The lifetime of tungsten (W) monoblocks under fusion conditions is ambivalent. In this work, the microstructure dependent mechanical behaviour of pulsed high heat flux (HHF) exposed W monoblock is investigated. Two different microstructural states, i.e. initial (deformed) and recrystallized, both machined from HHF exposed monoblocks are tested using tensile and small punch tests. The initial microstructural state reveals a higher fraction of low angle boundaries along with a preferred orientation of crystals. Following HHF exposure, the recrystallized state exhibits weakening of initial texture along with a higher fraction of high angle boundaries. Irrespective of the testing methodology, both the microstructural states display brittle failure for temperatures lower than 400∘C. For higher temperatures (>400∘C), the recrystallized microstructure exhibits more ductile behaviour as compared to the initial state. The observed microstructural state-dependent mechanical behaviour is further discussed in terms of different microstructural features. The estimated brittle-to-ductile transition temperature (BDTT) range is noticed to be lower for the recrystallized state as compared to the initial state. The lower BDTT in the recrystallized state is attributed to the high purity of the W in combination with its low defect density, thereby preventing segregation of impurities at the recrystallized boundaries and the related premature failure. Based on this observation, it is concluded that the common opinion of the aggravation of BDTT in W due to recrystallization is not unerring, and as a matter of fact, recrystallization in W could be instrumental for preventing the self-castellation of the monoblocks.

Small Punch Creep technique was used as a screening procedure to evaluate the creep properties of different microstructures developed in a thermomechanical simulator. The goal seek was to generate alternative microstructures in a conventional ferritic-martensitic G91 steel grade which boost thermal stability at temperatures as high as 700 °C. The developed microstructures allow studying the effect of the austenitization temperature optimized by thermodynamic calculations and the ausforming on the creep strength and ductility. The improvement in creep strength recorded was attributable to a higher number density of MX precipitates. By contrast, these microstructures showed an important reduction in creep ductility., Authors acknowledge financial support to Spanish Ministerio de Economia y Competitividad (MINECO) through in the form of a Coordinate Project (MAT2016-80875-C3-1-R). The authors are grateful for the dilatometer tests by Phase Transformation laboratory. J. Vivas acknowledges financial support in the form of a FPI Grant BES-2014-069863. This work contributes to the Joint Programme on Nuclear Materials (JPNM) of the European Energy Research Alliance (EERA).