Search

The fabrication and characterization of IR chalcogenide polarization-maintaining (PM) step-index optical fibers with elliptical-core and 1-in-line-core have been reported for the first time. An improved isolated co-extrusion method was used to fabricate these core-shaped PM fibers. The elliptical core had a horizontal radius of a = 3.66 μm, vertical radius of b = 1.83 μm and the 1-in-line core of a = 4.83 μm, b = 1.42 μm, respectively. Single-mode PM beam spots were observed for the elliptical-core and 1-in-line-core fibers in the near-field energy distributions. The highest values of birefringence of the elliptical-core and 1-in-line-core fibers are 2.09 × 10 −4 at 2.7 μm and 3.272 × 10 −4 at 2.8 μm, respectively. The extinction ratios of −3.7 dB and −2 dB were achieved in fibers of 0.5 m long with elliptical-core and 1-in-line-core, respectively. [ABSTRACT FROM AUTHOR]

As 2 Se 3 glass fibers measuring 250 μm in diameter were fabricated based on different draw processing parameters, including preform dropping temperatures (T 1 = T g + ΔT, ΔT = 20, 30, 40, 50 °C), fiber-drawing temperatures (T 2 = T g + ΔT, ΔT = 10, 20, 50 °C), and drawing speeds. Raman spectra indicated crystallization on fiber surface at high temperatures. After fiber drawing, oxygen was detected on fiber surface by energy dispersive X-ray spectra. High-quality fiber with minimum loss of 1.88 dB/m (at 9.05 µm) was achieved under optimal dropping temperature of 218.1 °C (T g + 30 °C), fiber-drawing temperature of 208.1 °C (T g + 20 °C), and drawing speed of 0.10 m/min. [ABSTRACT FROM AUTHOR]

We have investigated the optimization parameters for polishing end-surface of chalcogenide glass fiber connector in the paper. Six SiC abrasive particles of different sizes were used to polish the fiber in order of size from large to small. We analyzed the effects of polishing parameters such as particle sizes, grinding speeds and polishing durations on the quality of the fiber end surface and determined the optimized polishing parameters. We found that, high-quality fiber end surface can be achieved using only three different SiC abrasives. The surface roughness of the final ChG fiber end surface is about 48 nm without any scratches, spots and cracks. Such polishing processes could reduce the average insertion loss of the connector to about 3.4 dB. [ABSTRACT FROM AUTHOR]

This work experimentally demonstrates the supercontinuum (SC) generation in a three-hole arsenic free Ge 20 Sb 15 Se 65 chalcogenide suspended-core fiber. Mechanical drilling was used to prepare the chalcogenide glass preform, which was drawn into suspended-core fibers. The zero-dispersion wavelength of the fiber is moved toward the shorter wavelength of about 3.2 μm through changing the fiber core diameter by controlling the pressure of inert gas during fiber drawing. When a 15 cm-long fiber with a core diameter of 6 μm is pumped using 150 fs pulses at 3.3 μm, SC spanning from ∼3 μm to ∼8 μm was generated. [ABSTRACT FROM AUTHOR]

A mechanical drilling method for the preparation of photonic crystal fibers (PCFs) is presented in this paper. Several PCFs were fabricated with Ge 20 Sb 15 S 65 chalcogenide glasses, which have high transparency in the mid-infrared (IR) range. The mechanical drilling method has been identified as a powerful tool to prepare fibers with a variety of structures and to increase the transmission of the obtained fibers. For a three-ring PCF, the near-field intensity distribution and the transmission loss were measured. It was found that most of the optical energy is contained in the core of the PCF. The profile of the near-field intensity image shows that the prepared PCF can work with a large mode area, which is important in high-power laser propagation and fiber amplifiers. [ABSTRACT FROM AUTHOR]

• A dual-clad step-index chalcogenide fiber based on tellurium glasses was proposed and investigated detailedly for midinfrared coherent supercontinuum generation. • The structure of the fiber with a W-type refractive-index profile was numerically studied and optimized for all-normal dispersion profile. • Due to the large material zero dispersion wavelength, an all-normal dispersion tellurium chalcogenide fiber was realized via the waveguide chromatic engineering. • The optimized fiber was fabricated via extrusion and employed for coherent supercontinuum generation. • The result shows that a high coherent supercontinuum covering 3.5–10.5 μm can be generated in this fiber with 5 μm femtosecond laser pumping. • This is the first numerical investigation on the dispersion engineering of tellurium chalcogenide dual-clad step-index fiber. Considerable investigations have been carried out for chromatic dispersion tailoring of chalcogenide glass fiber with various structures and different material compositions. Here we proposed a tellurium-based chalcogenide glass fiber with a dual-clad structure in a W-type refractive-index profile. The structure of the fiber based on Ge-As-Se-Te glasses was numerically analyzed in detail. The simulation results indicate that an all normal dispersion profile can be realized in this tellurium glass fiber with an optimized dual-cladding structure. Then the optimized tellurium chalcogenide fiber with an all-normal dispersion profile was fabricated by multi-extrusion method. Pumping with a 5 μm ultra-short pulsed laser (150 fs, 1 kHz), abroadband supercontinuum (SC) covering 1.5–11 μm can be generated in the 19 cm-long fiber. The coherence of SC was also investigated by numerical simulation. The result shows that a high coherent SC covering 3.5–10.5 μm can be generated in this all-normal dispersion fiber. In conclusion, all-normal dispersion profile can be realized easily in this tellurium-based glass fiber due to their large materials ZDWs. [ABSTRACT FROM AUTHOR]