Search

During the heat treatment by quenching in a liquid medium the convective heat transfer coefficient plays a crucial role in the extraction of heat. The heat extraction ultimately influences the cooling rate and hence the hardness and mechanical properties. A Finite Element analysis of quenching a simple flat copper sample with different orientation of sample and with different quenchant temperatures were carried out to check and verify the results obtained from the experiments. The heat transfer coefficient (HTC) was calculated from temperature history in a simple flat copper disc sample experimentally. This HTC data was further used as input to simulation software and the cooling curves were back calculated. The results obtained from software and using experimentation shows nearly consistent values. [ABSTRACT FROM AUTHOR]

This work describes the effect of austempering heat treatment on microstrcuture and mechanical properties of SAE 9260 steel. Steel samples, austenitized at 900 °C for one hour, were isothermally heat treated in the temperature range 300,325 and 350 °C for different times. Microstructural characterization was carried out using optical and scanning electron microscopes. The microstructure of the austempered samples consisted of bainitic ferrite and retained austenite. The volume fraction of retained austenite was determined using X-ray diffraction. Isothermal heat treatment at 350 °C for 20 min, resulted in a retained austenite content of around 38% in the microstructure. Increase in isothermal transformation temperature led to an increase in the fraction of retained austenite. Also, good combination of strength and ductility was obtained in the samples with increased amounts of retained austenite . [ABSTRACT FROM AUTHOR]