Search

We report on the coexistence of magnetic and superconducting states in CeFeAsO1-xFx for x=0.06(2), characterized by transition temperatures T_m=30 K and T_c=18 K, respectively. Zero and transverse field muon-spin relaxation measurements show that below 10 K the two phases coexist within a nanoscopic scale over a large volume fraction. This result clarifies the nature of the magnetic-to-superconducting transition in the CeFeAsO1-xFx phase diagram, by ruling out the presence of a quantum critical point which was suggested by earlier studies., Comment: 4 pages, 3 figs, accepted for publication as PRB Rapid comm

The evolution of the magnetic order in FeSeTe crystals as a function of Se content was investigated by means of ac/dc magnetometry and muon-spin spectroscopy. Experimental results and self-consistent DFT calculations both indicate that muons are implanted in vacant iron-excess sites, where they probe a local field mainly of dipolar origin, resulting from an antiferromagnetic (AFM) bicollinear arrangement of iron spins. This long-range AFM phase disorders progressively with increasing Se content. At the same time all the tested samples manifest a marked glassy character that vanishes for high Se contents. The presence of local electronic/compositional inhomogeneities most likely favours the growth of clusters whose magnetic moment "freezes" at low temperature. This glassy magnetic phase justifies both the coherent muon precession seen at short times in the asymmetry data, as well as the glassy behaviour evidenced by both dc and ac magnetometry., Comment: Approved for publication in J. Phys.: Condens. Matter

The nuclear and magnetic structure of Fe1+y(Te1-x,Sex) (0 < x < 0.20) compounds was analyzed between 2 K and 300 K by means of Rietveld refinement of neutron powder diffraction data. Samples with x < 0.075 undergo a tetragonal to monoclinic phase transition at low temperature, whose critical temperature decreases with increasing Se content; this structural transition is strictly coupled to a long range antiferromagnetic ordering at the Fe site. Both the transition to a monoclinic phase and the long range antiferromagnetism are suppressed for 0.10 < x < 0.20. The onset of the structural and of the magnetic transition remains coincident with the increase of Se substitution. The low temperature monoclinic crystal structure has been revised. Superconductivity arises for x > 0.05, therefore a significant region where superconductivity and long range antiferromagnetism coexist is present in the pseudo-binary FeTe - FeSe phase diagram., 33 pages, 4 tables, 13 figures

We present a study concerning the partial substitution of yttrium at the lanthanum site of the undoped LaFeAsO and superconducting LaFeAsO0.85F0.15 compounds. We prepared samples with a nominal yttrium content up to 70% producing simultaneous shrinkage of both the a- and c-lattice parameters by 1.8% and 1.7%, respectively. The chemical pressure provided by the partial substitution with this smaller ion size causes a lowering of the spin density wave temperature in the undoped compounds, as well as an increase of the superconducting transition temperatures in the doped ones. The 15% fluorine-doped samples reach a maximum critical temperature of 40.2 K for the 50% yttrium substitution. Comparison with literature data indicates that chemical pressure cannot be the only mechanism which tunes drastically both TSDW and Tc in 1111 compounds. Our data suggest that structural disorder induced by the partial substitution in the La site or by doping could play an important role as well.

SmFeAsO and the isostructural superconducting SmFeAs(O0.93F0.07) samples were prepared. Characterization by means of Rietveld refinement of X-ray powder diffraction data, scanning electron microscope observation, transmission electron microscope analysis, resistivity and magnetization measurements were carried out. Sintering treatment strongly improves the grain connectivity, but, on the other hand, induces a competition between the thermodynamic stability of the oxy-pnictide and Sm2O3, hence worsening the purity of the sample. In the pristine sample both magnetization and resistivity measurements clearly indicate that two different sources of magnetism are present: the former related to Fe ordering at 140 K and the latter due to the Sm ions that orders antiferromagnetically at low temperature. The feature at 140 K disappears in the F-substituted sample and, at low temperatures a superconducting transition appears. The magnetoresistivity curves of the F-substituted sample probably indicates very high critical field values., Submitted to: Superconductor Science and Technology

In this paper we present the physical characterization of sintered RuSr2GdCu2O8 samples prepared with different procedures. In particular we show how the physical properties are affected by the final step, which is one week annealing in flowing Oxygen, and how extensively the annealing procedure affects the visibility of the superconducting behaviour. Moreover, we analyse the complexity of the d.c. magnetic measurements performed on such type of samples below the superconducting transition and the possibility to decode them., Comment: Submitted to Physical Rewiew B, 12 pages 6 figures