Acoustic and dielectric properties of Pb[(Zn1/3Nb2/3)1-xTix]O3 (PZN-xPT) single crystals with x=0.045 have been studied by the high-resolution micro-Brillouin scattering and dielectric spectroscopy in a wide temperature range. The softening of the Brillouin shift and the increase of dielectric relaxation time upon cooling indicated the formation of polar nanoregions (PNRs) and the slowing down of their dynamics. In contrast to the acoustic properties of typical model relaxors such as lead magnesioniobate, the change in the Brillouin shift near its minimum became sharper on heating compared to the change on cooling, pointing to the clear existence of hysteresis in the dynamics of the diffuse phase transition in PZN-4.5%PT. Since the number of PNRs will increase upon cooling, it may be expected that the kinetics of the phase transition would become slower, the lower the transition temperature resulting in the more sluggish, broad feature of the Brillouin shift observed during cooling. This result may indicate that the number and size of polar nanoregions, which are dependent on temperature, play an important role in the development of the mesoscopic ferroelectric order in PZN-4.5%PT. [ABSTRACT FROM AUTHOR]

The role of dynamic polar nanoregions (PNRs) of (1-x)Pb(Zn1/3Nb2/3)O3-xPbTiO3 (PZN-100xPT) single crystals with the PT content x = 0.15 (i.e., higher than above the morphotropic phase boundary composition x ∼ 0.09) has been investigated using inelastic light scattering. The remarkable anomaly of the longitudinal acoustic mode is clearly observed in the vicinity of the cubic-tetragonal phase transition temperature at the TC-T = 481 K. A broad central peak (CP) appears below the Burns temperature TB ∼ 700 K. Upon cooling, the relaxation time determined from the CP width clearly shows a critical slowing down when approaching TC-T in contrast with the suppressed slowing down previously observed in PZN-7PT [S. Tsukada and S. Kojima, Phys. Rev. B 78, 144106 (2008)]. These facts are due to the existence of dynamic PNRs and the disappearance of chemically ordered regions resulting from a higher PT content in the solid solution. In the cubic phase, the local symmetry breaking caused by the PNRs was observed by Raman scattering. The initial size of dynamic PNRs is about 3 nm just below TB, and it increases significantly upon cooling below the intermediate temperature T* ∼ 600 K, reaching 10 nm down to TC-T. [ABSTRACT FROM AUTHOR]

Presents an abstract of the article 'The Influence of Hydrogen on a Hyperfine Field of the Amorphous Alloy Fe[sub83.3]B[sub11.2]Si[sub3.5]C[sub2],' by Rongli Gui, WenZhi Chen and KaiYuan Llo.