Search

Characterizing materials at small scales presents major challenges in the engineering of nanocomposite materials having a high specific surface area. Here, we show the application of electron tomography to describe the three-dimensional structure of highly ordered TiO 2 nanotube arrays modified with Pt nanoparticles. The titanium oxide nanotubes were prepared by the electrochemical anodization of a Ti substrate after which Pt was deposited by magnetron sputtering. Such a composite shows high electrochemical activity that depends on the amount of the metal and the morphological parameters of the microstructure. However, a TiO 2 structure modified with metallic nanoparticles has never been visualized in 3D, making it very difficult to understand the relationship between electrocatalytic activity and morphology. In this paper, TiO 2 nanotubes of different sizes and different amounts of Pt were analyzed using the electron microscopy technique. Electrocatalytic activity was studied using the cyclic voltammetry (CV) method. For selected samples, electron tomography 3D structure reconstruction was performed to describe their fine microstructure. The highest activity was detected in the sample having bigger nanotubes (25 V) where the porosity of the structure was high and the Pt content was 0.1 mg cm -2 . 3D imaging using electron tomography opens up new possibilities in the design of electrocatalytic materials.

Titanium oxide nanotube layers with silver and zinc nanoparticles are attracting increasing attention in the design of bone and dental implants due to their antimicrobial potential and their ability to control host cell adhesion, growth, and differentiation. However, recent reports indicate that the etiology of dental infections is more complex than has been previously considered. Therefore, the antimicrobial potential of dental implants should be evaluated against at least several different microorganisms cooperating in human mouth colonization. In this study, Ag and Zn nanoparticles incorporated into titanium oxide nanotubular layers were studied with regard to how they affect Candida albicans, Candida parapsilosis, and Streptococcus mutans. Layers of titanium oxide nanotubes with an average diameter of 110 nm were fabricated by electrochemical anodization, annealed at 650 °C, and modified with approx. 5 wt % Ag or Zn nanoparticles. The surfaces were examined with the scanning electron microscopy-energy dispersive X-ray analysis, scanning transmission electron microscopy, and X-ray photoelectron spectroscopy techniques and subjected to evaluation of microbial-killing and microbial adhesion-inhibiting potency. In a 1.5 h long adhesion test, the samples were found more effective toward yeast strains than toward S. mutans. In a release-killing test, the microorganisms were almost completely eliminated by the samples, either within 3 h of contact (for S. mutans) or 24 h of contact (for both yeast strains). Although further improvement is advisable, it seems that Ag and Zn nanoparticles incorporated into TiO 2 nanotubular surfaces provide a powerful tool for reducing the incidence of bone implant infections. Their high bidirectional activity (against both Candida species and S. mutans) makes the layers tested particularly promising for the design of dental implants.