Using a hydrothermal method, (K0.88Na0.12)NbO3 films were deposited at 240 °C on (100) cSrRuO3//(100)SrTiO3 substrates. Moreover, without any poling treatment, direct and inverse transverse piezoelectric coefficients, e31,f, near 0 kV/cm were approximately −5.0 C/m2 for the as-deposited film. This value was nearly unchanged following the application of an electric field and poling treatment, suggesting that as-deposited films are almost in a fully self-polarized state without the application of an electric field. As-deposited films with a thickness of up to 22 μm showed constant piezoelectricity without any poling treatment. The films did not crack or peel because of substrates due to the small thermal strain originating from the low deposition temperature. The figures of merit (FOM) for the vibration energy harvester [FOM = e31,f2/(ε0εr)] and sensor [FOM = e31,f/(ε0εr)] were estimated to be good at 32.8 GPa and –5.9 GV/m, respectively, primarily because of the low relative dielectric constant of ∼110. Furthermore, the piezoelectric voltage coefficient g31 [= d31/(ε0εr)] was estimated and demonstrated a high value of 0.073 Vm/N. [ABSTRACT FROM AUTHOR]

Stacks are among the most important devices for influencing the energy-conversion efficiency of work flow to heat flow during thermoacoustic phenomena. An optimal stack design is indispensable for the practical application of thermoacoustic systems. To this end, it is necessary to estimate the heat flow generated in the stack. This study proposes to estimate this quantity based on the sound generated by a thermoacoustic phenomenon in a stack without any temperature gradient. The heat flow caused by a standing-wave component generated by this thermoacoustic phenomenon is successfully measured. [ABSTRACT FROM AUTHOR]