO4:Mn2+ phosphor (in the range from 298 K to 523 K) revealed significantly different thermal quenching behaviors between the host and Mn2+ ions, which cause a notable change in the fluorescence intensity ratio of the host versus Mn2+ ions and enable high absolute and relative sensitivities, with maximum values of 0.0172 K−1 and 2.1% K−1 at 523 K, respectively. The results indicated that the as-prepared STO:Mn2+ phosphor can be a potential candidate material for high temperature optical thermometry. [ABSTRACT FROM AUTHOR]

Background: Hepatocellular carcinoma (HCC) is a highly prevalent and deadly cancer, with limited treatment options for advanced-stage patients. Disulfidptosis is a recently identified mechanism of programmed cell death that occurs in SLC7A11 high-expressing cells due to glucose starvation-induced disintegration of the cellular disulfide skeleton. We aimed to explore the potential of disulfidptosis, as a prognostic and therapeutic marker in HCC. Methods: We classified HCC patients into two disulfidptosis subtypes (C1 and C2) based on the transcriptional profiles of 31 disulfrgs using a non-negative matrix factorization (NMF) algorithm. Further, five genes (NEIL3, MMP1, STC2, ADH4 and CFHR3) were screened by Cox regression analysis and machine learning algorithm to construct a disulfidptosis scoring system (disulfS). Cell proliferation assay, F-actin staining and PBMC co-culture model were used to validate that disulfidptosis occurs in HCC and correlates with immunotherapy response. Results: Our results suggests that the low disulfidptosis subtype (C2) demonstrated better overall survival (OS) and progression-free survival (PFS) prognosis, along with lower levels of immunosuppressive cell infiltration and activation of the glycine/serine/threonine metabolic pathway. Additionally, the low disulfidptosis group showed better responses to immunotherapy and potential antagonism with sorafenib treatment. As a total survival risk factor, disulfS demonstrated high predictive efficacy in multiple validation cohorts. We demonstrated the presence of disulfidptosis in HCC cells and its possible relevance to immunotherapeutic sensitization. Conclusion: The present study indicates that novel biomarkers related to disulfidptosis may serve as useful clinical diagnostic indicators for liver cancer, enabling the prediction of prognosis and identification of potential treatment targets. [ABSTRACT FROM AUTHOR]

Transition metal ion and/or rare earth ion doped CsPbCl3 nanocrystals (NCs) have attracted extensive attention due to their high combined emission efficiency characteristics. Their high-throughput preparation is of great significance for future industrialization that is still a challenge based on existing batch reaction technologies. Herein, we demonstrate a high-throughput preparation method of Mn2+-doped CsPbCl3 NCs based on a fluidic channel reactor. The as-prepared NCs show vivid yellowish-orange emission at 600 nm and high photoluminescence quantum yield (PLQY) of 63.3%. Meaningfully, due to the closer bond between surface ligands and NCs, NCs prepared by this method show better water durability than NCs obtained using the traditional hot injection method. Finally, a WLED with a high color rendering index (CRI) of 94 and a low correlated color temperature (CCT) of 3626 K was fabricated by combining the as-prepared yellowish-orange Mn-doped CsPbCl3 with the BaMgAl10O17:Eu2+ (BAM:Eu2+) blue phosphor and CaAlSiN3:Eu2+ (CASN:Eu2+) red phosphor on a 375 nm ultraviolet chip. These findings suggest that the Mn-doped CsPbCl3 prepared by the fluidic channel reaction is suitable for WLEDs. Our work paves the way for achieving a continuous, large-scale preparation of perovskite NCs by a fluidic channel reaction for the development of their WLED solid state lighting applications. [ABSTRACT FROM AUTHOR]

A green phosphor Sr2ZnGe2O7:Mn2+ with a melilite structure was prepared using a high‐temperature solid‐state reaction. When the 535 nm emission was monitored, the excitation spectrum of the Sr2ZnGe2O7:Mn2+ was found to contain two excitation bands in the ultraviolet (UV) region. When excited by UV light, the sample shows bright green emission at 535 nm, which corresponds to the distinctive transition of Mn2+ (4T1→6A1). Moreover, the quantum efficiency of Sr2ZnGe2O7:Mn2+ could reach 67.6%. Finally, a high‐performance white‐light‐emitting diode (WLED) with a low correlated colour temperature of 4632 K and a high colour rendering index (CRI) of 92.3 were packaged by coating commercial blue and red phosphors with an optimized Sr2ZnGe2O7:Mn2+ sample on a 310 nm UV chip. This indicated that Sr2ZnGe2O7:Mn2+ has the potential application as a green component in the WLED lighting field. [ABSTRACT FROM AUTHOR]

Single-component white-light luminescent materials are considered an economical and facile choice for phosphor-converted white light-emitting diodes (pc-WLEDs). Here, a new single-component white-light-emitting material Cs 2 MnCl 4 :Eu 2+ based on the combination of a lead-free halide structure and a rare-earth ion is first reported. Benefiting from the smart dilution-sensitization design strategy, white light composed of dual broad emission originating from Eu 2+ (blue light, 444 nm, 4f 6 5d 1 → 4f 7 ) and Mn 2+ (yellow light, 566 nm, 4 T 1g → 6 A 1g ) was successfully realized under near-ultraviolet light (404 nm) radiation with a high photoluminescence quantum yield of 66%. Based on the single-source Cs 2 MnCl 4 :Eu 2+ phosphor, a pc-WLEDs device with "eye-friendly" white light production was successfully fabricated. The pc-WLEDs exhibit suitable color coordinates of (0.3294, 0.2746) and a high color rendering index of 82.3, demonstrating the potential in the future health-conscious illumination application by reducing the risk of eye strain and high-energy blue-light damage. This work achieves a new single-component white-light-emitting Mn-based halide phosphor and provides a new path for the design of single-component white light sources in Mn-based halides.

A green phosphor Sr 2 ZnGe 2 O 7 :Mn 2+ with a melilite structure was prepared using a high-temperature solid-state reaction. When the 535 nm emission was monitored, the excitation spectrum of the Sr 2 ZnGe 2 O 7 :Mn 2+ was found to contain two excitation bands in the ultraviolet (UV) region. When excited by UV light, the sample shows bright green emission at 535 nm, which corresponds to the distinctive transition of Mn 2+ ( 4 T 1 → 6 A 1 ). Moreover, the quantum efficiency of Sr 2 ZnGe 2 O 7 :Mn 2+ could reach 67.6%. Finally, a high-performance white-light-emitting diode (WLED) with a low correlated colour temperature of 4632 K and a high colour rendering index (CRI) of 92.3 were packaged by coating commercial blue and red phosphors with an optimized Sr 2 ZnGe 2 O 7 :Mn 2+ sample on a 310 nm UV chip. This indicated that Sr 2 ZnGe 2 O 7 :Mn 2+ has the potential application as a green component in the WLED lighting field., (© 2023 John Wiley & Sons Ltd.)