Introduction: Nickel-titanium rotary endodontic files have been commercially available for decades, but more recent innovations have introduced heat-treated and surface-treated files. This study investigated the corrosion properties of various nickel-titanium files in normal saline and sodium hypochlorite (NaOCl)., Methods: Ten different file brands of size 40 with a 0.04 taper were subjected to electrochemical testing in 0.9% NaCl (saline) and 5.25% NaOCl at room temperature. The Open Circuit Potential (OCP) was observed for 1 hour followed by a cyclic polarization test from -300 to 700 mV and back to -300 mV (vs OCP). Nonparametric ANOVA and a pairwise comparison (P < .05) were used for statistical analysis of the OCP at 1 hour and the corrosion current (Icorr) obtained via the cyclic polarization test., Results: Significant differences (P < .05) were found between files with respect to OCP and Icorr in both solutions. Nine files exhibited significantly greater (P < .05) Icorrs in NaOCl than in saline. Conversely, pitting corrosion was observed in the saline solution but not NaOCl. Weak and/or moderate correlations existed between OCP and Icorr measures in the 2 solutions., Conclusion: Significant differences in electrochemical properties were observed among the 10 brands of files. Overall, there was not a clear trend between conventional, heat-treated, or surface-treated files among OCP or Icorr in either solution., (Copyright © 2024 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Introduction: Mineral trioxide aggregate (MTA) sets via hydration of calcium silicates to yield calcium silicate hydrates and calcium hydroxide (Ca[OH]2). However, a drawback of MTA is its long setting time. Therefore, many additives have been suggested to reduce the setting time. The effect those additives have on setting reaction product formation has been ignored. The objective was to examine the effect additives have on MTA's setting time and setting reaction using differential scanning calorimetry (DSC)., Methods: MTA powder was prepared with distilled water (control), phosphate buffered saline, 5% calcium chloride (CaCl2), 3% sodium hypochlorite (NaOCl), or lidocaine in a 3:1 mixture and placed in crucibles for DSC evaluation. The setting exothermic reactions were evaluated at 37°C for 8 hours to determine the setting time. Separate samples were stored and evaluated using dynamic DSC scans (37°C→640°C at10°C/min) at 1 day, 1 week, 1 month, and 3 months (n = 9/group/time). Dynamic DSC quantifies the reaction product formed from the amount of heat required to decompose it. Thermographic peaks were integrated to determine enthalpy, which was analyzed with analysis of variance/Tukey test (α = 0.05)., Results: Isothermal DSC identified 2 main exothermal peaks occurring at 44 ± 12 and 343 ± 57 minutes for the control. Only the CaCl2 additive was an accelerant, which was observed by a greater exothermic peak at 101 ± 11 minutes, indicating a decreased setting time. The dynamic DSC scans produced an endothermic peak around 450°C-550°C attributed to Ca(OH)2 decomposition. The use of a few additives (NaOCl and lidocaine) resulted in significantly less Ca(OH)2 product formation., Conclusions: DSC was used to discriminate calcium hydroxide formation in MTA mixed with various additives and showed NaOCl and lidocaine are detrimental to MTA reaction product formation, whereas CaCl2 accelerated the reaction., (Copyright © 2015 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Introduction: Recently introduced into the market are shape memory nickel-titanium (NiTi) rotary files. The objective of this study was to investigate the torsion and bending properties of shape memory files (CM Wire, HyFlex CM, and Phoenix Flex) and compare them with conventional (ProFile ISO and K3) and M-Wire (GT Series X and ProFile Vortex) NiTi files., Methods: Sizes 20, 30, and 40 (n = 12/size/taper) of 0.02 taper CM Wire, Phoenix Flex, K3, and ProFile ISO and 0.04 taper HyFlex CM, ProFile ISO, GT Series X, and Vortex were tested in torsion and bending per ISO 3630-1 guidelines by using a torsiometer. All data were statistically analyzed by analysis of variance and the Tukey-Kramer test (P = .05) to determine any significant differences between the files., Results: Significant interactions were present among factors of size and file. Variability in maximum torque values was noted among the shape memory files brands, sometimes exhibiting the greatest or least torque depending on brand, size, and taper. In general, the shape memory files showed a high angle of rotation before fracture but were not statistically different from some of the other files. However, the shape memory files were more flexible, as evidenced by significantly lower bending moments (P < .008)., Conclusions: Shape memory files show greater flexibility compared with several other NiTi rotary file brands., (Copyright © 2013 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Introduction: The purpose of this study was to compare the in vitro torsional stress characteristics of Twisted Files (TFs; SybronEndo, Orange, CA) with 2 milled files of a similar cross-section: EndoSequence (Brasseler USA, Savannah, GA) and ProFile Vortex (DENTSPLY Tulsa Dental, Tulsa, OK)., Methods: File sizes of 25/.06 and 30/.06 from the 3 file types were compared (n = 20/group). Torsional stress resistance was evaluated by measuring the torque in grams per centimeters and the angle of rotation (°) required for instrument separation with the use of a torsiometer instrument. The fractured files were examined using a scanning electron microscope to look at deformation and fracture surface characteristics. The data were analyzed with analysis of variance to determine statistical differences., Results: The 3 file types showed a statistically significant difference in both the maximum torsional stress and the angle of rotation before failure. TFs displayed the least amount of torsional stress resistance and the highest angle of rotation. The 30/.06 size files of all 3 types withstood more torsional stress than the size 25/06 files of the same type. Within each file design, there was not a statistically significant difference in angular rotation between the 25/.06 and 30/.06 groups. The scanning electron microscopic analysis of all 3 file types revealed dimpling near the center of rotation on the fractured surface indicative of torsional stress., Conclusions: The novel techniques used in manufacturing TFs do not make them more resistant to torsional stress as compared with milled nickel-titanium endodontic files of a similar cross-sectional design., (Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.)

Introduction: The purpose of this study was to compare galvanic currents generated by different combinations of commonly used brackets and archwires., Methods: As-received stainless steel, nickel-titanium, and beta-titanium wires were coupled to stainless steel and titanium brackets in an artificial saliva medium. The galvanic current and amount of charge transferred for each pair were monitored with a zero resistance ammeter for 10 hours., Results: Two-way analysis of variance (ANOVA) showed a significant difference in charge and galvanic currents when factored for type of bracket (P <0.001), but no significant difference between them when factored by type of wire (P >0.05). Specifically, a brazed stainless steel bracket was significantly greater in charge transferred and 10-hour galvanic current than metal injection molded stainless steel and titanium brackets (P <0.001), which were not different from each other (P >0.05)., Conclusions: The method of bracket manufacturing might be of equal or more relevance to galvanic corrosion susceptibility than bracket composition., (Copyright © 2011 American Association of Orthodontists. Published by Mosby, Inc. All rights reserved.)

Introduction: The purpose of this investigation was to study the effect of stress and phase transformation on the corrosion properties of a superelastic nickel-titanium orthodontic wire., Methods: The phase transformation profiles of superelastic nickel-titanium (Sentalloy, GAC International, Bohemia, NY) and beta-titanium (TMA, Ormco, Orange, Calif) archwires were analyzed by using differential scanning calorimetry. The force/deflection behavior of the wires at 37 degrees C was measured in a 3-point bending test per modified American Dental Association specification no. 32. Electrochemical testing consisted of monitoring the open circuit potential (OCP) for 2 hours followed by polarization resistance and cyclic polarization tests on archwire segments engaged in a 5-bracket simulation apparatus with bend deflections of 0.75, 1.5, or 3 mm in artificial saliva at 37 degrees C. Nondeflected segments were also tested. Sentalloy was additionally examined for bending and corrosion at 5 degrees C, where it exists as martensite and is devoid of stress-induced phase transformation. OCP at 2 hours and corrosion current density (i(corr)) were analyzed by using ANOVA and Tukey tests (alpha = .05) (n = 10 per deflection)., Results: Significant differences (P < 0.05) in OCP with deflection were found for the TMA and the Sentalloy wires at 5 degrees C, but not for Sentalloy at 37 degrees C. Significant differences (P < 0.05) in i(corr) with deflection were also observed. All 3 wire groups had their lowest mean i(corr) values when not deflected. The i(corr) for superelastic Sentalloy (37 degrees C) peaked at 0.75 mm deflection before the wire's stress-induced phase transformation point and then decreased with further deflection and transformation. The i(corr) values for TMA and Sentalloy at 5 degrees C, both of which do not undergo phase transformation with deformation, continuously increased from 0 to 1.5 mm deflection before decreasing at the 3.0-mm deflection., Conclusions: Stress increased the corrosion rate in nickel-titanium and beta-titanium orthodontic wires. Alterations in stress/strain associated with phase transformation in superelastic nickel-titanium might alter the corrosion rate in ways different from wires not undergoing phase transformation.

Objective: To investigate the effect of two glass-polyalkenoate restorative materials used as root-dentin replacements on the fracture strength of Class II amalgam restorations., Materials and Methods: Class II slot preparations extending 2mm apical to the cemento-enamel junction were made in 30 teeth and randomly assigned to three groups. Group 1 (Control): restored entirely with amalgam (Tytin, Sybron Kerr, Orange, CA, USA). Group 2: The root-dentin area was restored with a viscous conventional glass-polyalkenoate restorative material (Fuji IX GP, GC America, Alsip, IL, USA), and the remainder of the preparation restored with amalgam. Group 3: The root-dentin area was restored with a resin-modified glass-polyalkenoate restorative material (Fuji II LC, GC America) and the remainder restored with amalgam. The amalgam restorations were loaded in compression to failure and the data analyzed using one-way ANOVA (alpha=0.05)., Results: No significant differences in fracture strength were found., Conclusion: Root-dentin replacement with the tested glass-polyalkenoate materials did not affect the fracture strength of Class II amalgam restorations.

The purpose of this in vitro study was to evaluate the cutting efficiency of 4 orthograde ultrasonic tips and describe a nonstatic cutting model. Forty molars were extracted and decoronated. Each group contained 10 tips. The samples were fixed to a double pan balance that applied a constant vertical force of 40 g to the ultrasonic tips. The ultrasonic handpiece was mounted to a cyclic axial fatigue testing apparatus to generate a 3-mm horizontal movement of the ultrasonic tip during the cutting procedure. Three cutting cycles of 30 seconds were tested for each power setting of 3, 5, and 7. The weight of the samples was measured before and after the 3 cycles. The cutting efficiency was determined by the weight change caused by dentin removal. The Buc-1 ultrasonic tip had a significantly greater cutting efficiency than the other 3 tips at each of the 3 power settings (P < .05).

The purpose of this in vitro study was to compare the bond strength of various obturation materials to root canal dentin by using a push-out test design. Twenty-five single-rooted extracted human teeth were used in this study. The crowns were removed, and root canal instrumentation was completed by using Endogel-coated 0.06 EndoSequence rotary files (Brasseler, Savannah, GA) and appropriate irrigation with 5.25% NaOCl and a final rinse with 17% EDTA. After instrumentation, the roots were randomly divided into five single-matched cone obturation groups (n = 5 roots/group), as follows: group 1, gutta percha with Kerr EWT (Kerr Corp, Romulus, MI); group 2, gutta percha with AH Plus (Dentsply, DeTrey, Germany); group 3, Resilon (Pentron Clinical Technologies, Wallingford, CT) and Epiphany (Pentron); group 4, Activ GP (Brasseler) obturation system; and group 5, EndoREZ obturation system (Ultradent, South Jordan, UT). The obturated roots were cut perpendicular to the long access to create 1-mm thick slices from the apical, middle, and coronal thirds. The bond strength was measured for each test slice with a push-out testing machine. Statistical analysis was completed by using a two-way analysis of variance and the post hoc Tukeys test with significance set at p < 0.05. Group 2 showed a significantly (p < 0.05) greater bond strength compared with all other groups. Also, groups 1 and 4 had significantly (p < 0.05) higher bond strengths compared with groups 3 and 5.

The purpose of this study was to compare the micropush-out bond strength of Resilon to that of gutta-percha. Extracted human anterior teeth were used for evaluation. The crowns were removed and the root canals were instrumented with Gates Glidden drills and 0.06 Profile rotary files. Instrumentation was performed with 5.25% sodium hypochlorite irrigation and a final rinse of 17% EDTA. The teeth were randomly divided into two groups. Gutta-percha group: obturation with gutta-percha and Kerr Pulp Canal Sealer EWT. Resilon group: obturation with Resilon points, Epiphany Primer, and Root Canal Sealant. The teeth were cut perpendicular to their long axis to obtain a series of 1.0 mm thick disks (n = 15 per group). Micropush-out bond strengths to root canal dentin were measured. The results show that the mean bond strength to root canal dentin was significantly higher (p < 0.05) in the Resilon/Epiphany group as compared to the gutta-percha/Kerr Pulp Canal Sealer EWT group.

A new polymer-based obturating material, Resilon, has been developed but there have been no studies identifying its thermal properties. The purpose of this study was to compare the melting point, specific heat, enthalpy change with melting and heat transfer between gutta-percha (GP) and Resilon (R). The first three tests were determined using a differential scanning calorimeter and the heat transfer test was determined using a split-tooth model. Results show no significant difference (t test, p > 0.05) between gutta-percha and Resilon for the melting point temperature (GP: 60.01 degrees C; R: 60.57 degrees C). There was a significant difference (t test, p < 0.05) in specific heat capacity (GP: 0.94 J/g degrees C, R: 1.15 J/g degrees C) and endothermic enthalpy change (GP: 10.88 J/g, R: 25.20 J/g) between the two materials. The heat transfer test showed a significant difference (Mann-Whitney, p < 0.05) in temperature increase between gutta-percha and Resilon within 3 mm of the heat source.