Search

A three-component system comprising surfactant molecules and molecularly cross-linked metal centers assembles into nanoring structures. The thickness of the nanorings is determined by the dimensions of the surfactant bilayer while the dimensions of the ring opening depend on and can be regulated by the concentrations of the participating species. Once formed, these organic-inorganic hybrids can be transformed, by air plasma treatment, into all-metal nanorings exhibiting strong adsorption in the near IR.

The Langmuir-Schaefer (LS) technique was applied to prepare two-dimensional films of tridodecylamine (TDA)-stabilized Co nanoparticles. Ethylene glycol was used as the subphase because the Co nanoparticles spread better on it than on water. Surface pressure-area isotherms provided very little information on the floating films, and Brewster angle microscopy (BAM) was needed to characterize the film formation in situ. In addition to the subphase, various other experimental factors were tested in the LS film preparation, including solvent and presence of free TDA ligands and poly(styrene-b-ethylene oxide) (PS-b-PEO) in the nanoparticle dispersion. LS films deposited from dispersions from which the excess TDA ligands had been removed by washing the Co nanoparticles with 2-propanol consisted of hexagonally organized particles in rafts that were organized in necklace structures. The addition of PS-b-PEO to the deposition dispersion resulted in small nanoparticle rafts evenly distributed over the substrate surface. The best Co-nanoparticle-PS-b-PEO films were obtained with a mass ratio of 20:1 between Co (9 nm) and block copolymer (38 200 g/mol, PEO content 22 mass %). These films were successfully transferred onto Formvar-coated TEM grids and characterized by transmission electron microscopy (TEM) and a superconducting quantum interference device (SQUID) magnetometer. At room temperature the films showed superparamagnetic behavior with a saturation magnetization M(s) of 100 emu/g (Co). Our work indicates that it is possible to obtain thin superparamagnetic LS films of TDA-stabilized Co nanoparticles. This is an important result as the TDA-stabilized Co nanoparticles show a very good resistance to corrosion.

Flexible and magnetic artificial cilia were grown on various substrates by a facile bottom-up approach based on template-free magnetic assembly. The magnetic cilia formed spontaneously from a suspension of micrometer-sized ferromagnetic particles and elastomeric polymer in a liquid solvent when dried in an external magnetic field. The cilia mimics were mechanically stable even in the absence of an external magnetic field and a solvent due to the polymer, which acted as "glue" holding the particles together and connecting the cilia to the substrate. The length of the magnetic cilia was in the millimeter range, that is, two to three orders of magnitude times the length of typical biological cilia. The aspect ratio reached values over 100 and was tunable with the magnetic field gradient and the size of the ferromagnetic particles. The cilia mimics responded to an external magnetic field by reversibly bending along the field. The bending actuation was sufficiently powerful to allow two functions: to translate macroscopic nonmagnetic objects placed over the cilia mimics and to mix liquids of even high viscosity. The mechanical properties of the magnetic cilia could be easily tuned by changing the impregnating polymer. The particularly simple template-free construction and fixation on various surfaces suggest applications as an externally controllable surface.