The purpose of this study was to investigate the magnetotransport properties of the Ge(0.743)Pb(0.183)Mn(0.074)Te mixed crystal. The results of magnetization measurements indicated that the compound is a spin-glass-like diluted magnetic semiconductor with critical temperature TSG = 97.5 K. Nanoclusters in the sample are observed. Both, matrix and clusters are magnetically active. Resistivity as a function of temperature has a minimum at 30 K. Below the minimum a variable-range hopping is observed, while above the minimum a metallic-like behavior occurs. The crystal has high hole concentration, p = 6.6E20 cm-3, temperature-independent. Magnetoresistance amplitude changes from -0.78 to 1.18% with increase of temperature. In the magnetotransport measurements we observed the anomalous Hall effect (AHE) with hysteresis loops. Calculated AHE coefficient, RS = 2.0E6 m3/C, is temperature independent. The analysis indicates the extrinsic skew scattering mechanism to be the main physical mechanism responsible for AHE in Ge(0.743)Pb(0.183)Mn(0.074)Te alloy., Comment: 4 pages, 3 figures

Magnetotransport properties of spin-glass-like Ge/1-x-y/Sn/x/Mn/y/Te mixed crystals with chemical composition changing in the range of 0.083 < x < 0.142 and 0.012 < y < 0.119 are presented. The observed negative magnetoresistance we attribute to two mechanisms i.e. weak localization occurring at low fields and spin disorder scattering giving contribution mainly at higher magnetic fields. A pronounced hysteretic anomalous Hall effect (AHE) was observed. The estimated AHE coefficient shows a small temperature dependence and is dependent on Mn-content, with changes in the range of 10E-7 < R_S < 10E-6 m^3/C. The scaling law analysis has proven that the AHE in this system is due to the extrinsic mechanisms, mainly due to the skew scattering accompanied with the side jump processes., 7 pages, 4 figures

High-field magnetic measurements performed with the use of magnetooptical Kerr effect (MOKE) in the polar configuration as well as high-field and low-field magnetotransport studies were carried out on Ga1-xMnxAs epilayers grown by low temperature molecular beam epitaxy, and subsequently annealed under various conditions. The structural investigations by means of high resolution XRD were also performed. We observe significant changes in magnetoresistivity curves, magnetization and strain introduced by the annealing., Comment: International Conference on Magnetism, ICM 2003, Roma; to be published on Journal of Magnetism and Magnetic Materials