Nanocrystalline silicon carbide has been prepared via reacting magnesium silicide (Mg2Si) with carbon tetrachloride (CCl4) in an autoclave at 450–600°C. X-ray diffraction patterns of the products can be indexed as the cubic cell of SiC with the lattice constant, a=4.352 Å, in good agreement with a=4.349 Å (JCPDS card No. 75-0254). The transmission electron microscopy images show that the sample mainly consists of nanoparticles with an average size from 30 to 80 nm co-existing with a small fraction of nanorods and nanowires. Typically the nanorods range from 20 to 40 nm in diameter and the nanowires have diameters of 20 nm and lengths up to 10 μm. The Raman spectrum shows a characteristic sharp peak at 790 cm-1. X-ray photoelectron spectra (XPS) gives an atomic ratio of Si to C as 1.08:1.00 from the quantification of the peak intensities. Photoluminescence spectrum reveals that the SiC sample emits ultraviolet light of 328 nm. A possible mechanism and the influence of temperature on the formation of crystalline SiC are proposed. [Copyright &y& Elsevier]

Abstract: Four types of BN nanotubes are selectively synthesized by annealing porous precursor in flowing NH3 and NH3/H2 atmosphere at temperature ranging from 1000 to 1200°C in a vertical furnace. The as-synthesized BN nanotubes, including cylinder, wave-like, bamboo-like and bubble-chain, are characterized by XRD, FTIR, Raman, SEM, TEM and HRTEM. Three phenomenological growth models are proposed to interpret growth scenario and structure features of the four types of BN nanotubes. Selectivity of nanotubes formation is estimated as approximately 80–95%. The precursor containing B, Mg, Fe and O prepared by self-propagation high-temperature synthesis (SHS) method plays a key role in selective synthesis of the as-synthesized BN nanotubes. Chemical reactions are also discussed. [Copyright &y& Elsevier]