Room temperature sensing characteristics of the polypyrrole (PPy) films modified with different weight percentages of ZnO nanowires (ZnO-NWs) have been studied for various oxidizing (NO2 and Cl2) as well as reducing (H2S, NH3, CH4, and CO) gases. We demonstrate that ZnO-NW (50 wt %):PPy composite films are highly selective to Cl2 along with high-sensitivity (40 at 10 ppm), fast-response (55 s), and highly reproducible response curves. It has been shown that negatively charged O2- surfaces of ZnO-NW transfer electrons to PPy, making it in a highly reduced form. A strong localization of charge carriers in the reduced PPy makes composite film highly resistive (>1010 Ω cm) as well insensitive to interaction with most of the gases except Cl2. Cl2 being highly oxidizing gas interacts with composite films and causes a sharp reduction in its resistivity. [ABSTRACT FROM AUTHOR]

Low temperature electrical transport properties of composite polypyrrole (PPy) films having ZnO-nanowires (ZnONWs) in the range of 0–50 wt. % have been investigated. It has been found that pure PPy film is in the critical regime of the metal-to-insulator transition, and adding ZnONWs drive composite films into the insulating regime. For PPy films, the transport is governed by Motts three-dimensional-variable range hopping (VRH) (ln ρ∼T-1/4) conduction and with increasing ZnONWs content above 10 wt. % results in a crossover to one-dimensional-VRH conduction (ln ρ∼T-1/2). It has been observed that films having ZnONWs content ≥10 wt. % exhibit reproducible hysteresis in the current-voltage characteristics. [ABSTRACT FROM AUTHOR]

Sensing characteristics of the drop-cast thin films of poly(3-hexylthiophene) (P3HT), ZnO nanowires, and P3HT:ZnO-nanowire hybrids with different compositions have been studied for various gases, namely, NO2, H2S, NH3, CH4, and CO. At room temperature, pure P3HT and ZnO-nanowire films were highly sensitive to NO2 and H2S, moderately sensitive to CO, and nearly insensitive to NH3 and CH4. P3HT:ZnO-nanowire hybrid films, with increasing ZnO-nanowire content, exhibited gradual enhancement in NO2 sensitivity, while reducing sensitivity for H2S. P3HT:ZnO-nanowire (1:1 ratio by weight) films were found to be highly selective for NO2. Plausible mechanisms explaining the enhanced NO2 selectivity by hybrid films are discussed. [ABSTRACT FROM AUTHOR]