Search

This work aimed to synthesize an effective material having greater potential to reduce water pollution caused by industrial waste and exhibit efficient antibacterial potential. The transition metals (Manganese-Mn, Zinc-Zn) and post transition metal (Tin-Sn) reacted with TeO2 in a stoichiometric ratio by adopting a solid-state reaction. The crystallite size of the synthesized compounds MnTeO3 (D1), ZnTeO3 (D2), and SnTe3O8 (D3) was measured by the Debye-Scherrer formula by extracting data from the FWHM. D1 and D2 exhibit the orthorhombic structure whereas D3 has a simple cubic structure and crystalline size was measured by FWHM i.e., 221 nm, 458 nm, and 153 nm. Catalytic degradation efficiency for the removal of MB dye was found to be in the range of 66%-73%. Additionally, these substances have strong antimicrobial action alongside both bacteria and fungi, such as Escherichia coli, Staphylococcus aureus with maximal zone inhibitions of 35.0 mm and 12.5 mm for each kind of bacterium. The highest antifungal activity of Mn integrated was estimated to be 37.2 mm versus Aspergillus niger and 15.1 mm alongside Coccidioides. According to the findings, the manufactured material has effective photocatalytic and antimicrobial activities.

The wastewater released from industries contains many harmful materials like organic dyes and toxic metal ions which badly affect our environment. Nanotechnology is one of the unique approaches to reducing these chemicals. In current research work monometallic ZnO and Co-ZnO bimetallic NPs were synthesized from Brassica rapa leave’s extract and then these were employed for the elimination of methylene blue (MB) and metal ions of Cu (II). Characterization was done by several analytical techniques such as EDX, FTIR, UV–Visible spectroscopy, SEM and XRD. The average diameter of ZnO and Co-ZnO BMNPs was found to be 32.94 nm and 13.82 nm assessed by XRD analysis. The SEM investigation revealed that the produced NPs had a spherical shape. Three distinct methods have opted to determine the antioxidant potential of synthesized NPs. Different factors like pH, contact time, NPs conc., dye conc. and temperature were studied for the elimination of dye while for the eradication of Cu (II) ions; pH, contact time, NPs conc. and adsorbate doses were studied. Adsorption isotherm and kinetic studies were employed for MB and Cu (II) ions elimination while thermodynamic studies were also done for the elimination of MB.

This research work includes the fabrication of iron oxide nanoparticles (Fe2O3 NPs) by green construction approach using Wisteria sinensis leaves extract. Due to its eco-friendly approach, the synthesis of iron oxide NPs (Fe2O3 NPs) using various plant sources, such as plant parts, and microbial cells have gained a lot of attention in recent years. Cost-effectiveness and ease of availability make Wisteria sinensis leaves extract a potential candidate for the construction of iron oxide NPs. The various key features like biocompatibility, non-toxicity capping, and stabilizing agents present in biological sources are advantageous for usage in a variety of applications. The phytoconstituents present in the leaf extract of Wisteria sinensis serve as reducing and stabilizing agents. The biologically fabricated (Fe2O3 NPs) were analyzed using FT-IR, XRD, UV–vis spectroscopy, and SEM. In the present work, the antioxidant and photocatalytic dye degradation efficiency of Fe2O3 NPs has been studied. The dye degradation efficiency of methylene blue dye was found to be 87% at 180 min upon exposure to sunlight. The capacity of Fe2O3 NPs to scavenge 2,2-diphenyl-1-picrylhydrazyl hydrate free radicals (DPPH) was examined using a UV–Vis spectrophotometer. The study compared the radical scavenging activity (RSA) of Fe2O3 nanoparticles (NPs) with that of the standard antioxidant ascorbic acid. The results demonstrated that Fe2O3 NPs have a greater ability to scavenge radicals than ascorbic acid. The half-maximal inhibitory concentration (IC50) of Fe2O3 NPs was observed to range from 0.12 to 0.17. Furthermore, Fe2O3 NPs displayed the highest antifungal activity, with an inhibition zone of 26.8 mm against F. oxysporum. These findings suggest that the biologically synthesized Fe2O3 NPs possess potent antimicrobial and dye degradation properties.