Search

Underwater superoleophobic coatings exhibit promising prospects in the field of oil contamination resistance. However, their poor durability, stemming from the fragile structures and unstable hydrophilicity, greatly restricted their development. In this report, we proposed a novel strategy of combination water-induced phase separation and biomineralization to prepare the robust underwater superoleophobic epoxy resin-calcium alginate (EP-CA) coating by utilizing a surfactant-free emulsion of epoxy resin/sodium alginate (EP/SA). The EP-CA coating not only exhibited excellent adhesion to various substrates, but also had remarkable resistance to the physical/chemical attacks such as abrasion, acid, alkali and salt. It could also protect the substrate (e.g., PET substrate) from the damage of organic solution and the fouling of crude oil. This report provides a new perspective to fabricate robust superhydrophilic coating with a facile way., Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2023 Elsevier Inc. All rights reserved.)

CeO 2 was used as the only oxidant for aniline polymerization, and polyaniline (PANI) was grown on CeO 2 surface to form CeO 2 @PANI nanocomposites. SEM and TEM showed that the CeO 2 @PANI composites were nanorods in a core-shell structure. XPS indicated that CeO 2 -core was reduced by aniline into Ce 3+ , which was then captured by the PANI-shell. Then the passive ability of CeO 2 @PANI coating on steels was explored. EIS showed that the impedance modulus of the CeO 2 @PANI coating exceeded 10 8  Ω·cm 2 after accelerated immersion. The SVET and XPS confirmed that PANI polarized the anodic reaction, Ce 3+ suppressed the cathodic reaction, and PO 4 3- formed complex precipitation. Some high-valent metal oxides can directly oxidize the aniline polymerization to form MO@PANI hybrid particles. The cations obtained by the metal oxide reduction can be captured by PANI and participate in passivation together with dopants. This study provides a new kind of nanocomposite fillers that can effectively passivate steel substrates within epoxy coatings for long-time protection., Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2020 Elsevier Inc. All rights reserved.)

In this work, birnessite-type δ-MnO 2 nanoflowers were uniformly deposited on 3D nickel foam (NF) by one-step hydrothermal route for high-efficient activation of peroxymonosulfate (PMS) towards degradation of acid orange 7 (AO7). High specific surface area, large pore volume and 3D hierarchical structure promotes the mass and electron transfer for great catalytic activity. Low reaction energy barrier (E a  = 27.5 kJ/mol) and outstanding reusability with extremely low manganese leaching during recycling (<0.06 mg/L) was achieved due to the 3D hierarchical structure which could effectively avoid the agglomeration of nano-sized MnO 2 . SO 4 - was confirmed to be the predominant reactive species for AO7 decomposition by electron spin resonance and quenching tests. The synergistic catalytic mechanism of MnO 2 /NF and the role of inner-sphere complexation between the active sites of MnO 2 and peroxymonosulfate were thoroughly investigated. Compared with traditional nano/micro-sized catalysts, 3D macroscopic MnO 2 /NF with facile recovery and high stability potentially facilitates fascinating applications as green heterogeneous catalysis approach., Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2020 Elsevier Inc. All rights reserved.)

Single-stage oil/water separation membranes usually suffer from weak chemical stability, susceptible mechanical damage and relatively low permeating flux, and the sophisticated preparation processes also limit their massive utilization. In this work, Cu(OH) 2 nanoneedles coated copper mesh (CM) is prepared by simple and eco-friendly anodic oxidation at a current density of 4 mA/cm 2 for 6 min, which is the most efficient route reported so far. The mesh exhibits outstanding superhydrophilicity and underwater superoleophobicity towards various oils with contact angles up to 164.9°, achieving superior oil/water separation efficiency of above 99.5% and ultrahigh permeating flux of 191 160 L·m -2 h -1 solely driven by gravity. Impressively, the Cu(OH) 2 /CM demonstrates excellent chemical stability and anti-fouling performance when exposed to acidic and strongly alkaline solutions, saturated NaCl solution and various organic solvents. High durability to withstand mechanical challenges, e.g. high-power sonication and sand abrasion, is experimentally confirmed owing to strong cohesional strength of Cu(OH) 2 nanoneedles on CM surface. Importantly, the Cu(OH) 2 /CM exhibits favorable long-term recyclability with stable microstructure morphologies even after 50 cycles. These distinct advantages endow the Cu(OH) 2 /CM to be an ideal candidate to efficiently separate oil pollutants from water. The oil/water separation mechanisms are proposed based on the concept of intrusion pressure., (Copyright © 2019 Elsevier Inc. All rights reserved.)