Search

Oriented construction of high-performance mesoporous TiNb 2 O 7 (m-TNO) is important to the design innovation of anode material for next-generation lithium-ion batteries (LIBs) due to the high capacity and long cyclic life of m-TNO. However, the conductivity enhancement of m-TNO and thus accelerating Li+ transfer is still the key point to realize its practical application in LIBs. In this work, a synergistic strategy based on the single-core/dual-shell m-TNO@TiC@NC hierarchical structure is put forward, which is achieved by using m-TNO as host architecture as well as TiC and N-doped carbon layer (NC) as dual-shell layers. The results show that the m-TNO@TiC@NC hierarchical structure can not only provide an integrated conductive network to improve the conductivity of m-TNO, but also can establish a reinforced structure to maintain the anode stability. Besides, it is found that the m-TNO@TiC@NC composite has a high capacity of 328.6 mAh g−1 at 0.5 C after 200 cycles and a high-rate capacity of 186.4 mAh g−1 at 5 C by galvanostatic discharge-charge tests. Therefore, this kind of special single-core/dual-shell structure design can convincingly enhance the conductivity of m-TNO and facilitate the Li+ transfer rate, thus promoting electrochemical performances of LIBs due to the synergistic effect of dual-shell layers. Image 1 • The m-TNO@TiC@NC composite is achieved by using m-TNO as host architecture as well as TiC and NC as dual-shell layers. • The m-TNO@TiC@NC composite shows the single-core/dual-shell hierarchical structure. • The new-type ceramic material TiC is used as conducting layer. • The m-TNO@TiC@NC composite displays good electrochemical performance. [ABSTRACT FROM AUTHOR]

The activated carbon cloth (ACC@TNO) with flexible self-support structure, which is decorated by TiNb 2 O 7 (TNO) nanoparticle, is successfully obtained through hydrothermal reaction and calcination process in high temperature, and is used as the binder-free anode material of lithium ion batteries (LIBs). The morphology characteristic, pore structure properties and the phase structure of the ACC@TNO composites are detailedly studied by the scanning electron microscopy (SEM), Brunauer–Emmett–Teller adsorption/desorption measurement (BET) and X-ray diffraction (XRD). Meanwhile, the electrochemical properties of ACC@TNO composite are further tested by cyclic voltammetry and galvanostatic charge-discharge tests. As a result, the LIBs with ACC@TNO as anode material shows an initial discharge capacity of 356 mAh g−1 and an initial coulombic efficiency (ICE) of 87% at the current density of 0.5 C with the voltage window of 1.0–3.0 V. It also has been found that the reversible capacity can still keep as 290 mAh g−1 with the capacity retention of 81% after 500 cycles. Besides, when the cutoff voltage range is set to 0.01–3.0 V, the reversible capacity can reach 340 mAh g−1. Apparently, this work is of great significance for the exploration of the new anode materials with high performance and long cyclic life in next-generation LIBs. Image 1 • The ACC@TNO composite is obtained by epitaxially growing TNO particles on ACC surface like stab grown on the thorn. • The thiourea is use as a nitrogen source and sulfur source to treat the carbon cloth. • The ACC@TNO composite is binder-free anode material. • The ACC@TNO composite displays good electrochemical performance. [ABSTRACT FROM AUTHOR]