The absorption spectra, emission under 940 nm excitation by laser diode, and fluorescence lifetimes of as-grown and annealed Cr,Yb:YAG crystal have been investigated at room temperature. The increase of absorption coefficients at 941 and 1030 nm and the quenching of Yb3+ emission intensity and fluorescence lifetime after annealing are due to the increase of the concentration of Cr4+ ions. The data of thermal expansion and specific heat of the crystal have been measured. The thermal expansion coefficient is α=8.71×10−6 /K. The specific heat is 89.9 cal/mol K at 320.5 K. [Copyright &y& Elsevier]

Five atomic percent Yb:YAG laser crystals have been grown by Czochralski (CZ) and temperature gradient technique (TGT) method. The absorption spectra of as-grown and annealed Yb:YAG crystals have been investigated. There is no Yb2+ and color center absorption in TGT-grown Yb:YAG crystals; the absorption peak of CZ-grown Yb:YAG crystals after O2-annealing at 255 nm is attributed to Fe3+ ions. The longitudinal distribution of Yb3+ ions has also been studied; TGT-grown Yb:YAG crystal has a larger distributing inhomogeneity of Yb3+ although it is large sized. [Copyright &y& Elsevier]

Abstract: The high optical quality Tm: YAG single crystals with dopant concentrations of 2, 4, 8 at % Tm3+ ions have been grown by the Czochralski (CZ) method .The segregation coefficients of Tm3+ ions in CZ-grown 2, 4, 8 at % doped Tm: YAG crystals determined by ICP-AES method are equal to 0.93, 1.04, 1.10, respectively. The absorption spectra in the range of 190–900nm and the IR absorption spectra in the range of 1000–4500cm-1 of the Tm: YAG crystals were also measured at room temperature. The results indicate that Tm: YAG is favorable for laser diode-pumped system, and air annealing can improve the quality of the Tm: YAG crystal. [Copyright &y& Elsevier]