Increased urbanization and increase in population has led to an increased demand for fuels. The result is the prices of fuels are reaching new heights every day. Using low-cost feedstocks such as rendered animal fats in biodiesel production will reduce biodiesel expenditures. One of the low-cost feedstocks for biodiesel production from poultry feathers. This paper describes a new and environmentally friendly process for developing biodiesel production technology from feather waste produced in poultry industry. Transesterification is one of the well-known processes by which fats and oils are converted into biodiesel. The reaction often makes use of acid/base catalyst. If the material possesses high free fatty acid then acid catalyst gives better results. The data resulted from gas chromatography (GC) revealed these percentages for fatty acid compositions: myristic acid, palmitic acid, stearic acid, oleic acid, linoleic acid and arachidonic acid. The biodiesel function group was analyzed by using FTIR. This study concluded that the rooster feathers have superior potential to process them into biodiesel than broiler chicken feathers fat because of fatty acid composition values and it has important properties of biodiesel.

Alstonia scholaris is one of the most important medicinal plants and herein, we present the synthesis of zinc oxide nanoparticles using the bark extract of Alstonia scholaris, and evaluation of their antimicrobial efficacy. Stable ZnO nanoparticles were formed by treating 90 mL of 1 mM zinc nitrate aqueous solution with 10 mL of 10% bark extract. The formation of Alstonia scholaris bark extract mediated zinc oxide nanoparticles was confirmed by UV-visible spectroscopic analysis and recorded the localized surface plasmon resonance (LSPR) at 430 nm. Fourier transform infrared spectroscopic (FT-IR) analysis revealed that primary and secondary amine groups in combination with the proteins present in the bark extract is responsible for the reduction and stabilization of the ZnONPs. The crystalline phase of the nanocrystals was determined by XRD analysis and morphology was studied using transmission electron microscopy (TEM). The hydrodynamic diameter (26.2 nm) and a positive zeta potential (43.0 mV) were measured using the dynamic light scattering technique. The antimicrobial activity of Alstonia scholaris ZnONPs was evaluated ( in-vitro ) using disc diffusion method against fungi, Gram-negative and Gram-positive bacteria which were isolated from the biofilm formed in drinking water PVC pipelines. The results obtained suggested that ZnO nanoparticles exhibit a good anti-fungal activity than bactericidal effect towards all pathogens tested in in-vitro disc diffusion method (170 ppm, 100 ppm and 50 ppm). Further, the toxicity of biosynthesized ZnONPs was tested against Alstonia scholaris to evaluate the cytotoxic effect that displayed LC 50 value of 95% confidence intervals.