Congruent LiNbO3 crystals doped with 5.5/1, 6/0.15, and 7/0.8 mol %/mol % of Zn/Er were thermally treated at 1120 °C over 101 h using vapor transport equilibration (VTE) technique. Unpolarized visible and infrared absorption spectra of the VTE-treated and corresponding as-grown crystals were recorded at room temperature. It is shown that VTE treatment has brought these crystals closer to stoichiometric composition. X-ray powder diffraction and optical absorption results show that the VTE treatment induces the crystalline phase transformation with respect to Er3+ from the original Er3+:LiNbO3 to the ErNbO4 in all crystals studied. The formation of the ErNbO4 phase results in substantial absorption changes that include the drop of the transparency in the visible region, the reduction of Er3+ absorption, and the Zn-doping-level-dependent changes in spectral shape and peaking position at 0.98 and 1.5 μm regions. Based upon the measured absorption spectra, the influences of Zn-doping level and VTE treatment on the Er3+ spectroscopic properties were studied by using the Judd-Ofelt (JO) theory. The results show that the VTE treatment has a little effect on the fluorescence branch ratio, while a large effect on the JO parameters, oscillator strength, and electron transition probability. The Zn doping level affects the JO parameters, oscillator strength, and transition probabilities of some individual manifolds. In addition, the VTE treatment leads to the increases of the theoretical radiative lifetimes of almost all manifolds considered. For the emission at 1.5 μm, the lifetime increase is as much as 30% and the theoretical results are in well agreement with the experimental data. The VTE-induced lifetime increase is qualitatively explained. [ABSTRACT FROM AUTHOR]

Two optimized methods for accurately measuring the 1.5 µm lifetime of Er[sup 3+] in LiNbO[sub 3] crystals and waveguides are proposed. The first method, suitable for measurement of bulk material, was suggested by forming an annealed proton exchanged sandwich structure and fluorescence was collected through an adjustable aperture. This excitation collection scheme was used to investigate bulk Er-doped LiNbO[sub 3] crystals with eight different Er[sup 3+] doping levels, three different crystal thicknesses, and three different cut orientations. The 1.5 µm lifetime was investigated in three configurations: with both a sandwich and an aperture, with a sandwich but without an aperture, and without not only a sandwich but also without an aperture. In addition, the effect of the aperture was also studied. The second method, suitable for a waveguide structure, was proposed on the basis of transversely gathering the fluorescence aided by an outcoupling fiber. It was optimized by comparing three different fluorescence collection schemes. Using this method, the lifetimes of some Ti: Er:LiNbO[sub 3] strip waveguides were measured. In addition, the effect of radiation trapping on the polarized fluorescence spectrum was also investigated. The experimental results are discussed and summarized. [ABSTRACT FROM AUTHOR]