Search

Hierarchical porous ceramic catalyst carriers, which exhibit good catalytic performance, are widely used in the petrochemical industry. However, the fabrication of ceramic carriers with hierarchically porous structures is highly challenging for conventional preparation processes. Thus, a strategy for designing and manufacturing hierarchically porous alumina ceramic catalyst carriers using aluminium trihydrate as raw material and powder bed fusion (PBF) as the forming process is proposed herein. PBF process parameters were optimised to define the processing window for creating ceramics with complex structures. Controllable pore characteristics in nano- and microscales has been achieved by combining dehydroxylation, PBF, and post-sintering processes. The effects of raw material composition and process parameters on crush strength, porosity, and specific surface area were systematically investigated. The resulting porous ceramics exhibit a crush strength of 86.03 ± 18.10 N/cm, specific surface area of 1.958 ± 0.123 m2/g, and porosity of 64.85 ± 1.15% with a multipeak distribution at 95 ± 1.23 nm and 17.76 ± 0.14 μm. The possibility of complicated monolithic catalyst carrier structures with bionic leaf vein characters has been validated for potential industrial applications. [ABSTRACT FROM AUTHOR]

Abstract: The effects of laser sintering parameters (laser power, scan speed and hatching space) and post sintering process (heating rate, sintering temperature and holding time) on the physical and mechanical properties of porcelain components have been investigated. The study has been carried out using the Taguchi''s method for the experimental design. In the laser sintering process, lower laser energy density and higher hatching space will increase the final mechanical properties of the porcelain components. A stress relief principle has been put forward to explain the different influence of the factors. The appropriate laser sintering parameters are attained in this paper: laser power 50W; scan speed 85mm/s; and hatching space 0.6mm. Sintering temperature has been determined to be the most important factor in the post sintering process. Appropriate sintering temperature for the laser sintered porcelain bodies is in the range of 1425–1475°C regarding the mechanical properties of the porcelain components. The maximum bending strength, 34.0±4.9MPa, is reached. [Copyright &y& Elsevier]

The local properties of continuous fiber reinforced heterogeneous composites (CFRHCs) can be tailored through fiber arrangement design to maximize load and fiber utilization efficiency. Design method and integrated manufacturing process for CFRHCs have been investigated in the current research, based on 3D printing of continuous fiber reinforced composites (CFRCs). Based on the tensile and compressive properties of 3D printed CFRCs, the optimal design method of CFRHCs under process constraints and actual working conditions was studied. The mapping relationship between fiber volume content and process parameters was studied, and a digital transition from optimized design to 3D printing solutions was implemented. The flexural strength of the optimized CFRHCs is 207 MPa, and the maximum increase ratio is 115% compared with other heterogeneous designs with the same fiber volume content. The failure process of CFRHCs was analyzed by the simulation model, and the damage mechanism of CFRHCs under bending load was revealed. The optimization design and integrated manufacturing solution of the CFRHCs have potential applications in aerospace, automotive and other fields. [ABSTRACT FROM AUTHOR]

Multifunctional heat flux manipulation plays an essential role on the industrial processes. A well-designed spatial distribution of thermal conductivity enables a variety of thermal functions, including thermal cloaks and rotators. Despite the promising potential of metamaterials in achieving multifunctional heat transfer in complex nonconformal geometries, significant challenges remain due to limitations in design methods. In this work, a novel approach based on conformal discretization was proposed to address these major challenges, in which the thermal conductivity tensors of discrete functional cells were diagonalized with the local thermal conductivity tensors as inputs. To verify the effectiveness of the conformal discretization, a nonconformal thermal rotating cloak was designed and manufactured. Both simulations and experiments confirmed the effectiveness of this approach in obtaining multifunctional thermal metamaterial with remarkable thermal cloaking and rotating capabilities. Moreover, the nonconformal thermal rotating cloak still maintained thermal functionality well under the condition of omnidirectional heat flow. This work provides a feasible approach to realize multifunctional thermal manipulation in arbitrarily transformed regions, and thus shows significant application potential in the fields of aerospace engineering and civil engineering. [ABSTRACT FROM AUTHOR]