Search

Conductive textiles (CTs) are promising electromagnetic interference (EMI) shielding materials. Nevertheless, limited stretchability and poor reliability restrict their potential applications in stretchable electronic devices because of the rigid conductive networks. Herein, a highly stretchable and reliable CT is developed for effective EMI shielding by designing a deformable liquid-metal (LM) coating and polydimethylsiloxane (PDMS) protective layer. The resultant PDMS-LM/Textile exhibits an outstanding EMI shielding efficiency (EMI SE) of 72.6 dB at a thickness of only 0.35 mm while maintaining EMI SEs of 66.0 and 52.4 dB under strains of 30 and 50%, respectively. The corresponding EMI SEs hold 91.7 and 80.3% retention after 5000 stretching-releasing cycles, respectively. The superior and durable EMI SE should be ascribed to the perfect connectivity and good deformability of conductive LM networks. Moreover, the LM coating has a robust fastness to the textile substrate, without any obvious decrease in EMI SE after 10 min of ultrasonic treatment and 100 peeling cycles because of the protective effect of the PDMS layer. This work provides a novel route to developing highly stretchable CTs for advanced EMI shielding applications, especially in the field of highly stretchable electronic devices.

Personal cooling technologies (PCTs) locally control the temperature of an individual instead of a whole building and are thus energy saving. However, most PCTs still consume energy and are heavy in weight, restricting their application among human beings. To achieve personal thermal comfort and no energy consumption on hot summer days, we designed a bilayer structure fabric with high thermal comfort by increasing the dissipation of human thermal radiation and reducing solar energy absorption simultaneously. The fabric consisted of two layers, including a polyethylene film with nanopores (100-1000 nm in pore size) and a film made of nylon 6 nanofibers (ca. 100 nm in diameter) with beads (ca. 230 nm in diameter), which could increase the visible light reflectance but not affect the infrared wave radiation. Therefore, the designed fabric showed a high heat dissipation power, which was 14.13, 17.93, and 17.93 W/m 2 higher than that of the selected traditional textiles of cotton, linen, and odile, respectively, suggesting good cooling capability. Its cooling performance was better than those reported by the previous research works even at a higher ambient temperature. Meanwhile, the moisture penetrability and hygroscopic property results indicated that the wearing comfort of the designed fabric reached the levels of the selected traditional textiles.

Lightweight conductive polymer composites based on biomass could be a promising candidate for electromagnetic interference (EMI) shielding application. Herein, tailoring porous microstructure and regulating the distribution of carbon nanotubes (CNTs) in cellulose composites are attempts to achieve highly efficient EMI shielding properties accompanying desired mechanical property and low density. Specifically, aligned porous structure is fabricated by ice-template freeze-drying method; meanwhile, CNT is regulated to decorate inside the cellulose matrix (CNT-matrix/cellulose porous composites) or to directly bind over the cellulose cell walls (CNT-interface/cellulose porous composites). It is found that, owing to the preferential distribution of CNT on the cell walls, the CNT-interface/cellulose porous composites possess a very high electrical conductivity of 38.9 S m -1 with an extremely low percolation threshold of 0.0083 vol % with regard to CNT-matrix/cellulose porous composites. Therefore, a shielding effectiveness of 40 dB with merely 0.51 vol % CNT under a thickness of 2.5 mm is achieved in CNT-interface/cellulose porous composites, which is attributed to efficient multiple reflections and the accompanying absorption with promoted conductivity and better-defined porous structure. More laudably, the CNT-interface/cellulose porous composites reveal a superior mechanical property with a specific modulus of 279 MPa g -1 cm 3 . The value behind the current work is to pave an effective way to fabricate environmentally benign, high-performance EMI shielding materials to practically boost numerous advanced applications of cellulose.

Highly efficient electromagnetic shielding materials entailing strong electromagnetic wave absorption and low reflection have become an increasing requirement for next-generation communication technologies and high-power electronic instruments. In this study, a new strategy is employed to provide flexible waterborne polyurethane composite films with an ultra-efficient electromagnetic shielding effectiveness (EMI SE) and low reflection by constructing gradient shielding layers with a magnetic ferro/ferric oxide deposited on reduced graphene oxide (rGO@Fe 3 O 4 ) and silver-coated tetraneedle-like ZnO whisker (T-ZnO/Ag) functional nanoparticles. Because of the differences in density between rGO@Fe 3 O 4 and T-ZnO/Ag, a gradient structure is automatically formed during the film formation process. The gradient distribution of rGO@Fe 3 O 4 over the whole thickness range forms an efficient electromagnetic wave absorption network that endows the film with a strong absorption ability on the top side, while a thin layer of high-density T-ZnO/Ag at the bottom constructs a highly conductive network that provides an excellent electromagnetic reflection ability for the film. This specific structure results in an "absorb-reflect-reabsorb" process when electromagnetic waves penetrate into the composite film, leading to an excellent EMI shielding performance with an extremely low reflection characteristic at a very low nanofiller content (0.8 vol % Fe 3 O 4 @rGO and 5.7 vol % T-ZnO/Ag): the EMI SE reaches 87.2 dB against the X band with a thickness of only 0.5 mm, while the shielding effectiveness of reflection (SE R ) is only 2.4 dB and the power coefficient of reflectivity ( R) is as low as 0.39. This result means that only 39% of the microwaves are reflected in the propagation process when 99.9999998% are attenuated, which is the lowest value among the reported references. This composite film with remarkable performance is suitable for application in portable and wearable smart electronics, and this method offers an effective strategy for absorption-dominated EMI shielding.

Electromagnetic protection in optoelectronic instruments such as optical windows and electronic displays is challenging because of the essential requirements of a high optical transmittance and an electromagnetic interference (EMI) shielding effectiveness (SE). Herein, we demonstrate the creation of an efficient transparent EMI shielding film that is composed of calcium alginate (CA), silver nanowires (AgNWs), and polyurethane (PU), via a facile and low-cost Mayer-rod coating method. The CA/AgNW/PU film with a high optical transmittance of 92% achieves an EMI SE of 20.7 dB, which meets the requirements for commercial shielding applications. A superior EMI SE of 31.3 dB could be achieved, whereas the transparent film still maintains a transmittance of 81%. The integrated efficient EMI SE and high transmittance are superior to those of most previously reported transparent EMI shielding materials. Moreover, our transparent films exhibit a highly reliable shielding ability in a complex service environment, with 98 and 96% EMI SE retentions even after 30 min of ultrasound treatment and 5000 bending cycles (1.5 mm radius), respectively. The comprehensive performance that is associated with the facile fabrication strategy imparts the CA/AgNW/PU film with great potential as an optimized EMI shielding material in emerging optoelectronic devices, such as flexible solar cells, displays, and touch panels.

Remarkable combination of excellent gas barrier performance, high strength, and toughness was realized in polylactide (PLA) composite films by constructing the supernetworks of oriented and pyknotic crystals with the assistance of ductile in situ nanofibrils of poly(butylene adipate-co-terephthalate) (PBAT). On the basis that the permeation of gas molecules through polymer materials with anisotropic structure would be more frustrated, we believe that oriented crystalline textures cooperating with inerratic amorphism can be favorable for the enhancement of gas barrier property. By taking full advantage of intensively elongational flow field, the dispersed phase of PBAT in situ forms into nanofibrils, and simultaneously sufficient row-nuclei for PLA are induced. After appropriate thermal treatment with the acceleration effect of PBAT on PLA crystallization, oriented lamellae of PLA tend to be more perfect in a preferential direction and constitute into a kind of network interconnecting with each other. At the same time, the molecular chains between lamellae tend to be more extended. This unique structure manifests superior ability in ameliorating the performance of PLA film. The oxygen permeability coefficient can be achieved as low as 2 × 10(-15) cm(3) cm cm(-2) s(-1) Pa(-1), combining with the high strength, modulus, and ductility (104.5 MPa, 3484 MPa, and 110.6%, respectively). The methodology proposed in this work presents an industrially scalable processing method to fabricate super-robust PLA barrier films. It would indeed push the usability of biopolymers forward, and certainly prompt wider application of biodegradable polymers in the fields of environmental protection such as food packaging, medical packaging, and biodegradable mulch.