Search

Diffusive dielectric materials such as white paint have been demonstrated as effective back reflectors in the photovoltaic technology. In this work, a one-dimensional (1D) optical modeling approach for simulation of white paint films is developed and implemented in a 1D optical simulator for thin-film solar cells. The parameters of white paint, such as the paint film thickness, the pigment volume concentration (PVC), and the pigment/binder refractive index ratio (RIR), are examined and optimized to achieve the required optical properties for back reflector application. The simulation trends indicate that white paint back reflectors with sufficient film thickness and higher PVC and RIR values exhibit improved reflectivity characteristics which results in an increased long-wavelength quantum efficiency of thin-film silicon solar cells. The simulation results based on the 1D model agree very well with the experimental data obtained from reflectance measurements of various white paint compositions and quantum efficiency measurements of amorphous silicon solar cells with white paint back reflectors. [ABSTRACT FROM AUTHOR]

The poly-Si carrier-selective passivating contacts (CSPCs) parasitically absorb a substantial amount of light, especially in the form of free carrier absorption. To minimize these losses, we developed CSPCs based on oxygen-alloyed poly-Si (poly-SiOx) and deployed them in c-Si solar cells. Transmission electron microscopy analysis indicates the presence of nanometer-scale silicon crystals within such poly-SiOx layers. By varying the O content during material deposition, we can manipulate the crystallinity of the poly-SiOx material and its absorption coefficient. Also, depending on the O content, the bandgap of the poly-SiOx material can be widened, making it transparent for longer wavelength light. Thus, we optimized the O alloying, doping, annealing, and hydrogenation conditions. As a result, an extremely high passivation quality for both n-type poly-SiOx (J0 = 3.0 fA/cm2 and iVoc = 740 mV) and p-type poly-SiOx (J0 = 17.0 fA/cm2 and iVoc = 700 mV) is obtained. A fill factor of 83.5% is measured in front/back-contacted solar cells with both polarities made up of poly-SiOx. This indicates that the carrier transport through the junction between poly-SiOx and c-Si is sufficiently efficient. To demonstrate the merit of poly-SiOx layers' high transparency at long wavelengths, they are deployed at the back side of interdigitated back-contacted (IBC) solar cells. A preliminary cell efficiency of 19.7% is obtained with much room for further improvement. Compared to an IBC solar cell with poly-Si CSPCs, a higher internal quantum efficiency at long wavelengths is observed for the IBC solar cell with poly-SiOx CSPCs, thus demonstrating the potential of poly-SiOx in enabling higher JSC. [ABSTRACT FROM AUTHOR]

Ion-implanted passivating contacts based on poly-crystalline silicon (polySi) are enabled by tunneling oxide, optimized, and used to fabricate interdigitated back contact (IBC) solar cells. Both n-type (phosphorous doped) and p-type (boron doped) passivating contacts are fabricated by ionimplantation of intrinsic polySi layers deposited via low-pressure chemical vapor deposition and subsequently annealed. The impact of doping profile on the passivation quality of the polySi doped contacts is studied for both polarities. It was found that an excellent surface passivation could be obtained by confining as much as possible the implanted-and-activated dopants within the polySi layers. The doping profile in the polySi was controlled by modifying the polySi thickness, the energy and dose of ion-implantation, and the temperature and time of annealing. An implied open-circuit voltage of 721mV for n-type and 692mV for p-type passivating contacts was achieved. Besides the high passivating quality, the developed passivating contacts exhibit reasonable high conductivity (Rsh n-type = 95 Ω/□ and Rsh p-type = 120 Ω/□. An efficiency of 19.2% (Voc = 673 mV, Jsc = 38.0 mA/cm², FF = 75.2%, and pseudo-FF = 83.2%) was achieved on a front-textured IBC solar cell with polySi passivating contacts as both back surface field and emitter. By improving the front-side passivation, a VOC of 696mV was also measured. [ABSTRACT FROM AUTHOR]

We have fabricated a-SiOx:H/a-Si:H/nc-Si:H/nc-Si:H quadruple-junction thin-film silicon-based solar cells (4J TFSSCs) to obtain high spectral utilization and high voltages. By processing the solar cells on micro-textured superstrates, extremely high open-circuit voltages for photovoltaic technology based on thin-film silicon alloys up to 2.91 V have been achieved. Optical simulations of quadruple-junction solar cells using an advanced in-house model are a crucial tool to effectively tackle the challenging task of current matching among the individual sub-cells in such devices. After optimizing the optical design of the device and the absorber thicknesses, an energy conversion efficiency of 11.4% has been achieved. The open-circuit voltage, short-circuit current density, and fill factor were 2.82 V, 5.49mA/cm², and 73.9%, respectively. Based on this demonstration, strategies for further development of highly efficient 4J TFSSCs are proposed. [ABSTRACT FROM AUTHOR]

Substrates with a modulated surface texture were prepared by combining different interface morphologies. The spatial frequency surface representation method is used to evaluate the surface modulation. When combining morphologies with appropriate geometrical features, substrates exhibit an increased scattering level in a broad wavelength region. We demonstrate that the improved scattering properties result from a superposition of different light scattering mechanisms caused by the different geometrical features integrated in a modulated surface texture. [ABSTRACT FROM AUTHOR]

Micro-textures with large opening angles and smooth U-shape are applied to nanocrystalline silicon (nc-Si:H) solar cells. The micro-textured substrates result in higher open-circuit-voltage (Voc) and fill-factor (FF) than nano-textured substrates. For thick solar cells, high Voc and FF are maintained. Particularly, the Voc only drops from 564 to 541 mV as solar cell thickness increases from 1 to 5 μm. The improvement in electrical performance of solar cells is ascribed to the growth of dense nc-Si:H layers free from defective filaments on micro-textured substrates. Thereby, micromorph tandem solar cells with an initial efficiency of 13.3%, Voc = 1.464 V, and FF = 0.759 are obtained. [ABSTRACT FROM AUTHOR]