The longitudinal CoCrPt thin films have been prepared on CrW underlayer at room temperature. The dependence of CoCrPt’s structure and magnetic properties on the Pt content was investigated. The addition of platinum element in the CoCrPt magnetic layer increases the lattice constant and longitudinal coercivity of the CoCrPt thin films. The coercivity mechanism of the CoCrPt thin film is analyzed by using the micromagnetic models, with careful discussions of the uniaxial crystalline anisotropy and the magnetostriction. It is found that the magnetostriction effects play an important role on the coercivity mechanisms when the Pt content is more than 15 at. % Pt concentrate. [ABSTRACT FROM AUTHOR]

FeCoAlO thin films with good soft magnetic properties were fabricated by using RF magnetron sputtering. In order to obtain good high-frequency performance, the in-plane uniaxial anisotropy was tuned by combining the effects of in situ magnetic field and the gradient of Al-O concentration. The composition gradient was controlled by using an asymmetric target and different Ar gas flow rates changing from 5 sccm to 17.5 sccm. It was found that at the range of Ar gas flow rate from 7.5 sccm to 15 sccm, the films showed an excellent high-frequency performance: the resonance frequency was beyond 3.0 GHz and the real permeability μ′ had a high value of ∼200 at low-frequency side. In particular, the film prepared at the Ar gas flow rate of 15 sccm showed a resonance frequency of 4.0 GHz. Large resonance frequency can be attributed to the high in-plane uniaxial anisotropy field which was induced by stress and the external magnetic field. The high values of permeability and resonance frequency enable the FeCoAlO thin films to be one of the important candidates for microwave applications. [ABSTRACT FROM AUTHOR]

Zn1 - xCoxFe2O4 (x = 0-1 in a step of 0.2) nanoparticles with different range of particle size including 5-10 nm and 200-250 nm have been prepared by sol-gel process. Mössbauer spectra at room temperature indicated that, with increasing cobalt content, there is a transition from paramagnetic to magnetically ordered-ferrimagnetic state. Magnetic properties were measured at 300 and 10 K using a Quantum Design MPMS-5S SQUID magnetometer. It was found that with an increase in cobalt content the saturation magnetization and coercivity increase. [ABSTRACT FROM AUTHOR]