Prehydrolysis liquid (PHL) from dissolving pulp and biorefinery industries is rich in saccharides and lignin, being considered as a potential source of value-added materials and platform molecules. This study proposed an environmentally friendly and simple method to prepare morphologically controllable hollow lignin nanoparticles (LNPs) and levulinic acid (LA) from PHL. In the first step, after hydrothermal treatment of PHL with p -toluenesulfonic acid ( p -TsOH), lignin with a uniform molecular weight was obtained to prepare LNPs. The prepared LNPs have an obvious hollow structure, with an average size of 490-660 nm, and exhibit good stability during 30 days of storage. When the as-obtained LNPs were used as a sustained-release agent for amikacin sulfate, the encapsulation efficiency reached over 70% and the release efficiency within 40 h reached 69.2% in a pH 5.5 buffer. Subsequently, the remaining PHL that contains saccharides was directly used for LA production under the catalysis of p -TsOH. At 150 °C for 1.5 h, the LA yield reached 58.4% and remained at 56% after 5 cycles of p -TsOH. It is worth noting that only p -TsOH was used as a reactive reagent throughout the entire preparation process. Overall, this study provided a novel pathway for the integrated utilization of PHL and showed the immense potential of the preparation and application of LNPs.

Here, we describe the all-aqueous bicontinuous emulsions with cholesteric liquid crystal domains through hierarchical colloidal self-assembly of nanoparticles. This is achieved by homogenization of a rod-like cellulose nanocrystal (CNC) with two immiscible, phase separating polyethylene glycol (PEG) and dextran polymer solutions. The dispersed CNCs exhibit unequal affinity for the binary polymer mixtures that depends on the balance of osmotic and chemical potential between the two phases. Once at the critical concentration, CNC particles are constrained within one component of the polymer phases and self-assemble into a cholesteric organization. The obtained liquid crystal emulsion demonstrates a confined three-dimensional percolating bicontinuous network with cholesteric self-assembly of CNC within the PEG phase; meanwhile, the nanoparticles in the dextran phase remain isotropic instead. Our results provide an alternative way to arrest bicontinuous structures through intraphase trapping and assembling of nanoparticles, which is a viable and flexible route to extend for a wide range of colloidal systems.

Cellulose nanocrystals (CNCs) offer excellent mechanical properties. However, measuring the strength by performing reliable experiments at the nanoscale is challenging. In this paper, we model Iβ crystalline cellulose using reactive molecular dynamics simulations. Taking the fibril twist into account, structural changes and hydrogen-bonding characteristics of CNCs during the tensile test are inspected and the failure mechanism of CNCs is analyzed down to the scale of individual bonds. The C4-O4 glycosidic bond is found to be responsible for the failure of CNCs. Finally, the effect of strain rate on ultimate properties is analyzed and a nonlinear model is used to predict the ultimate strength of 9.2 GPa and ultimate strain of 8.5% at a 1 s -1 strain rate. This study sheds light on the applications of cellulose in nanocomposites and further modeling of cellulose nanofibres.

Cellulose nanocrystals (CNC) are green, safe, and renewable nanomaterials with a variety of excellent performances but their morphologies are notoriously difficult to control as this is unfavorable to the diversification of the end products. Allomorphic conversion plays an important role in diversifying the morphology of CNC. However, this further complicates the prediction, design, and control of the geometric dimensions of CNC. Herein, allomorphically modified cellulose (mercerized cellulose, ethylenediamine (EDA)-treated cellulose, and ball-milled cellulose) is designed and used as the starting material for CNC isolation. Subsequently, the morphological evolution of cellulose particles during acid hydrolysis is traced by scanning electron microscopy observations. A mechanism that facilitates further understanding of CNC shaping during sulfuric acid hydrolysis is proposed. According to the CNC shaping mechanism, precise prediction, design, and efficient control of the morphology of CNC (needle-like, ribbon-like, ellipsoid, and spherical) can be realized. CNC with various morphologies are favorable for their applications, such as templating synthesis of porous materials and Pickering emulsion dispersion.

Thehighly efficient utilization of lignin is of great importance for the development of the biorefinery industry. Herein, a novel "core-shell" lignin nanoparticle (LNP) with a diameter of around 135 nm was prepared, after the lignin was isolated from the effluent of formic acid fractionation via dialysis. In an attempt to endow composite materials with vital functionalities, the LNP was added to the starch film and the starch/polyvinyl alcohol (PVA) or starch/polyethylene oxide (PEO) composite film. The results showed that the hydrophobicity performance of the synthesized films was enhanced significantly. Specifically, the dynamic water contact angle value of the starch/PVA composite film with 1% (wt) addition of LNPs could be maintained as high as 122° for 180 s; the starch/PEO composite film also achieved an excellent water contact angle above 120°. The addition of LNPs promoted the formation of some rough structures on the film surface, as shown by the scanning electron microscopy images, which could repel the water molecules efficiently and are closely related to the enhanced hydrophobicity of the starch film. What is more, the as-prepared LNP conferred strengthened thermal stability and ultraviolet blocking properties on the starch composite film. The structural combination of the polymer film with LNPs holds the promise for providing advanced functionalities to the composite material with wide applications.

As a natural antitumor drug, curcumin (CUR) has received increasing attention from researchers and patients due to its various medicinal properties. However, currently CUR is still restricted due to its low and stand-alone therapeutic effects that seriously limit its clinical application. Here, by using cellulose nanocrystals (CNCs) as a nanocarrier to load CUR and AuNPs simultaneously, we developed a hybrid nanoparticle as a codrug delivery system to enhance the low and stand-alone therapeutic effects of CUR. Aided with the encapsulation of β-cyclodextrin (βCD), both the solubility and the stability of CUR are greatly enhanced (solubility increased from 0.89 to 131.7 μg/mL). Owing to the unique rod-like morphology of CNCs, the system exhibits an outstanding loading capacity of 31.4 μg/mg. Under the heat effects of coloaded AuNPs, the system demonstrates a high release rate of 77.63%. Finally, with CNC as a bridge nanocarrier, all aforementioned functions were integrated into one hybrid nanoparticle. The all-in-one integration ensures CUR to have enhanced therapeutic effects and enables the delivery system to exhibit combined chemo-photothermal therapy outcomes. This work presents a significant step toward CUR's clinical application and provides a new strategy for effective and integrative treatment of tumor disease.

The fabrication of biomimetic photonic materials with environmental stimuli-responsive functions from entirely biobased materials is becoming increasingly challenging with the growing demand for biodegradable materials. Herein, the effect of glucan with different molecular weights on the mechanical performance and tunable structural color of iridescent CNC composite films was investigated. The existence of glucan did not influence the self-assembly performance of CNCs, but rather led to an improvement in the mechanical performance, enabling cholesteric CNC composite films with an adjustable structural color. Simultaneously, the iridescent films showed a conspicuous redshift and enlarged initial pitch without obstruction of the chiral structure. In response to environmental humidity, the structural colors of the iridescent composite films can be changed by regulating their chiral nematic structure. In particular, the films demonstrate a reversible structural color change between blue and red at RH between 50 and 98%. The resulting biobased iridescent composite films have potential applications in decorative coating, optical and humidity sensing, and anticounterfeiting.

Cellulose hydrolysis is an extensively studied process due to its relevance in the fields of biofuels, chemicals production, and renewable nanomaterials. However, the direct visualization of the process accompanied with detailed scaling has not been reported because of the vast morphological alterations occurring in cellulosic fibers in typical heterogeneous (solid/liquid) hydrolytic systems. Here, we overcome this distraction by exposing hardwood cellulose nanofibers (CNFs) deposited on silica substrates to pressurized HCl gas in a solid/gas system and examine the changes in individual CNFs by atomic force microscopy (AFM). The results revealed that hydrolysis proceeds via an intermediate semi-fibrous stage before objects reminiscent of cellulose nanocrystals were formed. The length of the nanocrystal-like objects correlated well with molar mass, as analyzed by gel permeation chromatography, performed on CNF aerogels hydrolyzed under identical conditions. Meanwhile, X-ray diffraction showed a slight increase in crystallinity index as the hydrolysis proceeded. The results provide a modern visual complement to >100 years of research in cellulose degradation.

Cellulose nanocrystals (CNCs), having a high specific surface area and versatile surface chemistry, provide considerable potential to interact by various mechanisms with enzymes for nano-immobilization purposes. However, engineering chemically safe CNCs, suitable for edible administrations, presents a significant challenge. A reliable carboxylate form of H-CNCs was formed using H 2 O 2 oxidation of softwood pulp under mild thermal conditions. Negatively charged carboxyl groups (∼0.9 mmol g -1 ) played a key role in lysozyme immobilization via electrostatic interactions and covalent linkages, as evidenced by Fourier transform infrared and 13 C cross-polarization magic angle spinning nuclear magnetic resonance spectroscopies. Adsorption isotherms showed a high loading capacity of H-CNCs (∼240 mg g -1 ), and fitting the data to the Langmuir model confirmed monolayer coverage of lysozyme on their surface. Using a non-toxic coupling agent, 4-(4,6-dimethoxy-1,3,5-triazin-2-yl)-4-methylmorpholinium chloride, lysozyme-conjugated H-CNCs were developed with an immobilization yield of ∼65% and relative catalytic activity of ∼60%, similar to lysozyme adsorption on H-CNCs. These H-CNC-lysozyme nanohybrids, rationally processed via safe and green strategies, are specifically exploitable as catalytically active emulsifiers in food and pharmaceutical sectors.

Biodegradable and renewable materials, such as cellulose nanomaterials, have been studied as a replacement material for traditional plastics in the biomedical field. Furthermore, in chronic wound care, modern wound dressings, hydrogels, and active synthetic extracellular matrices promoting tissue regeneration are developed to guide cell growth and differentiation. Cells are guided not only by chemical cues but also through their interaction with the surrounding substrate and its physicochemical properties. Hence, the current work investigated plant-based cellulose nanomaterials and their surface characteristic effects on human dermal fibroblast (HDF) behavior. Four thin cellulose nanomaterial-based coatings produced from microfibrillar cellulose (MFC), cellulose nanocrystals (CNC), and two TEMPO-oxidized cellulose nanofibers (CNF) with different total surface charge were characterized, and HDF viability and adhesion were evaluated. The highest viability and most stable adhesion were on the anionic CNF coating with a surface charge of 1.14 mmol/g. On MFC and CNC coated surfaces, HDFs sedimented but were unable to anchor to the substrate, leading to low viability.

A green and facile method was designed to isolate a type of cellulose nanocrystal (CNC) with carboxylated surfaces from native cellulose materials. Because isolation and modification processes of cellulosic particles are generally performed separately using harmful chemicals and multiple steps, the one-pot approach employed in this work is interesting from both an economical and ecological point of view. The reaction is carried out by adding hydrogen peroxide as an oxidant and copper(II) sulfate as a catalyst in acidic medium under mild thermal conditions. The charge content of the carboxylated CNC is about 1.0 mmol g -1 , measured by a conductometric titration. Fourier transform infrared spectroscopy also proved the presence of carboxyl groups on the CNC particles. Atomic force microscopy along with optical polarized microscopy readily showed a rod shape morphology for the cellulosic particles. An average length of 263 nm and width of 23 nm were estimated by transmission electron microscopy. Dynamic laser scattering on carboxylated CNC suspensions by adding salt confirmed that nanoparticles are electrostatically stable. Carboxylated CNCs were furthermore characterized by solid carbon-13 nuclear magnetic resonance and X-ray spectroscopy.

Lignin is a vastly underutilized biomass resource. The preparation of water-dispersed lignin nanoparticles is an effective way to realize the high-value utilization of lignin. However, the currently reported preparation methods of lignin nanoparticles still have some drawbacks, such as the requirement for toxic organic solvent or chemical modification, complicated operation process, and poor dispersibility. Here, lignin/sodium dodecyl sulfate (SDS) composite nanoparticles (LSNPs) with outstanding water dispersibility and a size range of 70-200 nm were facilely prepared via acidifying the mixed basic solution of alkaline lignin and SDS. No harsh chemical was needed. The formation mechanism was systematically studied. Results indicated that the LSNPs were obtained by acid precipitation of the mixed micelles formed by the self-assembly of lignin and SDS. In addition, on the basis of the LSNP-stabilized Pickering emulsions, lignin/polyurea composite microcapsules combining the excellent chemical stability of a synthetic polyurea shell with the fantastic antiphotolysis and antioxidant properties of lignin were successfully prepared.

We present an approach to construct biocompatible and photoluminescent hybrid materials comprised of carbon quantum dots (CQDs) and TEMPO-oxidized cellulose nanocrystals (TO-CNCs). First, the amino-functionalized carbon quantum dots (NH 2 -CQDs) were synthesized using a simple microwave method, and the TO-CNCs were prepared by hydrochloric acid (HCl) hydrolysis followed by TEMPO-mediated oxidation. The conjugation of NH 2 -CQDs and TO-CNCs was conducted via carbodiimide-assisted coupling chemistry. The synthesized TO-CNC@CQD hybrid nanomaterials were characterized using X-ray photoelectron spectroscopy, cryo-transmittance electron microscopy, confocal microscopy, and fluorescence spectroscopy. Finally, the interactions of TO-CNC@CQD hybrids with HeLa and RAW 264.7 macrophage cells were investigated in vitro. Cell viability tests suggest the surface conjugation with NH 2 -CQDs not only improved the cytocompatibility of TO-CNCs, but also enhanced their cellular association and internalization on both HeLa and RAW 264.7 cells after 4 and 24 h incubation.

The temperature-dependence of xyloglucan (XG) adsorption onto smooth cellulose model films regenerated from N-methylmorpholine N-oxide (NMMO) was investigated using surface plasmon resonance spectroscopy, and it was found that the adsorbed amount increased with increasing temperature. This implies that the adsorption of XG to NMMO-regenerated cellulose is endothermic and supports the hypothesis that the adsorption of XG onto cellulose is an entropy-driven process. We suggest that XG adsorption is mainly driven by the release of water molecules from the highly hydrated cellulose surfaces and from the XG molecules, rather than through hydrogen bonding and van der Waals forces as previously suggested. To test this hypothesis, the adsorption of XG onto cellulose was studied using cellulose films with different morphologies prepared from cellulose nanocrystals (CNC), semicrystalline NMMO-regenerated cellulose, and amorphous cellulose regenerated from lithium chloride/dimethylacetamide. The total amount of high molecular weight xyloglucan (XGHMW) adsorbed was studied by quartz crystal microbalance and reflectometry measurements, and it was found that the adsorption was greatest on the amorphous cellulose followed by the CNC and NMMO-regenerated cellulose films. There was a significant correlation between the cellulose dry film thickness and the adsorbed XG amount, indicating that XG penetrated into the films. There was also a correlation between the swelling of the films and the adsorbed amounts and conformation of XG, which further strengthened the conclusion that the water content and the subsequent release of the water upon adsorption are important components of the adsorption process.

In this work, we take advantage of the rod-like structure of electrosterically stabilized nanocrystalline cellulose (ENCC, with a width of about 7 nm and a length of about 130 nm), which has dicarboxylated cellulose (DCC) chains protruding from both ends, providing electrosterical stability for ENCC particles, to chemically end-to-end assemble these particles into nanocellulose fibers. ENCC with shorter DCC chains can be obtained by a mild hydrolysis of ENCC with HCl, and subsequently the hydrolyzed ENCC (HENCC, with a width of about 6 nm and a length of about 120 nm) is suitable to be assembled into high aspect ratio nanofibers by chemically cross-linking HENCC from one end to another. Two sets of HENCC were prepared by carbodiimide-mediated formation of an alkyne and an azide derivative, respectively. Cross-linking these two sets of HENCC was performed by a click reaction. HENCCs were also end-to-end cross-linked by a bioconjugation reaction, with a diamine. From atomic force microscopy (AFM) images, about ten HENCC nanoparticles were cross-linked and formed high aspect ratio nanofibers with a width of about 6 nm and a length of more than 1 μm.

The complexation of nanoparticles in unheated and heated (at 75-95°) soy protein isolate (SPI) with curcumin and the effects on curcumin stability/bioaccessibility and in vitro protein digestibility were investigated. The nanoparticles did not display noticeable changes in size and morphology upon nanocomplexation with curcumin, except their surface hydrophobicity. The encapsulation efficiency of curcumin progressively decreased with increasing initial curcumin concentration in the dispersion, while the load amount linearly increased. The solubility of curcumin in water was enhanced by the complexation above 98000-fold (vs free curcumin in water). The formation of the nanocomplexes considerably improved the storage stability of curcumin. In vitro simulated digestion experiments indicated that the complexation also improved the bioaccessibility of curcumin; the bioaccessibility was greatly impaired by hydrolysis-induced protein aggregation. Addtionally, the nanocomplexation significantly improved the in vitro protein digestibility of both unheated and heated SPI.

Polysaccharide nanocrystals with a rodlike shape but with different dimensions and specific surface area were prepared from cotton and capim dourado cellulose, and with a plateletlike morphology from waxy maize starch granules. The rheological behavior of aqueous solutions of poly(ethylene oxide) (PEO) with different molecular weights when adding these nanoparticles was investigated evidencing specific interactions between PEO chains and nanocrystals. Because PEO also bears hydrophobic moieties, it was employed as a compatibilizing agent for the melt processing of polymer nanocomposites. The freeze-dried mixtures were used to prepare nanocomposite materials with a low density polyethylene matrix by extrusion. The thermal and mechanical behavior of ensuing nanocomposites was studied.

The interfacial and emulsifying properties of soy protein isolate nanoparticles formed by combined treatments of heating and electrostatic screening, as affected by variation of the protein concentration (c) and emulsification process, were investigated. These nanoparticles (with a z-average diameter of 103 nm at c = 0.1%, w/v) tended to aggregate at higher c values, and their internal structure was mainly maintained by hydrophobic interactions and disulfide bondings. In general, increasing c progressively favored diffusion and/or adsorption at the interface and formation of finer emulsions; increasing the energy input level of emulsification improved the emulsification efficiency and extent of droplet flocculation, as well as the emulsion coalescence and creaming stability. The rheological and creaming behavior of these emulsions was predominately determined by the amount of proteins adsorbed at the interface. The results confirmed that these nanoparticles can formulate Pickering emulsions with properties tailored by selecting c and the emulsification process.

In recent years, there have been increasing interests in developing food-grade Pickering stabilizers, due to their potential applications in formulations of novel functional foods. The present work was to investigate the potential of soy proteins to be developed into a kind of Pickering-like stabilizer for oil-in-water emulsions. The nanoparticle aggregates of soy protein isolate (SPI) were formed by sequential treatments of heating at 95 °C for 15 min and then electrostatic screening with NaCl addition. The particle size and microstructure of these aggregates were characterized using dynamic light scattering and atomic force microscopy, indicating that the fabricated nanoparticle aggregates were ∼100 nm in size with more surface hydrophobic nature (relative to unheated SPI). The influence of particle concentration (c; 0.5-6.0%, w/w) and increasing oil fraction (ϕ; in the range 0.2-0.6) on the droplet size and coalescence and/or creaming stability of the emulsions stabilized by these nanoparticle aggregates was investigated. The results showed that, at ϕ = 0.2, increasing the c resulted in a progressive but slight decrease in droplet size, and improved the stability against coalescence and creaming; at a specific c, the creaming stability was progressively increased by increasing the ϕ, with better improvement observed at a higher c (e.g., 6.0% vs 2.0%). The improvement of creaming stability was largely associated with the formation of a gel-like network that could entrap the oil droplets within the network. The observations are generally consistent with those observed for the conventional Pickering emulsions, confirming that soy proteins could be applied as a kind of effective Pickering-like stabilizer. The finding may have important implications for the design and fabrication of protein-based emulsion formulations, and even for the development of soy protein products with some unique functions. To the authors' knowledge, this is the first work to report that heat-induced soy protein aggregates exhibit a good potential to act as Pickering-type stabilizers.

When grafted β-cyclodextrin is used as targeting sites, Pluronic polymers have been introduced on the surface of cellulose nanocrystals by means of inclusion interaction between β-cyclodextrin and hydrophobic segment of the polymer. Because of the steric stabilization effect, surface poly(ethylene glycol) chains facilitate the dispersion and compatibility of nanocrystals, which also enhance the loading levels of nanocrystals in the hydrogel system. Meanwhile, uncovered poly(ethylene glycol) segments render the participating inclusion of α-cyclodextrin for the architecture of in situ hydrogels. Surface grafting and inclusion reactions were proved by solid (13)C NMR and FTIR. Grafting efficiency of β-cyclodextrin and inclusion efficiency of Pluronic on the surface of nanocrystals were confirmed by UV spectroscopy and elemental analysis. A significant enhancement of the structural and thermal stability of in situ hydrogels with high loading levels of modified nanocrystals (>5.77 wt %) was observed by rheological analysis. Further study reveals the performance and behavior of hydrogels under a different pH environment. Finally, in situ hydrogels were used as drug carrier for in vitro release of doxorubicin and exhibit the behavior of prolonged drug release with special release kinetics.

Crosslinked polysaccharide sponges have been prepared by freeze-drying of amorphous alginate-oxidized nanocellulose in the presence of a Ca(2+) ionic crosslinking agent. The new carboxyl groups on the surface of nanocellulose induced by the chemical oxidization provided the possibility of participating in the construction of an alginate-based sponge's structure and played a fundamental role in the structural and mechanical stability of ensuing sponges. Furthermore, enhanced mechanical strength induced by oxidized cellulose nanocrystals and the formation of a semi-interpenetrating polymer network from oxidized microfibrillated cellulose were reported. Together with the facile and ionic crosslinking process, the ultrahigh porosity, promising water absorption and retention, as well as the improved compression strength of the crosslinked sponges should significantly extend the use of this soft material in diverse practical applications.

Electrosterically stabilized nanocrystalline cellulose (ENCC) was modified in three ways: (1) the hydroxyl groups on C2 and C3 of glucose repeat units of ENCC were converted to aldehyde groups by periodate oxidation to various extents; (2) the carboxyl groups in the sodium form on ENCC were converted to the acid form by treating them with an acid-type ion-exchange resin; and (3) ENCC was cross-linked in two different ways by employing adipic dihydrazide as a cross-linker and water-soluble 1-ethyl-3-[3-(dimethylaminopropyl)] carbodiimide as a carboxyl-activating agent. Films were prepared from these modified ENCC suspensions by vacuum filtration. The effects of these three modifications on the properties of films were investigated by a variety of techniques, including UV-visible spectroscopy, a tensile test, thermogravimetric analysis (TGA), the water vapor transmission rate (WVTR), and contact angle (CA) studies. On the basis of the results from UV spectra, the transmittance of these films was as high as 87%, which shows them to be highly transparent. The tensile strength of these films was increased with increasing aldehyde content. From TGA and WVTR experiments, cross-linked films showed much higher thermal stability and lower water permeability. Furthermore, although the original cellulose is hydrophilic, these films also exhibited a certain hydrophobic behavior. Films treated by trichloromethylsilane become superhydrophobic. The unique characteristics of these transparent films are very promising for potential applications in flexible packaging and other high-technology products.

Starch nanocrystals (SNCs) are crystalline platelets resulting from the acid hydrolysis of starch. A limiting factor for their more widespread use is their preparation duration. Therefore, this study investigates the possibility of developing an enzymatic pretreatment of starch to reduce the acid hydrolysis duration. A screening of three types of enzymes, namely, α-amylase, β-amylase, and glucoamylase, is proposed, and the latter was selected for a pretreatment. Compared with the regular kinetics of hydrolysis for preparing SNC, that of pretreated starch was much faster. The extent of hydrolysis normally reached in 24 h was obtained after only 6 h, and the regular final yield (15% after 5 days) was reached in 45 h. AFM and X-ray diffraction measurements confirmed that the obtained nanoparticles were indeed SNC.

Great work has been done to reduce the batch production time of starch nanocrystals (SNCs) and improve their compatibilization with different matrices. However, only one study was reported on SNC production kinetics and none on size distributions and isolation techniques. This study was designed to assess if nonsolubilized particles in the hydrolyzed starch suspension reflect the actual amount of SNC. It was observed that SNCs are produced from a very early stage. It suggests, for the first time, that (i) nanocrystals are mixed together with other microparticles and (ii) some nanocrystals might turn to sugar by the end of the batch production process explaining the low yields. An isolation process has been proposed, but limits of differential centrifugations as washing step and isolation technique were also evidenced. This study clearly shows the need for a continuous production and extraction process of SNC.

Starch is a natural, renewable, and biodegradable polymer produced by many plants as a source of stored energy. It is the second most abundant biomass material in nature. The starch structure has been under research for years, and because of its complexity, an universally accepted model is still lacking (Buleon, A.; et al. Int. J. Biol. Macromol. 1998, 23, 85-112). However, the predominant model for starch is a concentric semicrystalline multiscale structure that allows the production of new nanoelements: (i) starch nanocrystals resulting from the disruption of amorphous domains from semicrystalline granules by acid hydrolysis and (ii) starch nanoparticles produced from gelatinized starch. This paper intends to give a clear overview of starch nanoparticle preparation, characterization, properties, and applications. Recent studies have shown that they could be used as fillers to improve mechanical and barrier properties of biocomposites. Their use for industrial packaging, continuously looking for innovative solutions for efficient and sustainable systems, is being investigated. Therefore, recently, starch nanoparticles have been the focus of an exponentially increasing number of works devoted to develop biocomposites by blending starch nanoparticles with different biopolymeric matrices. To our knowledge, this topic has never been reviewed, despite several published strategies and conclusions.

Cellulose nanocrystals (or whiskers) and microfibrillated cellulose (MFC) were successfully obtained from sisal fibers and modified with n-octadecyl isocyanate (C(18)H(37)NCO) using two different methods with one innovation that consists of an in situ solvent exchange procedure. The surface chemical modification was characterized by elemental analysis, as well as FTIR and XPS spectroscopies. The crystalline structure of both unmodified and modified nanoparticles was investigated through X-ray diffraction measurements. It was shown that the efficiency of the chemical modification is strongly dependent on the nature of the nanoparticle with explanation linked to specific area, ability of peeling, and solvent dispersion. The surface chemical modification with n-octadecyl isocyanate allows dispersion of the nanoparticles in organic solvents and may allow processing of nanocomposite films from a casting/evaporation technique for a broad range of polymeric matrices.

We report herein for the first time how a co-electrospinning technique can be used to overcome the issue of orienting cellulose nanocrystals within a neat cellulose matrix. A home-built co-electrospinning apparatus was fabricated that was comprised of a high-voltage power supply, two concentric capillary needles, and one screw-type pump syringe. Eucalyptus-derived cellulose was dissolved in N-methylmorpholine oxide (NMMO) at 120 degrees C and diluted with dimethyl sulfoxide (DMSO) which was used in the external concentric capillary needle as the shell solution. A cellulose nanocrystal suspension obtained by the sulfuric acid hydrolysis of bleached sisal and cotton fibers was used as the core liquid in the internal concentric capillary needle. Three flow rate ratios between the shell and core, four flow rates for the shell dope solution, and four high voltages were tested. The resultant co-electrospun composite fibers were collected onto a grounded metal screen immersed in cold water. Micrometer and submicrometer cellulose fiber assemblies were obtained which were reinforced with cellulose nanocrystals and characterized by FESEM, FTIR, TGA, and XRD. Surprisingly, it was determined that the physical properties for the cellulose controls are superior to the composites; in addition, the crystallinity of the controls was slightly greater.

In the present work, nanowhiskers and microfibrillated cellulose (MFC) both extracted from sisal were used to reinforce polycaprolactone (PCL). We report the influence of the nanoparticle's nature on the mechanical and thermal properties of the ensuing nanocomposites. The surface of both the nanoparticles was chemically modified to improve their compatibilization with the polymeric matrix. N-Octadecyl isocyanate (C18H37NCO) was used as the grafting agent. PCL nanocomposite films reinforced with sisal whiskers or MFC (raw or chemically modified) were prepared by film casting. The thermal behavior (Tg, Tm, Tc, and degree of crystallinity) and the mechanical properties of the nanocomposites in both the linear and the nonlinear range were determined using differential scanning calorimetry (DSC), dynamical mechanical analysis (DMA), and tensile tests, respectively. Significant differences were reported according to the nature of the nanoparticle and amount of nanofillers used as reinforcement. It was also proved that the chemical treatment clearly improves the ultimate properties of the nanocomposites.

Photoactive TiO(2) can be used to mediate a variety of disinfection processes. It was postulated that TiO(2) particles could be directed to specific targets of interest using biotin/streptavidin linkages. Biotinylated TiO(2) nanoparticles (anatase) were obtained by treating TiO(2) nanoparticles with 3-aminopropyltriethoxysilane (APTS) in anhydrous DMSO, followed by reaction with N-hydroxysuccinimidobiotin. 29Si CP-MAS NMR, 13C CP-MAS NMR, and FTIR spectra showed that biotin was covalently bound to the TiO(2) surface. Transmission electron microscopy (TEM) demonstrated that prolonging the silanization reaction times led to increasingly thick silsesquioxane coating layers of up to approximately 10 nm. The specific surface area (SSA) of the TiO2 particles decreased from 16 m(2) g(-1) before treatment to 9.1 m(2) g(-1) after aminosilanization and to 8.4 m(2) g(-)1 after biotinylation, as measured by nitrogen adsorption. Amino surfaces modified for 4, 16, and 26 h had total amino group densities ranging from 2.9 to 26 to 66 nm(-2), respectively, whereas accessible surface amino group densities ranged from 2.7 to 10 to 17 nm(-2) as shown from nitrogen adsorption, polyelectrolyte titration, conductometric titration, and biotin assays. Not all the amino groups were accessible for biotinylation: the densities of active biotin were found to be 2.1, 7.0, and 11.5 nm(-2). The ability of the attached biotin to bind to streptavidin was demonstrated by confocal microscopy with the use of fluorescently labeled streptavidin-FITC. Although streptavidin was readily able to bind to biotinylated TiO(2) particles, it did not act as a strong flocculating agent for the biotinylated TiO2 particles. The implications of these observations, with respect to particle accessibility to tethered streptavidin, are discussed.