Abstract: This paper compares the influence of the molecular weight of polylelectrolytes forming polyelectrolyte multilayers (PEM) on wood fibers on adhesion and paper strength. Sheets were made from fibers treated with poly(allylamine hydrochloride) (PAH)/poly(acrylic acid) (PAA) of molecular mass 70,000 and 240,000, respectively, and of poly(dimethyldiallylammonium chloride) (PDADMAC)/poly(styrene sulfonate) (PSS) of molecular mass 30,000 and 80,000, respectively. The results were compared to what has recently been reported for PEM formation on fibers using a low-molecular-mass combination of PAH and PAA and a high-molecular-mass combination of PDADMAC/PSS. There was a less significant improvement in the case of the low-molecular-mass PDADMAC/PSS and the high-molecular-mass PAH/PAA. The adsorbed amounts of PAH and PDADMAC were also determined, showing a lower adsorbed amount of the low-molecular-mass PAH than of the high-molecular-mass PDADMAC. The amount of low-molecular-mass PDADMAC was similar to that found for high-molecular-mass PDADMAC/PSS. Individual fibers were partly treated and studied, showing a less significant decrease in wettability with low-molecular-mass PDADMAC/PSS than with the high-molecular-mass combination. The effect of the molecular weight on the adhesion was discussed in terms of the structure and wettability of the PEMs. [Copyright &y& Elsevier]

Abstract: The influence of mixing procedure on the properties of polyelectrolyte complexes (PECs) was investigated using two complexation techniques, polyelectrolyte titration and jet mixing, the latter being a new method for PEC preparation. For the low-molecular-weight polyelectrolytes polyacrylic acid (PAA) and polyallyl amine hydrochloride (PAH), shorter mixing times produced smaller PECs, whereas for higher molecular weights of the same polyelectrolytes, PEC size first decreased with decreasing mixing time to a certain level, after which it started increasing again. This pattern was likely due to the diffusion-controlled formation of “pre-complexes”, which, in the case of low-molecular-weight polymers, occurs sufficiently quickly to form stable complexes; when polyelectrolytes are larger, however, non-equilibrium pre-complexes, more prone to aggregation, are formed. Comparing the techniques revealed that jet mixing produced smaller complexes, allowing PEC size to be controlled by mixing time, which was not the case with polyelectrolyte titration. Higher polyelectrolyte concentration during jet mixing led to the formation of larger PECs. It was also demonstrated that PEC size could be changed after preparation: increasing the pH of the PEC dispersion led to an irreversible increase in PEC size, whereas lowering the pH did not influence PEC size. The adsorption behavior of PECs formed from weak polyelectrolytes on model substrates was studied using QCM-D, SPAR, and AFM imaging; the results indicated that increasing the pH increased the amount of PECs adsorbed to model surfaces. However, the amount of PECs adsorbed to the model surfaces was low compared with other systems in all studied cases. [ABSTRACT FROM AUTHOR]