Search

Abstract: This paper compares the influence of the molecular weight of polylelectrolytes forming polyelectrolyte multilayers (PEM) on wood fibers on adhesion and paper strength. Sheets were made from fibers treated with poly(allylamine hydrochloride) (PAH)/poly(acrylic acid) (PAA) of molecular mass 70,000 and 240,000, respectively, and of poly(dimethyldiallylammonium chloride) (PDADMAC)/poly(styrene sulfonate) (PSS) of molecular mass 30,000 and 80,000, respectively. The results were compared to what has recently been reported for PEM formation on fibers using a low-molecular-mass combination of PAH and PAA and a high-molecular-mass combination of PDADMAC/PSS. There was a less significant improvement in the case of the low-molecular-mass PDADMAC/PSS and the high-molecular-mass PAH/PAA. The adsorbed amounts of PAH and PDADMAC were also determined, showing a lower adsorbed amount of the low-molecular-mass PAH than of the high-molecular-mass PDADMAC. The amount of low-molecular-mass PDADMAC was similar to that found for high-molecular-mass PDADMAC/PSS. Individual fibers were partly treated and studied, showing a less significant decrease in wettability with low-molecular-mass PDADMAC/PSS than with the high-molecular-mass combination. The effect of the molecular weight on the adhesion was discussed in terms of the structure and wettability of the PEMs. [Copyright &y& Elsevier]

Highlights: [•] We used difference in surface roughness to make different superhydrophobic coatings. [•] The coatings all had the same surface chemistry. [•] We found the superhydrophobic wetting state to greatly affect corrosion protection. [•] The lotus state was found to be most efficient regarding corrosion protection. [•] Air layer immobilization provided by the lotus effect is retarding corrosion. [ABSTRACT FROM AUTHOR]

Abstract: In this study, particle polyelectrolyte complexes (PPECs) were formed by mixing cationic polyacrylamide (CPAM) and silica nanoparticles using the jet mixing technique. Within certain limits, the size of the formed PPECs could be controlled. The aim was to prepare PPECs with embedded sacrificial bonds, similar to those found in bones. Examination of PPEC adsorption to silica model surfaces indicated that smaller PPECs adsorbed to a higher level than larger ones, due to the higher diffusion speed of smaller complexes. Adsorption studies of the same components as in the PPECs, but arranged in multilayers, that is, particle polyelectrolyte multilayers (PPEMs), indicated a stable, gradual build-up of material on the surface with smaller nanoparticles, whereas PPEMs comprising elongated nanoparticles appeared to be more loosely adsorbed onto the surface when the nanoparticles were in the outer layer, due to repulsive forces within the adsorbed layer. The AFM colloidal probe technique was used to study the interaction between surfaces treated with PPECs, multilayers, or polyelectrolyte complexes (PECs). The results showed that the expected long-range disentanglement could be achieved with PPECs but that the pull-off forces were generally low. Treatment with PPEMs comprising the same polymer and nanoparticle components produced higher pull-off values, together with disentanglement behaviour, possibly due to better contact between the surfaces. Adhesion experiments with polymer PECs showed significantly higher pull-off values than with the PPECs, probably due to polymer interdiffusion across the surface boundary. [Copyright &y& Elsevier]

Abstract: The wetting of two different model cellulose surfaces has been studied; a regenerated cellulose (RG) surface prepared by spin-coating, and a novel multilayer film of poly(ethyleneimine) and a carboxymethylated microfibrillated cellulose (MFC). The cellulose films were characterized in detail using atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). AFM indicates smooth and continuous films on a nanometer scale and the RMS roughness of the RG cellulose and MFC surfaces was determined to be 3 and 6 nm, respectively. The cellulose films were modified by coating with various amounts of an anionic fluorosurfactant, perfluorooctadecanoic acid, or covalently modified with pentadecafluorooctanyl chloride. The fluorinated cellulose films were used to follow the spreading mechanisms of three different oil mixtures. The viscosity and surface tension of the oils were found to be essential parameters governing the spreading kinetics on these surfaces. XPS and dispersive surface energy measurements were made on the cellulose films coated with perfluorooctadecanoic acid. A strong correlation was found between the surface concentration of fluorine, the dispersive surface energy and the contact angle of castor oil on the surface. A dispersive surface energy less than 18 mN/m was required in order for the cellulose surface to be non-wetting () by castor oil. [Copyright &y& Elsevier]

Abstract: Wet and dry adhesion between dextran-coated surfaces were measured aiming to understand the influence of polymer compatibility. The wet adhesion measurements were performed using the atomic force microscope (AFM) colloidal probe technique whereas the dry adhesion measurements were performed using the micro adhesion measurement apparatus (MAMA). Two types of dextrans were used, one cationically modified dextran (DEX) and one that was both cationically and hydrophobically modified (HDEX), leading to three different combinations of polymer-coated surfaces; (1) DEX:DEX, (2) HDEX:DEX, and (3) HDEX:HDEX. DEX increased dry adhesion more than HDEX did, which likely is due to differences in the ability to form specific interactions, especially hydrogen bonding. HDEX gave strong wet adhesion, probably due to its poorer solvency, while DEX contributed to reducing the wet adhesion due to its hydrophilicity. All combinations showed a steric repulsion on approach in aqueous media. Furthermore, when HDEX was adsorbed on either or both surfaces a long range attractive force between the surfaces was detected outside this steric regime. [Copyright &y& Elsevier]