Search

[Display omitted] • A class of Ru-Co single-atom alloy catalysts (marked as Ru x Co 1 SAA, x stands for Ru/Co molar ratio) were prepared. • The electronic structure of Ru x Co 1 SAA could be effectively tuned by regulating the Ru/Co molar ratio. • A moderate ratio of Ru/Co (1.7:1) favors superior NH 3 synthesis rate. • The excess Ru destroys the SAA structure, resulting in the diminution of SAA advantages. Rational design of efficient catalysts for ammonia (NH 3) synthesis at mild conditions is of paramount importance for the development of electrolysis driven Haber-Bosch (e HB) process. Ammonia synthesis is a structure sensitive reaction, and any small change of electronic structure could result in dramatic change of catalytic activity, especially for the Ru-based NH 3 synthesis catalysts. Electronic structure modulation of the Ru-based catalysts could provide desirable catalytic activity. Herein, we explore a class of Ru-Co single-atom alloy catalysts (marked as Ru x Co 1 SAA, x stands for Ru/Co molar ratio), in which Co single atoms are located on Ru nanoclusters to form Co-Ru coordination, and then electronic structure of Ru x Co 1 SAA could be effectively tuned by regulating the Ru/Co molar ratio. Our studies show that a moderate ratio of Ru/Co (1.7:1) favors superior NH 3 synthesis rate and low activation energy. Using a suite of elaborate characterizations, we have observed that the outstanding performance over Ru 1.7 Co 1 SAA can be attributed to the electron redistribution between Ru and Co atom, resulting in an upshift of d band center and lowering of work function. However, there is decrease of NH 3 synthesis rate when Ru/Co molar ratio is 2, due to the partial detachment of Ru entities from SAA structure, and the formed individual Ru nanoparticles (NPs) overlay the surface of catalyst. In such a case, N 2 activation behavior over Ru 2 Co 1 is alike that of Ru NPs catalysts. The present study demonstrates that the Ru/Co ratio in SAA structure can effectively regulate the electronic structure of catalyst for NH 3 synthesis rate enhancement. [ABSTRACT FROM AUTHOR]

The decrease of Ru particle size from nanoparticles (NPs) to nanoclusters (NCs) can not only increase the NH 3 synthesis performance, but also increase the proportion of corner sites. [Display omitted] • A series of diverse Ru particle sizes (1.4–5.0 nm) over N-doped carbon support were successfully prepared by colloidal Ru deposition method. • The decrease of Ru particle size from nanoparticles (NPs) to nanoclusters (NCs) can not only increase the NH 3 synthesis performance, but also promote the activation of N 2 via an association pathway. • The ample corner sites over Ru NCs can decrease the work function and thus promote N 2 activation. Ammonia (NH 3) synthesis is a structure-sensitive reaction, where a minute variation of catalyst structure would lead to a dramatic change of activity. To date, the roles of Ru size on NH 3 synthesis still remain elusive, and it remains a major challenge. Herein, a series of Ru catalysts with sizes ranging from 1.4 to 5.0 nm were prepared by colloidal Ru deposition, which allows the investigation of size influence on NH 3 synthesis. Through analyses of the geometric and electronic properties of variable-sized Ru particles, it shows that the reduction of Ru particle size could increase the proportion of corner sites while decrease that of terrace sites, which can decrease the work function and thus promote N 2 for its activation. Isotopic investigations show that the decrease of dissociative contribution but the increase of associative contribution as Ru particle size was decreased from 5.0 to 1.4 nm. Meanwhile, the NH 3 synthesis rate increases when the size of Ru catalysts decreases from 5.0 to 1.4 nm. Using a suite of elaborate characterizations, we have observed that 1.4 nm Ru nanoclusters (NCs) with ample corner sites are conducive to activate N 2 via an associative route. As a result, the 1.4 nm Ru NCs catalyst shows the highest NH 3 synthesis rate (up to 17.13 mmol NH3 g cat −1h−1) at 400 ℃ and 1 MPa. [ABSTRACT FROM AUTHOR]

[Display omitted] • Unique pompon-like RuCo catalysts were fabricated. • Atomically dispersed Ru-Co sites facilitated the adsorption/activation of reactants. • Excellent catalytic performance was achieved in the guaiacol hydrodeoxygenation. • Ru-Co synergy, as well as favorable hcp structure, contributed to high catalytic efficiency. Currently, the highly efficient conversion of biomass resources into highly valuable chemicals and biofuels is one of the most prospective approaches to reduce greenhouse gases emission and environmental pollution caused by excess consumption of fossil fuels. Herein, three-dimensional pompon-like well-defined RuCo particles with tunable crystallographic structures and surface atomically dispersed Ru atoms were constructed and intensively investigated as support-free metal catalysts in the hydrodeoxygenation (HDO) of lignin-derived guaiacol. It was demonstrated that the 300 °C-reduced RuCo sample possessed the hexagonal close-packed (hcp) crystallographic structure with surface abundant atomically dispersed Ru atoms, whereas 600 °C-reduced RuCo sample presented the face-centered cubic phase with lower surface Ru concentration. The as-fabricated RuCo-300 sample showed excellent catalytic HDO activity with a high cyclohexane yield of 85.3%. Comprehensive structural characterizations unveiled that the introduction of atomically dispersed Ru atoms into the RuCo-300 favored the formation of abundant surface Ru-Co sites, as well as electron-rich Ru0, and such-constructed Ru-Co sites were highly beneficial to the hydrogen dissociation on single Ru0 atoms and the further hydrogen spillover to adjacent Co0 atoms to promote the HDO process. Moreover, density functional theory (DFT) calculations revealed that the hcp structure of RuCo catalysts benefited the adsorption of guaiacol. The unique pompon-like microstructure of RuCo catalysts was conducive to the exposure of active sites and provided more open channels for the easy diffusion of reactants and products. Over the RuCo-300 catalyst, the guaiacol HDO could proceed rapidly via an initial demethoxylation reaction. The present Ru-Co synergetic catalysis in the structure of RuCo catalysts would provide a new strategy for constructing robust heterogeneous bimetal catalysts applied in practical HDO processes of a variety of lignin-derived phenolic compounds. [ABSTRACT FROM AUTHOR]