Predominant high melting point solders for high-temperature and harsh environment electronics (operating temperatures from 200 to 250 °C) are Pb-based systems, which are being subjected to RoHS regulations because of their toxic nature. In this study, high bismuth (Bi) alloy compositions with Bi-XSb-10Cu (X from 10 wt % to 20 wt %) were designed and developed to evaluate their potential as high-temperature, Pb-free replacements. Reflow processes were developed to make die-attach samples made from the cast Bi alloys. Die-attach joints made from Bi-15Sb-10Cu alloy exhibited an average shear strength of 24 MPa, which is comparable to that of commercially available high Pb solders. These alloy compositions also retained original shear strength even after thermal shock (TS) between −55 °C and +200 °C and high-temperature storage (HTS) at 200 °C. Brittle interfacial fracture sometimes occurred along the interfacial NiSb layer formed between Bi(Sb) matrix and Ni metallized surface. In addition, heat dissipation capabilities, using flash diffusivity, were measured on the die-attach assembly and were compared to the corresponding bulk alloys. The thermal conductivity of all the Bi–Sb alloys was higher than that of pure Bi. By creating high volume fraction of precipitates in a die-attach joint microstructure, it was feasible to further increase thermal conductivity of this joint to 24 W/m·K, which is three times higher than that of pure Bi (8 W/m·K). Bi–15Sb–10Cu alloy has so far shown the most promising performance as a die-attach material for high-temperature applications (operated over 200 °C). Hence, this alloy was further studied to evaluate its potential for plastic deformation. Bi–15Sb–10Cu alloy has shown limited plastic deformation in room temperature tensile testing in which premature fracture occurred via the cracks propagated on the (111) cleavage planes of rhombohedral crystal structure of the Bi(Sb) matrix. The same alloy has, however, shown up to 7% plastic strain under tension when tested at 175 °C. The cleavage planes, which became oriented at smaller angles to the tensile stress, contributed to improved plasticity in the high-temperature test.

The connection between processing and performance in thermal barrier coatings produced by electron-beam physical-vapor-deposition is not well understood. A significant component of the problem is the limited understanding of the role that microstructure (including defects) plays in this connection, and the relationships between microstructure and process parameters. This presentation will review recent work aimed at understanding these relationships. The focus will be on the evolution of porosity within the TBC, which is of paramount importance to both thermal conductivity and strain tolerance. Porosity is a result of shadowing processes in the presence of insufficient surface diffusion, and thus deposition temperature and vapor incidence pattern are major parameters. The presentation will highlight the interplay between vapor flux and surface topography, illustrating the relevant phenomena with experimental and modeling results. (Work sponsored by ONR under Grant N00014-99-1-0471 and the UC-LANL Collaborative Research Program.)