Currently, advanced ODS copper alloy is under study as a potential fusion material providing good mechanical properties. In this work, in order to develop a high performance ODS copper containing 0.5 wt% Y2O3 oxide particles, the effect of room temperature rolling and subsequent annealing on the grain structure evolution, texture development and tensile properties are studied using EBSD, TEM and tensile tests. Microstructure evolution studies show the grain structure coarsens by enhancing the Brass texture during increase of rolling reduction and a unique single crystal-like brass-texture deformed structure is achieved after 80% rolling reduction. We found the deformation mechanism of partial slip by a/2 211 dislocations facilitated by the pinning of a/2 101 perfect dislocations through fine oxide particles is responsible for formation of Brass texture during room temperature rolling. Furthermore, the recrystallization of ODS copper retards to high temperature of similar to 700 degrees C and shows a fine-grained microstructure with different orientations of Goss, Brass, S and Copper. Evaluation of microstructure-mechanical properties of the recrystallized samples expresses that the bimodal grain size distribution at 800 degrees C for 30 min offers a good tensile strength-ductility (UTS: 491 MPa, el(t): 19%) at ambient temperature.

Static discontinuous recrystallization was studied during room temperature annealing of a newly designed 80% room temperature rolled oxide dispersion strengthened copper. At early stages of annealing, fine new oriented nanosized/submicron grains were recrystallized in the unique matrix of single brass-oriented deformed grain. Upon longer annealing time up to 14 months, the size, area fraction and number density of the recrystallized grains increased significantly along with changing the crystallographic textures. The analysis of misorientation angle distribution of boundaries indicated transformation of low angle boundaries to high angle boundaries results in nucleation of recrystallized grains by significant contribution of static recovery. Furthermore, the constant level of mechanical hardness after recrystallization was interpreted by the balance between grain size hardening, oxide particle hardening and strain hardening. (C) 2019 Elsevier B.V. All rights reserved.