Search

Recent works[1-3] reported evidence for charge density waves (CDWs) in infinite layer nickelates (112 structure) based on resonant diffraction at the Ni $L_3$ edge measured at fixed scattering angle. We have found that a measurement with fixed momentum transfer, rather than scattering angle, does not show a resonance effect. We have also observed that a nearby structural Bragg peak from the substrate appears due to third harmonic content of the incident beam, and spreads intensity down to the region of the attributed CDW order. This was further confirmed by testing a bare substrate. We suggest procedures to confirm an effective resonant enhancement of a diffraction peak.

In the study of dynamic charge order correlations in the cuprates, most high energy-resolution resonant inelastic x-ray scattering (RIXS) measurements have focused on momenta along the high-symmetry directions of the copper oxide plane. However, electron scattering along other in-plane directions should not be neglected as they may contain information relevant, for example, to the origin of charge order correlations or to our understanding of the isotropic scattering responsible for strange metal behavior in cuprates. We report high-resolution resonant inelastic x-ray scattering (RIXS) experiments that reveal the presence of dynamic electron correlations over the $q_x$-$q_y$ scattering plane in underdoped $\textrm{Bi}_2\textrm{Sr}_2\textrm{Ca}\textrm{Cu}_2\textrm{O}_{8+δ}$ with $T_c=54$ K. We use the softening of the RIXS-measured bond stretching phonon line as a marker for the presence of charge-order-related dynamic electron correlations. The experiments show that these dynamic correlations exist at energies below approximately $70$ meV and are centered around a quasi-circular manifold in the $q_x$-$q_y$ scattering plane with radius equal to the magnitude of the charge order wave vector, $q_{CO}$. We also demonstrate how this phonon-tracking procedure provides the necessary experimental precision to rule out fluctuations of short-range directional charge order (i.e. centered around $[q_x=\pm q_{CO}, q_y=0]$ and $[q_x=0, q_y=\pm q_{CO}]$) as the origin of the observed correlations., Submitted and under review

The $A$-site spinel NiRh$_2$O$_4$ is the only known realization of a spin-1 diamond lattice magnet and is predicted to host unconventional magnetic phenomena driven by frustrated nearest and next-nearest neighbor exchange as well as orbital degeneracy. Previous works found no sign of magnetic order but found a gapped dispersive magnetic excitation indicating a possible valence bond magnetic ground state. However, the presence of many competing low energy degrees of freedom and limited empirical microscopic constraints complicates further analysis. Here, we carry out resonant inelastic x-ray scattering (RIXS) and x-ray absorption spectroscopy (XAS) to characterize the local electronic structure of NiRh$_2$O$_4$. The RIXS data can be partly described by a single-ion model for tetrahedrally coordinated Ni$^{2+}$ and indicates a tetragonal distortion $\Delta t_2\!=\!70$ meV that splits the $t_2$ orbitals into a high energy orbital singlet and lower energy orbital doublet. We identify features of the RIXS spectra that are consistent with a Rh-Ni two-site excitation indicating strong metal-metal hybridization mediated by oxygen in NiRh$_2$O$_4$. We also identify signatures of electron-phonon coupling through the appearance of phonon sidebands that dress crystal field excitations. These results establish the key energy scales relevant to the magnetism in NiRh$_2$O$_4$ and further demonstrate that covalency and lattice dynamics play essential roles in controlling the magnetic ground states of $A$-site spinels.

The discovery of superconductivity in square-planar low valence nickelates has ignited a vigorous debate regarding their essential electronic properties: Do these materials have appreciable oxygen charge-transfer character akin to the cuprates, or are they in a distinct Mott-Hubbard regime where oxygen plays a minimal role? Here, we resolve this question using O $K$-edge resonant inelastic x-ray scattering (RIXS) measurements of the low valence nickelate La$_{4}$Ni$_{3}$O$_{8}$ and a prototypical cuprate La$_{2-x}$Sr$_{x}$CuO$_{4}$ ($x=0.35$). As expected, the cuprate lies deep in the charge-transfer regime of the Zaanen-Sawatzky-Allen scheme. The nickelate, however, is not well described by either limit of the ZSA scheme and is found to be of mixed charge-transfer/Mott-Hubbard character with the Coulomb repulsion $U$ of similar size to the charge-transfer energy $\Delta$. Nevertheless, the transition-metal-oxygen hopping is larger in La$_{4}$Ni$_{3}$O$_{8}$ than in La$_{2-x}$Sr$_{x}$CuO$_{4}$, leading to a significant superexchange interaction and an appreciable hole occupation of the ligand O orbitals in La$_{4}$Ni$_{3}$O$_{8}$ despite its larger $\Delta$. Our results clarify the essential characteristics of low valence nickelates and put strong constraints on theoretical interpretations of superconductivity in these materials., Comment: 13 pages; to appear in PRX

The discovery of superconductivity in a $d^{9-��}$ nickelate has inspired disparate theoretical perspectives regarding the essential physics of this class of materials. A key issue is the magnitude of the magnetic superexchange, which relates to whether cuprate-like high-temperature nickelate superconductivity could be realized. We address this question using Ni L-edge and O K-edge spectroscopy of the reduced trilayer nickelate $d^{9-1/3}$ La4Ni3O8 and associated theoretical modeling. A magnon energy scale of ~80 meV resulting from a nearest-neighbor magnetic exchange of $J = 69(4)4$ meV is observed, proving that $d^{9-��}$ nickelates can host a large superexchange. This value, along with that of the Ni-O hybridization estimated from our O K-edge data, implies that trilayer nickelates represent an intermediate case between the infinite-layer nickelates and the cuprates, and suggests that they represent a promising route towards higher-temperature nickelate superconductivity., 7 pages not including supplmentary material; To appear in Physical Review Letters

Charge density wave (CDW) correlations are prevalent in all copper-oxide superconductors. While CDWs in conventional metals are driven by coupling between lattice vibrations and electrons, the role of the electron-phonon coupling (EPC) in cuprate CDWs is strongly debated. Using Cu $L_3$ edge resonant inelastic x-ray scattering (RIXS), we study the CDW and Cu-O bond-stretching phonons in the stripe-ordered cuprate La$_{1.8-x}$Eu$_{0.2}$Sr$_{x}$CuO$_{4+��}$. We investigate the interplay between charge order and EPC as a function of doping and temperature, and find that the EPC is enhanced in a narrow momentum region around the CDW wave vector. By detuning the incident photon energy from the absorption resonance, we extract an EPC matrix element at the CDW wave vector of $M\simeq$ 0.36 eV, which decreases to $M\simeq$ 0.30 eV at high temperature in the absence of the CDW. Our results suggest a feedback mechanism in which the CDW enhances the EPC which, in turn, further stabilizes the CDW., 5 pages, 4 figures

The hole distribution in Sr$_{14}$Cu$_{24}$O$_{41}$ is studied by low temperature polarization dependent O K Near-Edge X-ray Absorption Fine Structure measurements and state of the art electronic structure calculations that include core-hole and correlation effects in a mean-field approach. Contrary to all previous analysis, based on semi-empirical models, we show that correlations and antiferromagnetic ordering favor the strong chain hole-attraction. For the remaining small number of holes accommodated on ladders, leg-sites are preferred to rung-sites. The small hole affinity of rung-sites explains naturally the 1D - 2D cross-over in the phase diagram of (La,Y,Sr,Ca)$_{14}$Cu$_{24}$O$_{41}$, Comment: 6 pages, 8 figures

We probe the collective magnetic modes of La$_2$CuO$_4$ (LCO) and underdoped La$_{2-x}$Sr$_x$CuO$_4$ (LSCO) by momentum resolved Resonant Inelastic X-ray Scattering (RIXS) at the Cu $L_3$ edge. In LCO the single magnon dispersion measured by RIXS coincides with the one determined by inelastic neutron scattering. For LSCO the spin dynamics shows a branch dispersing up to $\sim$400 meV coexisting with a branch at lower energy. Only the latter has been observed with neutrons so far and is considered a key signature of doped cuprates. The presence of the high-energy branch indicates that LSCO is in a dynamic inhomogeneous spin state., Comment: 5 pages, 4 figures

In the early days of high temperature superconductivity it was already recognized that magnetic properties of these materials are intimately related to the superconducting ones . When doped, the long-range ordered antiferromagnetic background of pristine copper-oxide insulators melts away and makes room for a spin liquid and superconductivity. By resonant inelastic x-ray scattering (RIXS) in the soft regime we probe the hitherto inaccessible dynamical multiple-spin correlations of the magnetic background in a series of parent compounds and in high Tc materials [NCCO (Nd2-xCexCuO4) and LSCO (La2-xSrxCuO4)]. High resolution measurements allows the clear observation of dispersing bimagnon excitations. In the undoped compounds the theory, fits the data on these coherent spin excitations without free parameters. In nearly optimally doped LSCO we observe the appearance of a new collective excitation at an energy of 250 +/- 60 meV having the signature of a coupled bimagnon-charge mode. It has a strongly reduced dispersion and lies in a so far unexplored region of momentum and energy space in the mid-infrared., Comment: 16 pages, 3 figures embedded

Electronic properties of transition metal oxides at interfaces are influenced by strain, electric polarization and oxygen diffusion. Linear dichroism (LD) x-ray absorption, diffraction, transport and magnetization on thin La0.7Sr0.3MnO3 films, allow identification of a peculiar universal interface effect. We report the LD signature of preferential 3d-eg(3z2-r2) occupation at the interface, suppressing the double exchange mechanism. This surface orbital reconstruction is opposite of that favored by residual strain and independent of dipolar fields, chemical nature of the substrate and capping., Comment: 13 pages, 5 figures