Search

Lead-free piezoelectric ceramics of (1 − x)K0.5Na0.5NbO3-xCaTiO3 were fabricated, and their crystal structure, microstructure, and electrical properties were systematically studied. Rietveld refinement of the x-ray diffraction data and Raman spectroscopic analyses revealed a composition-dependent structural phase transition: three phase transitions, namely, from a pure orthorhombic phase for x ≤ 0.02 to a mixed phase of orthorhombic and tetragonal phases (0.03 ≤ x ≤ 0.08) and finally another mixed phase of tetragonal + cubic for x = 0.10 and 0.15 at room temperature (RT). The morphological study reveals a decrease in grain size along with a more uniform distribution of grains as the concentration of CaTiO3 (CT) increases; notably, a homogeneous distribution of grains is observed for x = 0.05. The temperature-dependent dielectric properties show two phase transitions, from orthorhombic to tetragonal (TO-T) and tetragonal to cubic (TC), for unmodified K0.5Na0.5NbO3 (KNN). However, both the phase transition temperatures (TO-T and TC) decrease, and the transition peaks broaden with an increase in CT substitution, and for x > 0.06, the TO-T shifted below RT. The broadening of the transition peak at TO-T may be due to the relaxation behavior. Among the prepared samples, the 5 mol. % CT-modified KNN shows the optimum electrical properties (d33 = 114 pC/N, ɛr = 412, and 2Pr = 15.25 μC/cm2) at RT. The enhanced electrical properties for x = 0.05 are due to the coexistence of orthorhombic and tetragonal phases, facilitating easy polarization rotation and flattening of the free energy profile. A phase diagram has been constructed based on the information gathered from the temperature-dependent dielectric measurements, RT x-ray diffraction, and Raman spectroscopy data and is discussed in detail. [ABSTRACT FROM AUTHOR]

Here, we have studied the phase transition and magneto-electric properties of a 70 wt. % Pb(Fe0.5Nb0.5)O3–30 wt. % Co0.6Zn0.4Fe1.7Mn0.3O4 (70 wt. % PFN–30 wt. % CZFMO) multiferroic composite that exhibits a maximum magneto-electric (ME) coefficient of 26.78 mV/cm Oe at room temperature. Raman analysis confirms the formation of composite and development of strain with the shifting of Raman modes. The local symmetry breaking of end members of the composite is observed by the splitting of Raman modes. The first-order derivative of magnetization with temperature (dM/dT vs T) shows anomalies across 140 K due to the PFN phase, whereas the anomaly around 250 K is due to the spin glass transition of the CZFMO phase. The magnetization vs magnetic field (M–H) study at different temperatures reveals the existence of superparamagnetic behavior above 300 K. The temperature-dependent dielectric behavior of the composite shows an anomaly around ferroelectric phase transition (Tm) for the PFN phase along with the broad relaxation peak arising due to the CZFMO phase. The linear behavior of magnetocapacitance (MD%) with the square of magnetization (M2) suggests the existence of biquadratic ME coupling. The ME study on the composite suggests the existence of both direct and converse ME effects. [ABSTRACT FROM AUTHOR]

Magnetoelectric (ME) materials with ferroelectric and magnetic transition temperatures near room temperature are of current interest in research due to their technological importance and potential applications. Herein, we report the coupled magnetic ordering and phonons in gallium ferrite (GaFeO3), a near room temperature ME perovskite, using magnetization and inelastic light scattering measurements as a function of temperature. Temperature-dependent magnetization behavior studied in a wide temperature range of 5–395 K at both field-cooled (FC) and zero-field-cooled (ZFC) conditions using different static magnetic fields confirms the magnetic transition temperature Tc at 220 K. On temperature dependent Raman spectroscopy, no significant changes in Raman spectra were observed at an elevated temperature that can be attributed to the absence of structural phase transition. Instead of expected anharmonic behavior, several librational (rigid rotation) and stretching modes of rigid BO6 units were found to be hardening below Tc, suggesting the significant magnetoelastic coupling contributions to phonon frequencies. The asymmetric stretching mode at 753 cm−1 is found to have larger spin-phonon coupling contribution (λ∼2.93), while the lattice mode at 153 cm−1 and external librational mode at 240 cm−1 had the lowest effect (λ∼0.88). [ABSTRACT FROM AUTHOR]

We report systematic studies on crystal structure and magneto-dielectric properties of (1-x) BiFeO3-x DyMnO3 (0.0⩽x⩽0.2) nanoceramics synthesized by auto-combustion method. Rietveld refinement of X-ray diffraction data indicates a structural transition from R3c to R3c + Pn21a at x=0.1. Field emission scanning electron micrographs display a decrease in grain size with increase in x. The presence of dielectric anomalies around antiferromagnetic transition temperature implies the magnetoelectric coupling. Dielectric measurements showed decrease in magnetic ordering temperature with increasing x in agreement with differential scanning calorimetry results. A significant increase in magnetization has been found with increasing DyMnO3 substitution. Magnetoimpedance spectroscopy reveals a significant change (∼18%) in dielectric permittivity at H=2T for x=0.2. [ABSTRACT FROM AUTHOR]

We report the crystal structure, dielectric, magnetic, and magneto-electric properties of (1-x) BiFeO3-xYMnO3 (0.00 ≤ x ≤ 0.2) multiferroic nanoceramics prepared by auto-combustion technique. YMnO3 substitution is found to induce a structural phase transition from R3c to R3c+Pbnm after x ≈ 0.1 using Rietveld refinement technique. Field emission scanning electron micrographs show decrease in grain size with increase in YMnO3 content. The dielectric permittivity and loss tangent are found to be increased with composition x. The anomalies noticed from the temperature dependent dielectric analysis reveal the signature of magneto-electric coupling in the system. A decrease in magnetic ordering temperature as a function of composition is found from dielectric study. At room temperature, the dielectric permittivity of all the YMnO3 modified samples decrease with increasing magnetic field. The maximum value of magneto-electric coupling coefficient ([variant_greek_epsilon](H)-[variant_greek_epsilon](0))/[variant_greek_epsilon](0) is found to be ∼ -5.5% at H = 2 T for x = 0.2. The behaviour of the magnetic hysteresis loop observed at room temperature suggests the suppression of space modulated spin structure. [ABSTRACT FROM AUTHOR]

We investigate the structural and electronic properties of VO2 thin films on c-plane sapphire substrates with three different surface morphologies to control the strain at the substrate-film interface. Only non-annealed substrates with no discernible surface features (terraces) provided a suitable template for VO2 film growth with a semiconductor-metal transition (SMT), which was much lower than the bulk transition temperature. In addition to strain, oxygen vacancy concentration also affects the properties of VO2, which can be controlled through deposition conditions. Oxygen plasma-assisted pulsed laser deposition allows favorable conditions for VO2 film growth with SMTs that can be easily tailored for device applications. [ABSTRACT FROM AUTHOR]