Search

In this Letter, we report the demonstration of zinc ion-implantation to realize planar mid-wavelength infrared photodetectors based on type-II InAs/InAs1−xSbx superlattices. At 77 K, the photodetectors exhibit a peak responsivity of 0.68 A/W at 3.35 μm, corresponding to a quantum efficiency of 23.5% under Vb = −80 mV, without anti-reflection coating; these photodetectors have a 100% cutoff wavelength of 4.28 μm. With an R0 × A value of 1.53 × 104 Ω cm2 and a dark current density of 1.23 × 10−6 A/cm2 under an applied bias of −80 mV at 77 K, the photodetectors exhibit a specific detectivity of 9.12 × 1011 cm·Hz1/2/W. [ABSTRACT FROM AUTHOR]

We report a Zn-diffused planar mid-wavelength infrared photodetector based on type-II InAs/InAs1−xSbx superlattices. Both the superlattice growth and Zn diffusion were performed in a metal-organic chemical vapor deposition system. At 77 K, the photodetector exhibits a peak responsivity of 0.70 A/W at 3.65 μm, corresponding to a quantum efficiency of 24% at zero bias without anti-reflection coating, with a 50% cutoff wavelength of 4.28 μm. With an R0A value of 3.2 × 105 Ω cm2 and a dark current density of 9.6 × 10−8 A/cm2 under an applied bias of −20 mV at 77 K, the photodetector exhibits a specific detectivity of 2.9 × 1012 cm Hz1/2/W. At 150 K, the photodetector exhibits a dark current density of 9.1 × 10−6 A/cm2 and a quantum efficiency of 25%, resulting in a detectivity of 3.4 × 1011 cm Hz1/2/W. [ABSTRACT FROM AUTHOR]

A high operating temperature mid-wavelength infrared pBn photodetector based on the type-II InAs/InAsSb superlattice on a GaSb substrate has been demonstrated. At 150 K, the photodetector exhibits a peak responsivity of 1.48 A/W, corresponding to a quantum efficiency of 47% at −50 mV applied bias under front-side illumination, with a 50% cutoff wavelength of 4.4 µm. With an R × A of 12 783 Ω cm2 and a dark current density of 1.16 × 10−5 A/cm2 under −50 mV applied bias, the photodetector exhibits a specific detectivity of 7.1 × 1011 cm Hz1/2/W. At 300 K, the photodetector exhibits a dark current density of 0.44 A/cm2 and a quantum efficiency of 39%, resulting in a specific detectivity of 2.5 × 109 cm Hz1/2/W. [ABSTRACT FROM AUTHOR]

We report design, growth, and characterization of midwavelength infrared nBn photodetectors based on a type-II InAs/InAs1-xSbx superlattice on a GaSb substrate grown by metal-organic chemical vapor deposition. An InAs/AlAs1-ySby/InAs/InAs1-xSbx superlattice design was used as the large bandgap electron barrier in the photodetectors. At 150 K, the photodetector exhibits a peak responsivity of 1.23 A/W, corresponding to a quantum efficiency of 41% at an applied bias voltage of −100 mV under front-side illumination, with a 50% cut-off wavelength of 4.6 μm. With an R × A of 356 Ω cm2 and a dark current density of 1.6 × 10−4 A/cm2 under an applied bias of −100 mV at 150 K, the photodetector exhibits a specific detectivity of 1.4 × 1011 cm Hz1/2/W. [ABSTRACT FROM AUTHOR]

A two terminal extended short wavelength infrared heterojunction phototransistor based on type-II InAs/AlSb/GaSb on a GaSb substrate is designed, fabricated, and investigated. With the base thickness of 40 nm, the device exhibited a 100% cut-off wavelength of ∼2.3 μm at 300 K. The saturated peak responsivity value is 320.5 A/W at 300 K, under front-side illumination without any antireflection coating. A saturated optical gain of 245 at 300 K was measured. At the same temperature, the device exhibited a collector dark current density (at unity optical gain) and a DC current gain of 7.8 × 10−3 A/cm2 and 1100, respectively. The device exhibited a saturated dark current shot noise limited specific detectivity of 4.9 × 1011 cm·Hz1/2/W at 300 K which remains constant over a broad range of wavelengths and applied biases. [ABSTRACT FROM AUTHOR]

We report the growth and characterization of mid-wavelength infrared type-II InAs/InAs1−xSbx superlattice photodiodes on GaSb substrates grown by metal-organic chemical vapor deposition. At 150 K, the 50% cut-off wavelength is 5.0 μm, the dark current density is 3.3 × 10−4 A/cm2 under −20 mV bias, and the peak responsivity is 1.76 A/W corresponding to a quantum efficiency of 55% without anti-reflection coating. A specific detectivity of 1.2 × 1011 cm Hz1/2/W is achieved at 4.0 μm under −20 mV bias at 150 K. [ABSTRACT FROM AUTHOR]

We report the demonstration of high-performance long-wavelength infrared (LWIR) nBn photodetectors based on InAs/InAs1-xSbx type-II superlattices. A new saw-tooth superlattice design was used to implement the electron barrier of the photodetectors. The device exhibited a cut-off wavelength of ~10 μm at 77 K. The photodetector exhibited a peak responsivity of 2.65 A/W, corresponding to a quantum efficiency of 43%. With an R X A of 664 Ωcm2 and a dark current density of 8 X 10-5 A/cm2, under -80 mV bias voltage at 77 K, the photodetector exhibited a specific detectivity of 4.72 X 1011 cm√Hz/W and a background-limited operating temperature of 110 K. [ABSTRACT FROM AUTHOR]