Search

In this study, biomorphic poly(dl-lactic-co-glycolic acid)/nano-hydroxyapatite (PLGA/nHA) composite scaffolds were successfully prepared using cane as a template. The porous morphology, phase, compression characteristics and in vitro biocompatibility of the PLGA/nHA composite scaffolds and biomorphic PLGA scaffolds as control were investigated. The results showed that the biomorphic scaffolds preserved the original honeycomb-like architecture of cane and exhibited a bimodal porous structure. The average channel diameter and micropore size of the PLGA/nHA composite scaffolds were 164±52μm and 13±8μm, respectively, with a porosity of 89.3±1.4%. The incorporation of nHA into PLGA decreased the degree of crystallinity of PLGA, and significantly improved the compressive modulus of biomorphic scaffolds. The in vitro biocompatibility evaluation with MC3T3-E1 cells demonstrated that the biomorphic PLGA/nHA composite scaffolds could better support cell attachment, proliferation and differentiation than the biomorphic PLGA scaffolds. The localization depth of MC3T3-E1 cells within the channels of the biomorphic PLGA/nHA composite scaffolds could reach approximately 400μm. The results suggested that the biomorphic PLGA/nHA composite scaffolds were promising candidates for bone tissue engineering. [ABSTRACT FROM AUTHOR]

An ideal scaffold in bone tissue-engineering strategy should provide biomimetic extracellular matrix-like architecture and biological properties. Poly(γ-benzyl-L-glutamate) (PBLG) has been a popular model polypeptide for various potential biomedical applications due to its good biocompatibility and biodegradability. This study developed novel bimodal porous PBLG polypeptide scaffolds via a combination of biotemplating method and in situ ring-opening polymerization of γ-benzyl-L-gIutamate N-carboxyanhydride (BLG-NCA). The PBLG scaffolds were characterized by proton nuclear magnetic resonance spectroscopy, X-ray diffraction, differential scanning calorimetry, scanning electron microscope (SEM) and mechanical test. The results showed that the semi-crystalline PBLG scaffolds exhibited an anisotropic porous structure composed of honeycomb-like channels (100–200μm in diameter) and micropores (5–20μm), with a very high porosity of 97.4±1.6%. The compressive modulus and glass transition temperature were 402.8±20.6 kPa and 20.2°C, respectively. The in vitro biocompatibility evaluation with MC3T3-E1 cells using SEM, fluorescent staining and MTT assay revealed that the PBLG scaffolds had good biocompatibility and favored cell attachment, spread and proliferation. Therefore, the bimodal porous polypeptide scaffolds are promising for bone tissue engineering. [ABSTRACT FROM AUTHOR]

Hydrogels fabricated from natural polysaccharides may serve as ideal scaffolds for tissue engineering because of their similarity to the extracellular matrices. In this study, novel hydrogel scaffolds with bubble-like porous structure were prepared from hydroxyethyl chitosan (HECS) and cellulose (CEL) by a combination of chemical crosslinking, particle-leaching using silicon dioxide particles as porogen and freeze-drying method. The morphology, compression stress-strain curves, wettability, and swelling and rheological behaviors of the HECS/CEL scaffolds were characterized by SEM, mechanical test, contact angle measurement and rheometer. HECS/CEL scaffolds had good comprehensive performances and could reach equilibrium swelling state in water within 20s. The results from in vitro biocompatibility evaluated using SEM, live/dead cell viability and MTT assays demonstrated that the HECS/CEL scaffolds could well support the attachment, spreading and proliferation of osteoblastic MC3T3-E1 cells and showed good biocompatibility. Therefore, the novel HECS/CEL scaffolds may be promising for bone tissue engineering applications. [ABSTRACT FROM AUTHOR]

Though much progress in utilizing tissue engineering technology to investigate tumor development in vitro has been made, the effective management of human melanoma is still a challenge in clinic due to lack of suitable 3D culture systems. In this study, we prepared a poly(γ-benzyl- l -glutamate)/poly(lactic acid) (PBLG/PLA) nanofiber membrane by electrospinning and demonstrated its suitability as a matrix for 3D culture of melanoma cells in vitro . The electrospun PBLG/PLA nanofiber membrane displayed a smooth and uniform fibrous morphology and had a desirable water contact angle of 79.3 ± 0.6°. The average diameter of PBLG/PLA nanofibers was 320.3 ± 95.1 nm that was less than that (516.2 ± 163.3 nm) of pure PLA nanofibers. The addition of PBLG into PLA decreased the cold crystallization peak of PLA fibers from 93 to 75 °C. The in vitro biocompatibility of PBLG/PLA nanofiber membrane was evaluated with B16F10 cells using PLA nanofiber membrane as control. It was found that, compared to PLA nanofiber membrane, PBLG/PLA nanofiber membrane could better support cell viability and proliferation, as indicated by MTT assay and live-dead staining. SEM results revealed that PBLG/PLA rather than PLA nanofiber membrane promoted the generation of tumoroid-like structures. These findings clearly demonstrated that the electrospun PBLG/PLA nanofiber membrane could mimick the extracellular matrix of melanoma microenvironment and be a promising platform for 3D cell culture. [ABSTRACT FROM AUTHOR]

In this study, novel poly(γ-benzyl l -glutamate)/poly(lactic- co -glycolic acid)/bioglass (PBLG/PLGA/BG) composite scaffolds with different weight ratios were fabricated using a negative NaCl-templating method. The morphology, compression modulus and degradation kinetics of the scaffolds were characterized. The results showed that the PBLG/PLGA/BG composite scaffolds with a weight ratio of 5:5:1, namely PBLG5PLGA5BG composite scaffolds, displayed a pore size range of 50–500 μm, high compressive modulus (566.6 ± 8.8 kPa), suitable glass transition temperature (46.8 ± 0.2 °C) and low degradation rate (> 8 weeks). The in vitro biocompatibility of the scaffolds was evaluated with MC3T3-E1 cells by live-dead staining, MTT and ALP activity assays. The obtained results indicated that the PBLG5PLGA5BG composite scaffolds were more conducive to the adhesion, proliferation and osteoblastic differentiation of MC3T3-E1 cells than PBLG and PBLG/PLGA composite scaffolds. The in vivo biocompatibility of the scaffolds was evaluated in both SD rat subcutaneous model and rabbit tibia defect model. The results of H&E, Masson's trichrome and CD34 staining assays demonstrated that the PBLG5PLGA5BG composite scaffolds allowed the ingrowth of tissue and microvessels more effectively than PBLG/PLGA composite scaffolds. The results of digital radiography confirmed that the PBLG5PLGA5BG composite scaffolds significantly improved in vivo osteogenesis. Collectively, the PBLG5PLGA5BG composite scaffolds could be a promising candidate for tissue engineering applications. [ABSTRACT FROM AUTHOR]