Highlights: [•] The effects of Mn doping on structures, electric, magnetic, and magnetocapacitive properties of the 0.33Ba0.70Ca0.30TiO3–0.67BiFeO3 + x wt%MnO2 (BCT-67BF:Mn100x, x =0–0.6) ceramics have been intensively investigated. [•] The BCT-67BF:Mn100x ceramics with x =0–0.6 have diphasic tetragonal–rhombohedral phases. Mn doping improves the densification and significantly decreases the grain size. [•] As x increases, the relaxor degree increases, the ferroelectricity and piezoelectricity weaken monotonically, while the magnetism enhances firstly, reaching the maximum near x =0.5, and then decreases. [•] The room temperature relative dielectric constant shows an obvious increase with increasing applied magnetic fields (H), the magnetocapacitive coefficient (ε r(H)− ε r(0))/ε r(0) decreases with increasing Mn content, from 2.96% for x =0 – 0.86% for x =0.6 . [ABSTRACT FROM AUTHOR]

Abstract: The effects of sintering temperature and poling conditions on the electrical properties of tetragonal and orthorhombic diphasic Ba0.70Ca0.30TiO3 (BCT) lead-free ceramics have been systematically investigated. On the one hand, with increasing sintering temperature from 1270°C to 1400°C, the bulk density increases monotonically and the Curie temperature keeps almost constant with the value of ∼120°C, whereas the grain size, the maximum relative dielectric constant, room temperature polarization reach the maximum values for samples sintered at 1340°C. On the other hand, it is found that the piezoelectric property depends on poling electric field and poling temperature significantly. An enhanced piezoelectric behavior of d 33=126pC/N, k p =0.29, and Q m =588 is obtained for the BCT ceramics poled at 100°C with 30kV/cm field for 20min. The aging behavior of the piezoelectric property is also investigated. [Copyright &y& Elsevier]