12 results on '"Sápi, András"'
Search Results
2. Optimized Pt–Co Alloy Nanoparticles for Reverse Water–Gas Shift Activation of CO2.
- Author
-
Szamosvölgyi, Ákos, Pitó, Ádám, Efremova, Anastasiia, Baán, Kornélia, Kutus, Bence, Suresh, Mutyala, Sápi, András, Szenti, Imre, Kiss, János, Kolonits, Tamás, Fogarassy, Zsolt, Pécz, Béla, Kukovecz, Ákos, and Kónya, Zoltán
- Abstract
Different Co contents were used to tune bimetallic Pt–Co nanoparticles with a diameter of 8 nm, resulting in Pt:Co ratios of 3.54, 1.51, and 0.96. These nanoparticles were then applied to the MCF-17 mesoporous silica support. The synthesized materials were characterized with HR-TEM, HAADF-TEM, EDX, XRD, BET, ICP-MS, in situ DRIFTS, and quasi in situ XPS techniques. The catalysts were tested in a thermally induced reverse water–gas shift reaction (CO
2 :H2 = 1:4) at atmospheric pressure in the 200–700 °C temperature range. All bimetallic Pt–Co particles outperformed the pure Pt benchmark catalyst. The nanoparticles with a Pt:Co ratio of 1.51 exhibited 2.6 times higher activity and increased CO selectivity by 4% at 500 °C. Experiments proved that the electron accumulation and alloying effect on the Pt–Co particles are stronger with higher Co ratios. The production of CO followed the formate reaction pathway on all catalysts due to the face-centered-cubic structure, which is similar to the Pt benchmark. It is concluded that the enhanced properties of Co culminate at a Pt:Co ratio of 1.51 because decreasing the ratio to 0.96 results in lower activity despite having more Co atoms available for the electronic interaction, resulting in the lack of electron-rich Pt sites. [ABSTRACT FROM AUTHOR]- Published
- 2024
- Full Text
- View/download PDF
3. Highly Porous Polymer Beads Coated with Nanometer-Thick Metal Oxide Films for Photocatalytic Oxidation of Bisphenol A.
- Author
-
Ballai, Gergő, Kotnik, Tomaž, Finšgar, Matjaž, Pintar, Albin, Kónya, Zoltán, Sápi, András, and Kovačič, Sebastijan
- Abstract
Highly porous metal oxide–polymer nanocomposites are attracting considerable interest due to their unique structural and functional features. A porous polymer matrix brings properties such as high porosity and permeability, while the metal oxide phase adds functionality. For the metal oxide phase to perform its function, it must be fully accessible, and this is possible only at the pore surface, but functioning surfaces require controlled engineering, which remains a challenge. Here, highly porous nanocomposite beads based on thin metal oxide nanocoatings and polymerized high internal phase emulsions (polyHIPEs) are demonstrated. By leveraging the unique properties of polyHIPEs, i.e., a three-dimensional (3D) interconnected network of macropores, and high-precision of the atomic-layer-deposition technique (ALD), we were able to homogeneously coat the entire surface of the pores in polyHIPE beads with TiO
2 -, ZnO-, and Al2 O3 -based nanocoatings. Parameters such as nanocoating thickness, growth per cycle (GPC), and metal oxide (MO) composition were systematically controlled by varying the number of deposition cycles and dosing time under specific process conditions. The combination of polyHIPE structure and ALD technique proved advantageous, as MO-nanocoatings with thicknesses between 11 ± 3 and 40 ± 9 nm for TiO2 or 31 ± 6 and 74 ± 28 nm for ZnO and Al2 O3 , respectively, were successfully fabricated. It has been shown that the number of ALD cycles affects both the thickness and crystallinity of the MO nanocoatings. Finally, the potential of ALD-derived TiO2 -polyHIPE beads in photocatalytic oxidation of an aqueous bisphenol A (BPA) solution was demonstrated. The beads exhibited about five times higher activity than nanocomposite beads prepared by the conventional (Pickering) method. Such ALD-derived polyHIPE nanocomposites could find wide application in nanotechnology, sensor development, or catalysis. [ABSTRACT FROM AUTHOR]- Published
- 2023
- Full Text
- View/download PDF
4. CO2 Conversion on N‑Doped Carbon Catalysts via Thermo- and Electrocatalysis: Role of C–NOx Moieties.
- Author
-
Hursán, Dorottya, Ábel, Marietta, Baán, Kornélia, Fako, Edvin, Samu, Gergely F., Nguyën, Huu Chuong, López, Núria, Atanassov, Plamen, Kónya, Zoltán, Sápi, András, and Janáky, Csaba
- Published
- 2022
- Full Text
- View/download PDF
5. Bioplastics and Carbon-Based Sustainable Materials, Components, and Devices: Toward Green Electronics.
- Author
-
Bozó, Éva, Ervasti, Henri, Halonen, Niina, Shokouh, Seyed Hossein Hosseini, Tolvanen, Jarkko, Pitkänen, Olli, Järvinen, Topias, Pálvölgyi, Petra S., Szamosvölgyi, Ákos, Sápi, András, Konya, Zoltan, Zaccone, Marta, Montalbano, Luana, De Brauwer, Laurens, Nair, Rakesh, Martínez-Nogués, Vanesa, San Vicente Laurent, Leire, Dietrich, Thomas, Fernández de Castro, Laura, and Kordas, Krisztian
- Published
- 2021
- Full Text
- View/download PDF
6. Nesting Well-Defined Pt Nanoparticles within a Hierarchically Porous Polymer as a Heterogeneous Suzuki–Miyaura Catalyst.
- Author
-
Kim, Soobin, Varga, Gábor, Seo, Myungeun, Sápi, András, Rácz, Viktória, Gómez-Pérez, Juan F., Sebők, Dániel, Lee, Jeonghyeon, Kukovecz, Ákos, and Kónya, Zoltán
- Abstract
A hierarchically porous polymer (HPP) consisting of micropores (∼1 nm) within a 3D continuous mesoporous wall (∼15 nm) was used to support well-defined Pt nanoparticles (2 nm in diameter) as a heterogeneous catalyst for the Suzuki–Miyaura cross-coupling reaction in the liquid phase. The ligand-capped nanoparticles were loaded into the polymer and treated with plasma to expose the active surface. The dual porosity was essential: the block polymer-templated mesopores provided the reactants facile access to the nanoparticle center, which was firmly immobilized by the microporous surface. Compared to inorganic mesoporous silica supports, which are intrinsically susceptible to basic hydrolysis, the Pt-HPP featured higher activity for all halide leaving groups, even in green solvents, as well as excellent recyclability. Only 5% decrease in activity was observed after 10 cycles. Pt-HPP was one of the most active heterogeneous catalysts for aryl chloride substrates compared to literature Pt or Pd examples. [ABSTRACT FROM AUTHOR]
- Published
- 2021
- Full Text
- View/download PDF
7. High-Entropy Oxides: A New Frontier in Photocatalytic CO 2 Hydrogenation.
- Author
-
Tatar D, Ullah H, Yadav M, Kojčinović J, Šarić S, Szenti I, Skalar T, Finšgar M, Tian M, Kukovecz Á, Kónya Z, Sápi A, and Djerdj I
- Abstract
Herein, we investigate the potential of nanostructured high-entropy oxides (HEOs) for photocatalytic CO
2 hydrogenation, a process with significant implications for environmental sustainability and energy production. Several cerium-oxide-based rare-earth HEOs with fluorite structures were prepared for UV-light driven photocatalytic CO2 hydrogenation toward valuable fuels and petrochemical precursors. The cationic composition profoundly influences the selectivity and activity of the HEOs, where the Ce0.2 Zr0.2 La0.2 Nd0.2 Sm0.2 O2-δ catalyst showed outstanding CO2 activation (14.4 molCO kgcat -1 h-1 and 1.27 mol CH 3 OH kgcat -1 h-1 ) and high methanol and CO selectivity (7.84% CH3 OH and 89.26% CO) under ambient conditions with 4 times better performance in comparison to pristine CeO2 . Systematic tests showed the effect of a high-entropy system compared to midentropy oxides. XPS, in situ DRIFTS, as well as DFT calculation elucidate the synergistic impact of Ce, Zr, La, Nd, and Sm, resulting in an optimal Ce3+ /Ce4+ ratio. The observed formate-routed mechanism and a surface with high affinity to CO2 reduction offer insights into the photocatalytic enhancement. While our findings lay a solid foundation, further research is needed to optimize these catalysts and expand their applications.- Published
- 2024
- Full Text
- View/download PDF
8. Optimized Pt-Co Alloy Nanoparticles for Reverse Water-Gas Shift Activation of CO 2 .
- Author
-
Szamosvölgyi Á, Pitó Á, Efremova A, Baán K, Kutus B, Suresh M, Sápi A, Szenti I, Kiss J, Kolonits T, Fogarassy Z, Pécz B, Kukovecz Á, and Kónya Z
- Abstract
Different Co contents were used to tune bimetallic Pt-Co nanoparticles with a diameter of 8 nm, resulting in Pt:Co ratios of 3.54, 1.51, and 0.96. These nanoparticles were then applied to the MCF-17 mesoporous silica support. The synthesized materials were characterized with HR-TEM, HAADF-TEM, EDX, XRD, BET, ICP-MS, in situ DRIFTS, and quasi in situ XPS techniques. The catalysts were tested in a thermally induced reverse water-gas shift reaction (CO
2 :H2 = 1:4) at atmospheric pressure in the 200-700 °C temperature range. All bimetallic Pt-Co particles outperformed the pure Pt benchmark catalyst. The nanoparticles with a Pt:Co ratio of 1.51 exhibited 2.6 times higher activity and increased CO selectivity by 4% at 500 °C. Experiments proved that the electron accumulation and alloying effect on the Pt-Co particles are stronger with higher Co ratios. The production of CO followed the formate reaction pathway on all catalysts due to the face-centered-cubic structure, which is similar to the Pt benchmark. It is concluded that the enhanced properties of Co culminate at a Pt:Co ratio of 1.51 because decreasing the ratio to 0.96 results in lower activity despite having more Co atoms available for the electronic interaction, resulting in the lack of electron-rich Pt sites., Competing Interests: The authors declare no competing financial interest., (© 2024 The Authors. Published by American Chemical Society.)- Published
- 2024
- Full Text
- View/download PDF
9. CO 2 Conversion on N-Doped Carbon Catalysts via Thermo- and Electrocatalysis: Role of C-NO x Moieties.
- Author
-
Hursán D, Ábel M, Baán K, Fako E, Samu GF, Nguyën HC, López N, Atanassov P, Kónya Z, Sápi A, and Janáky C
- Abstract
N-doped carbon (N-C) materials are increasingly popular in different electrochemical and catalytic applications. Due to the structural and stoichiometric diversity of these materials, however, the role of different functional moieties is still controversial. We have synthesized a set of N-C catalysts, with identical morphologies (∼27 nm pore size). By systematically changing the precursors, we have varied the amount and chemical nature of N-functions on the catalyst surface. The CO
2 reduction (CO2 R) properties of these catalysts were tested in both electrochemical (EC) and thermal catalytic (TC) experiments (i.e., CO2 + H2 reaction). CO was the major CO2 R product in all cases, while CH4 appeared as a minor product. Importantly, the CO2 R activity changed with the chemical composition, and the activity trend was similar in the EC and TC scenarios. The activity was correlated with the amount of different N-functions, and a correlation was found for the -NOx species. Interestingly, the amount of this species decreased radically during EC CO2 R, which was coupled with the performance decrease. The observations were rationalized by the adsorption/desorption properties of the samples, while theoretical insights indicated a similarity between the EC and TC paths., Competing Interests: The authors declare no competing financial interest., (© 2022 The Authors. Published by American Chemical Society.)- Published
- 2022
- Full Text
- View/download PDF
10. Photoelectrochemistry by Design: Tailoring the Nanoscale Structure of Pt/NiO Composites Leads to Enhanced Photoelectrochemical Hydrogen Evolution Performance.
- Author
-
Sápi A, Varga A, Samu GF, Dobó D, Juhász KL, Takács B, Varga E, Kukovecz Á, Kónya Z, and Janáky C
- Abstract
Photoelectrochemical hydrogen evolution is a promising avenue to store the energy of sunlight in the form of chemical bonds. The recent rapid development of new synthetic approaches enables the nanoscale engineering of semiconductor photoelectrodes, thus tailoring their physicochemical properties toward efficient H
2 formation. In this work, we carried out the parallel optimization of the morphological features of the semiconductor light absorber (NiO) and the cocatalyst (Pt). While nanoporous NiO films were obtained by electrochemical anodization, the monodisperse Pt nanoparticles were synthesized using wet chemical methods. The Pt/NiO nanocomposites were characterized by XRD, XPS, SEM, ED, TEM, cyclic voltammetry, photovoltammetry, EIS, etc. The relative enhancement of the photocurrent was demonstrated as a function of the nanoparticle size and loading. For mass-specific surface activity the smallest nanoparticles (2.0 and 4.8 nm) showed the best performance. After deconvoluting the trivial geometrical effects (stemming from the variation of Pt particle size and thus the electroactive surface area), however, the intermediate particle sizes (4.8 and 7.2 nm) were found to be optimal. Under optimized conditions, a 20-fold increase in the photocurrent (and thus the H2 evolution rates) was observed for the nanostructured Pt/NiO composite, compared to the benchmark nanoparticulate NiO film.- Published
- 2017
- Full Text
- View/download PDF
11. Nitrogen-doped anatase nanofibers decorated with noble metal nanoparticles for photocatalytic production of hydrogen.
- Author
-
Wu MC, Hiltunen J, Sápi A, Avila A, Larsson W, Liao HC, Huuhtanen M, Tóth G, Shchukarev A, Laufer N, Kukovecz Á, Kónya Z, Mikkola JP, Keiski R, Su WF, Chen YF, Jantunen H, Ajayan PM, Vajtai R, and Kordás K
- Subjects
- Catalysis, Ethanol chemistry, Light, Microscopy, Electron, Transmission methods, Palladium chemistry, Platinum chemistry, Time Factors, Ultraviolet Rays, Water chemistry, Hydrogen chemistry, Metal Nanoparticles chemistry, Nanofibers chemistry, Nanotechnology methods, Photochemistry methods, Titanium chemistry
- Abstract
We report the synthesis of N-doped TiO(2) nanofibers and high photocatalytic efficiency in generating hydrogen from ethanol-water mixtures under UV-A and UV-B irradiation. Titanate nanofibers synthesized by hydrothermal method are annealed in air and/or ammonia to achieve N-doped anatase fibers. Depending on the synthesis route, either interstitial N atoms or new N-Ti bonds appear in the lattice, resulting in slight lattice expansion as shown by XPS and HR-TEM analysis, respectively. These nanofibers were then used as support for Pd and Pt nanoparticles deposited with wet impregnation followed by calcination and reduction. In the hydrogen generation tests, the N-doped samples were clearly outperforming their undoped counterparts, showing remarkable efficiency not only under UV-B but also with UV-A illumination. When 100 mg of catalyst (N-doped TiO(2) nanofiber decorated with Pt nanoparticles) was applied to 1 L of water-ethanol mixture, the H(2) evolution rates were as high as 700 μmol/h (UV-A) and 2250 μmol/h (UV-B) corresponding to photo energy conversion percentages of ∼3.6 and ∼12.3%, respectively.
- Published
- 2011
- Full Text
- View/download PDF
12. Three-dimensional carbon nanotube scaffolds as particulate filters and catalyst support membranes.
- Author
-
Halonen N, Rautio A, Leino AR, Kyllönen T, Tóth G, Lappalainen J, Kordás K, Huuhtanen M, Keiski RL, Sápi A, Szabó M, Kukovecz A, Kónya Z, Kiricsi I, Ajayan PM, and Vajtai R
- Abstract
Three-dimensional carbon nanotube scaffolds created using micromachined Si/SiO2 templates are used as nanoparticulate filters and support membranes for gas-phase heterogeneous catalysis. The filtering efficiency of better than 99% is shown for the scaffolds in filtering submicrometer particles from air. In the hydrogenation of propene to propane reaction low activation energy of E(a) approximately 27.8 +/- 0.6 kJ x mol(-1), a considerably high turnover rate of approximately 1.1 molecules x Pd site(-1) x s(-1) and durable activity for the reaction are observed with Pd decorated membranes. It is demonstrated that appropriate engineering of macroscopic-ordered nanotube architectures can lead to multifunctional applications.
- Published
- 2010
- Full Text
- View/download PDF
Catalog
Discovery Service for Jio Institute Digital Library
For full access to our library's resources, please sign in.