Search

Abstract Background The pre-polymerization temperature of resin composite restorative materials could influence their adaptation to cavity details. As a current debate is existing about the refrigeration of resin composite restorative materials, this study was designed to assess the effect of refrigeration of 3 types of resin composite restorative materials with different matrix systems on their marginal adaptation in Class II restorations. Methods Forty-two sound maxillary molars, each with two separated Class II cavities, were used in this study. The teeth were assigned into 3 main groups (n = 14) according to the restorative /adhesive system used; an Ormocer-based composite (Admira Fusion/Futurabond M+, Voco GmbH, Cuxhaven, Germany), a methacrylate modified Ormocer-based (Ceram.X SphereTEC One/Prime&Bond Universal, Dentsply Sirona GmbH Konstanz, Germany), and a methacrylate-based (Tetric N-Ceram/Tetric N-Bond Universal, Ivoclar Vivadent AG, Schaan, Liechtenstein). Each group was then divided into 2 subgroups (n = 14) according to the gingival margin location; 1 mm above and 1 mm below the cemento-enamel junction (C.E.J). Each subgroup was further divided into 2 categories (n = 7) according to the storage temperature; stored at room temperature or stored in refrigerator at 4°- 5° C. Epoxy resin replicas were observed under scanning electron microscope (SEM) to examine the marginal gaps. A gab scoring system was used to assess the marginal adaptation of each restoration by giving scores on the basis of measurements of the maximum marginal gaps. The data obtained were statistically analyzed using the Chi-square test at a significance level of p 0.05). As well, there was no statistically significant difference when comparing both marginal locations for each material (p > 0.05). Regarding the effect of storage temperature, statistically significant difference was only observed between the room-temperature stored groups with margins located above C.E.J and their corresponding groups stored in refrigerator (p

Abstract Background The pre-cure temperature is considered an important parameter that affects the polymerization kinetics and the properties of composite restoration. As dissension exists about the effect of storing composite restorative materials in refrigerator, this study aimed to assess the effect of shelf-storage temperature on degree of conversion (DC) and microhardness of three composite restorative materials with different matrix systems. Methods Three commercially-available composite restorative materials were used in this study; an Ormocer-based composite (Admira Fusion, Voco GmbH), a nanoceramic composite, (Ceram.X SphereTEC One, Dentsply Sirona GmbH), and a nanohybrid composite (Tetric N-Ceram, Ivoclar Vivadent AG). Regarding DC and microhardness tests, 60 disc-shaped composite specimens for each test were randomly divided into 3 groups (n = 20) according to the restorative material used. Each group was divided into 2 subgroups (n = 10) according to the composite storage temperature; stored at room temperature or stored in the refrigerator at 4°–5 °C. DC was evaluated using a Fourier-transform infrared spectrometer coupled to an attenuated total reflectance accessory. Microhardness was evaluated using micro-Vickers hardness tester under a load of 50 g with a dwell time of 10 s. The results were analyzed by ANOVA, post-hoc LSD, and independent t-tests at a significance level of p