Search

The luminescence efficiency of AlxGa1−xN quantum dots (QDs) and quantum wells (QWs), buried in AlN cladding layers and emitting in the ultraviolet range between 234 and 310 nm, has been investigated. The growth and optical properties have been done using similar aluminum composition (varying from 0.4 to 0.75) for both QDs and QWs. In order to compare as much as possible the optical properties, the QWs were fabricated with a growth time tuned such that the QW width is similar to the average height of the QDs. The photoluminescence (PL) showed emission ranging from 4 to 5.4 eV, putting into evidence differences in terms of full width at half maximum, PL intensity, and asymmetry of the line shape between QDs and QWs. The results show shorter wavelengths and a slightly narrower PL linewidth for QWs. To determine the light emission dependence with the electric field direction in the crystal, the evolutions of the emission diagrams for all samples were recorded along two orthogonal directions, namely, the "in-plane" (growth) and the "on-side" directions, from which the light emission was collected. For the whole QDs and QWs samples' series, the shapes of the emission diagram indicate emission in both in-plane and on-side directions, as evidenced by intra-valence band mixings caused by strain effects combined with the anisotropic Coulomb interactions that are particularly contributing to the polarization at wavelengths below 260 nm. Furthermore, the degree of polarization, determined for each sample, showed good agreement with results from the literature. [ABSTRACT FROM AUTHOR]

A correction to the article "Dependence of the Mg-related acceptor ionization energy with the acceptor concentration in p-type GaN layers grown by molecular beam epitaxy" that was published in the previous issue is presented.

Hall effect and capacitance-voltage C(V) measurements were performed on p-type GaN:Mg layers grown on GaN templates by molecular beam epitaxy with a high range of Mg-doping concentrations. The free hole density and the effective dopant concentration NA-ND as a function of magnesium incorporation measured by secondary ion mass spectroscopy clearly reveal both a magnesium doping efficiency up to 90% and a strong dependence of the acceptor ionization energy Ea with the acceptor concentration NA. These experimental observations highlight an isolated acceptor binding energy of 245±25 meV compatible, at high acceptor concentration, with the achievement of p-type GaN:Mg layers with a hole concentration at room temperature close to 1019 cm-3. [ABSTRACT FROM AUTHOR]

We have grown (11-22)-oriented GaN/Al0.5Ga0.5N quantum wells (QWs) using molecular beam epitaxy on GaN (11-22)-oriented templates grown by metal-organic vapor phase epitaxy on m-plane oriented sapphire substrates. The performance of epitaxial growth of GaN/Al0.5Ga0.5N heterostructures on the semi-polar orientation (11-22) in terms of surface roughness and structural properties, i.e., strain relaxation mechanisms is discussed. In addition, high resolution transmission electron microscopy reveals very smooth QW interfaces. The photoluminescence of such samples are strictly originating from radiative recombination of free excitons for temperatures above 100 K. At high temperature, the population of localized excitons, moderately trapped (5 meV) at low temperature, is negligible. [ABSTRACT FROM AUTHOR]

We have investigated the optical properties of multi-stacked GaN/AlGaN self-assembled quantum dots (QDs) grown by molecular beam epitaxy. The QDs that emit visible light have a broad spectral range without incorporation of indium alloy because of the quantum-confined Stark effect. We found differences in the structural and optical properties between the layers of multi-stacked QDs. The carriers are more effectively transferred from the AlGaN barrier to the low energy side of the GaN QD emission than to the high energy side. We also observed long-lived carrier recombination dynamics for the visible range emission from QDs. [ABSTRACT FROM AUTHOR]