Search

This study focuses on enhancing the mechanical strength of aquaporin (AQP)-based biomimetic membranes for seawater desalination. AQP incorporated vesicles were embedded into the selective layer of an optimized thin film composite (TFC) membrane. The resultant membrane, denoted as ASW, exhibited a stable water flux around 20 L·m−2·h−1 and 99% NaCl rejection at a constant pressure of 55 bar using 32,000 mg·L−1 NaCl solution as feed in reverse osmosis (RO) measurement. The robustness of the ASW membranes were evaluated. The water flux of ASW membrane was almost 100% enhanced compared with that of AQP-free control TFC membranes. The filtration performance of the ASW membrane was further evaluated by a seven-day desalination test using a real seawater secondary effluent collected from a desalination plant in Singapore as feed. To our best knowledge, our study is the first report on the AQP-incorporated RO membrane applied for seawater desalination. A commercial SW30HR membrane was tested in parallel for comparison. The robust ASW membrane exhibited a nearly 80% higher water flux in comparison to the SW30HR membrane with a comparable overall solute rejection, suggesting the advantage and feasibility of Aquaporin based biomimetic membranes for seawater desalination. • The mechanical strength of aquaporin incorporated polyamide layer was characterized with AFM. • The effects of high pressure compaction and salinity on aquaporin incorporated polyamide layer were investigated. • The aquaporin based biomimetic membranes were optimized for seawater desalination (SWRO) application. • A seven-day SWRO measurement of the ASW was conducted using a real seawater secondary effluent. [ABSTRACT FROM AUTHOR]

Thin film composite (TFC) polyamide (PA) membranes experience compaction at high pressure applications, resulting in the reduction in water permeability. However, the compaction mechanism is still unclear especially for different PA morphologies and substrate structures. In this work, we systematically studied the compaction of TFC PA membranes with different structures and morphologies. We first examined 2 main types of commercial reverse osmosis (RO) membranes: brackish water RO and seawater RO membranes. After that, we synthesised four types of TFC membranes with tailored PA and substrate structures to further understand the compaction behaviors. TFC membrane with a PA layer of low protuberances or nodules and dense substrate showed excellent resistance against high pressure (50 bar), with only a slight irreversible decrease of 2.1–3.5% in water permeability when retested at 5 bar. However, the PA layer of high protuberances experienced significant compaction even when it was supported by a similar dense substrate. The permeability of the TFC membrane decreased ∼10% as a result of the decrease in the effective area of the active layer. On the other hand, the TFC membrane with a PA layer of low protuberances formed atop a loose substrate showed a greater decrease (∼18.5%) in water permeability. The densified skin layer and collapsed macro-voids within the loose substrate resulted in a ∼40% decrease in the overall height of the PA layer and a 65% decline in substrate surface porosity, respectively, which are identified as the reasons for the reducing water permeability. Notably, the water-salt selectivity of this particular membrane was seriously deteriorated after compaction due to the presence of subtle defects in the PA layer caused by the drastic deformation of the loose substrate. This work deepens the understanding of the compaction behaviors of TFC PA membranes, providing a clear fundamental guidance on designing membranes applied at high operating pressures. [Display omitted] • The compaction of TFC PA membranes with different PA and substrate structures at 50-bar hydraulic pressure was investigated. • The high protuberances on the PA layer were compressed at 50 bar, resulting in an apparent decline in water permeability. • A porous substrate resulted in the decreases of water permeability and selectivity simultaneously after membrane compaction. • A TFC membrane with a low-protuberance PA layer and dense substrate is suitable for use in high-pressure processes. [ABSTRACT FROM AUTHOR]

A scaled-up hollow fibre thin-film composite (TFC) module was successfully developed for organic solvent forward osmosis (OSFO) application in the pharmaceutical industry. The membrane consists of cross-linked P84 polyimide substrate with a polyamide selective layer, formed via interfacial polymerisation. The performance of the lab-scale module was compared to the scaled-up module in reverse osmosis and forward osmosis modes. The results from both tests revealed that the solvent permeability of the scaled-up module decreased while its selectivity increased slightly. This might be caused by the uneven distribution of liquids during interfacial polymerisation, leading to varied membrane performance. The scaled-up module was further tested for OSFO performance using a range of PEG-400 concentrations (0.5–2 M) in acetone and isopropanol as draw solutions. At 2 M PEG-400 concentration, the module demonstrated high isopropanol and acetone permeability of 0.63 LMH and 13.9 LMH, respectively. Moreover, the reverse solute flux of PEG-400 in acetone and isopropanol were relatively low at 0.188 g/l and 0.153 g/l, respectively. The module was further tested for OSFO application in the pharmaceutical industry by concentrating levofloxacin in acetone, using 2 M PEG-400 as draw solution. The process was able to concentrate levofloxacin from 1000 ppm to 16,000 ppm with very low reverse solute flux of 0.178 g/l. Therefore, this work presents a scalable TFC membrane for OSFO application in the pharmaceutical industry. [Display omitted] • Scaled-up module (0.4 m2) of TFC hollow fibre membrane for organic solvent forward osmosis process was successfully fabricated. • High porosity (79%) and low structural parameter (217 μm) for membrane substrate was achieved. • Membrane exhibited excellent acetone and IPA solvent flux of 13.9 LMH and 0.63 LMH, respectively, using a 2 M PEG-400 draw solution. • A pharmaceutical stream was concentrated to a factor of 16 with low specific reverse solute flux [ABSTRACT FROM AUTHOR]

Nanoscale characteristics of the polyamide layer are key towards the high desalination performance of thin-film composite reverse osmosis (TFC-RO) membranes. Further advancements in the performance of TFC membranes necessitate a comprehensive understanding of the desired polyamide characteristics and its formation mechanisms. Empirical evidence has shown that the properties of the support layer is as equally important as the interfacial polymerization (IP) conditions in the fabrication of high permselectivity TFC membranes for desalination. Herein, we discuss the properties of polyamide layers formed using identical IP conditions over support membranes of different polymers and chemistries (polyethersulfone, polyetherimide and polysulfone) under fairly similar surface pore properties. The characteristics of the polyamide layers formed thereon displayed different physicochemical properties. It is postulated that the support membrane chemistry actually affects the IP reaction and polyamide formation by controlling the amine diffusion speed as well as the breadth of the IP reaction zone (i.e., the region between the interface and the furthest point in which the reaction occurs). Transmission electron microscopy analyses further revealed the nanoscale differences in the polyamide layer (heights ranging from 50 to 200 nm), including intrinsic thickness of basal layer (~10–35 nm) and leaf-like top layer (~20–85 nm), as well as the presence of nanovoids. Finally, we propose a conceptual model to underline the role of support membrane chemistry in the IP reaction, and consequently the formation mechanism of the nanoscale polyamide features. The mechanistic insights from this study are expected to provide more understanding towards a better control over the fabrication of polyamide layers for TFC membranes. The findings in this work are also expected to facilitate tailoring polyamide layers for specific osmotically driven processes. [Display omitted] • Support membrane chemistry affects MPD diffusion and partitioning extent in IP. • TEM and SEM analyses revealed changes in the polyamide (PA) nanoscale morphology. • PA layer of TFC-PES membrane was thin and smooth without any nanovoids. • PA layer of TFC-PSf membrane had thick base, thin leaves and multi-layer nanovoids. • PA layer of TFC-PEI membrane had thin basal layer with clumpy roof-like top layer. [ABSTRACT FROM AUTHOR]

Seawater reverse osmosis (SWRO) is the key technology driving an energy-efficient and cost-effective desalination process. At the center of this technology are the thin film composite (TFC) membranes, which not only promise a stable operation but also high separation performances. The objective of this review is to consolidate recent advances in SWRO membranes from the standpoint of membrane materials, fabrication methodologies and applications. First, the thermodynamic limit and energy consumption of SWRO desalination are reviewed, before we discuss the current status of SWRO membranes, highlighting the four main challenges to date – permselective tradeoff, relatively low single-pass boron rejection, membrane fouling and poor chlorine resistance. Thereafter, a comprehensive review of the membrane development is presented. We examine findings reported in research papers and patents, and various methods to achieve SWRO membranes of higher permselectivity, boron rejection, and chlorine resistance as well as lower fouling propensity. Key insights from the membrane industry are also furnished. Then, we put together an outlook, featuring our perspectives on SWRO membrane development. Empirical data in this review are collated into an upper-bound relationship, which is tailored specifically for SWRO membranes and expected to provide benchmarking for future SWRO membrane development. Since the traits of SWRO membranes are unique from those of brackish water RO (BWRO) membranes, we also distinguish the methods used for SWRO membrane fabrication to help zero in on the correct strategies, and provide insights for advancing new membrane designs. Overall, this review sums up the current state-of-the-art SWRO membranes, looking at the array of fabrication methods used thus far, and putting into perspective critical strategies to realize the next-generation TFC membranes that can address the future demands of SWRO and deliver a more competitive desalination process. [Display omitted] • Recent advances in SWRO membrane are collated from papers and industrial patents. • Current status and future outlook of SWRO membrane industry are discussed. • A permselectivity upper bound is established specifically for SWRO membranes. • The upper bound is given by A/B = 46.75 A −1.72 (A/B in bar−1 and A in Lm−2h−1 bar−1). • A roadmap for SWRO membrane fabrication is proposed (short/long-term strategies). [ABSTRACT FROM AUTHOR]

This study examined the feasibility and performance of a nanochannel-based biomimetic membrane (NBM) for brackish reverse osmosis (RO) desalination. Two types of peptide-attached synthetic nanochannels, (pR)-pillar[5]arenes (pRPH) and (pS)-pillar[5]arenes (pSPH), were incorporated into liposomes. pSPH is a diastereomer of pRPH and was used as a negative control (i.e. mutant) to pRPH in this work. The nanochannel-containing liposomes (e.g. pRPH-liposomes) were then immobilized into the active layer of the RO membranes via in situ interfacial polymerization on the top of a polysulfone support membrane to form NBM-pRPH membranes. To maximize the potential and benefits of the NBM-pRPH membrane, the physical characteristics of the polyamide layer was further tuned using some additives and the eventual membrane was named as NBM-pRPH-A. The NBM-pRPH-A membrane exhibited a water permeability of 6.09 L m−2 h−1 bar−1 and 98.2% NaCl rejection under a 15.5 bar applied pressure using 2000 mg L−1 as feed solution. The 62% flux increment with respect to the pristine control is postulated to arise from a thinner, less cross-linked (more free volume) and more hydrophilic active layer as well as the possible supplementary transport pathways of the pRPH-liposomes. The performance of the NBMs under differential feed pressures and temperatures further exemplifies the water permeation property of the pRPH nanochannels. Accordingly, the NBM-pRPH-A gave a water permeability higher than commercial RO membranes tested in this work (DuPont BW30 and Hydranautics ESPA2) as well as other RO membranes reported in the literature. This study provides a tangible foundation for the development of NBMs for brackish RO desalination. [Display omitted] • Synthetic pRPH nanochannel-based biomimetic membrane was used for BWRO application. • pRPH-liposomes were incorporated onto the PA layer via interfacial polymerization. • STEM-EDX analysis revealed the existence of liposomes in the PA layer. • High permeability of 6.09 Lm−2h−1bar−1 (98.2% NaCl rejection) was reported in BWRO. • RO tests under increasing ΔP and temperature suggested water transport across pRPH. [ABSTRACT FROM AUTHOR]

Although a highly porous support membrane has attracted increasing attention as an alternative to enhance the water permeability of a thin-film composite (TFC) membrane without compromising salt rejection, its feasibility has not ever been tested in seawater desalination. This study explored the availability and potential of a highly porous microstructured (HPμS) support membrane as a support for a seawater reverse osmosis (SWRO) membrane. Our lab-made membranes, TFC-HPμS, exhibited a higher water permeability of 1.62 L m−2 h−1 bar−1 as compared with most of the state-of-the-art SWRO membranes recently reported in the literature, while achieving comparable NaCl rejection (99%) in SWRO test condition (55 bar, 35,000 mg L−1 of NaCl). This excellent performance is thought to stem from the HPμS support endowing a TFC membrane with comparable mechanical properties to that of existing support used for conventional SWRO membrane and shortened effective diffusion pathway of water molecules over the active layer. The robustness and enhanced mechanical strength of the TFC-HPμS membrane are attributed to its narrow and regularly arranged finger-like structure ensuring the even distribution of local stresses, thereby eliminating the presence of stress convergence points. The shortened effective diffusion pathway was estimated to be achieved mainly by less localized surface pores due to the HPμS support's highly porous surface with a larger number of even distributed surface pores. This study potentially opens up another workable pathway in the fabrication of SWRO membranes with enhanced performance without significant sacrifice of the selectivity. • Highly porous microstructured support membrane was used for seawater desalination. • The regularly arranged sublayer enhanced the mechanical strength of the support. • The effective diffusion pathway can be shortened with less localized surface pores. • The tuned TFC membrane exhibited higher permselectivity as compared to the control. • High permeability of 1.62 Lm−2h−1bar−1 (>99% NaCl rejection) was reported in SWRO. [ABSTRACT FROM AUTHOR]