Shape-memory polymers (SMPs) can be defined as a reversibly changing form through deformation and recovery by external stimuli. However, there remain application limitations of SMPs, such as complicated preparation processes and slow shape recovery. Here, we designed gelatin-based shape-memory scaffolds by a facile dipping method in tannic acid solution. The shape-memory effect of scaffolds was attributed to the hydrogen bond between gelatin and tannic acid, which acts as the net point. Moreover, gelatin (Gel)/oxidized gellan gum (OGG)/calcium chloride (Ca) was intended to induce faster and more stable shape-memory behavior through the introduction of a Schiff base reaction. The chemical, morphological, physicochemical, and mechanical properties of the fabricated scaffolds were evaluated, and those results showed that the Gel/OGG/Ca had improved mechanical properties and structural stability compared with other scaffold groups. Additionally, Gel/OGG/Ca exhibited excellent shape-recovery behavior of 95.8% at 37 °C. As a consequence, the proposed scaffolds can be fixed to the temporary shape at 25 °C in just 1 s and recovered to the original shape at 37 °C within 30 s, implying a great potential for minimally invasive implantation., Competing Interests: The authors declare no competing financial interest., (© 2023 The Authors. Published by American Chemical Society.)

To improve the mechanical properties of collagen hydrogels, which are widely utilized as biomaterials, post-cross-linking of collagen hydrogels was performed using polyrotaxane (PRX) as a cross-linker. Herein, carboxymethyl group-modified PRXs (CMPRs) composed of carboxymethylated α-cyclodextrins (α-CDs) threaded along poly(ethylene glycol) (PEG) capped with bulky stoppers were used to cross-link via reaction with the amino groups in the collagen. Four series of CMPRs with different α-CD threading ratios and axle PEG molecular weights were used for the post-cross-linking of the collagen hydrogels to verify the optimal CMPR chemical compositions. The post-cross-linking of the collagen hydrogels with CMPRs improved the swelling ratios and mechanical properties, such as viscoelasticity and tensile strength. Among the tested CMPRs, CMPRs with an axle PEG molecular weight of 35,000 (PEG35k) resulted in better mechanical properties than CMPRs with a PEG10k axis. Additionally, the cell adhesion and proliferation were greatly improved on the surface of the collagen hydrogels post-cross-linked with CMPRs with the PEG35k axle. These findings suggest that the molecular weight of an axle polymer in CMPRs is a more important parameter than the α-CD threading ratios. Accordingly, the post-cross-linking of hydrogels with PRXs is promising for improving the mechanical properties and biomaterial functions of collagen hydrogels.