The detailed mechanism of electronic bipolar resistance switching (BRS) in the Pt/TiO2/Pt structure was examined. The conduction mechanism analysis showed that the trap-free and trap-mediated space-charge-limited conduction (SCLC) governs the low and high resistance state of BRS, respectively. The SCLC was confirmed by fitting the current-voltage characteristics of low and high resistance states at various temperatures. The BRS behavior originated from the asymmetric potential barrier for electrons escaping from, and trapping into, the trap sites with respect to the bias polarity. This asymmetric potential barrier was formed at the interface between the trap layer and trap-free layer. The detailed parameters such as trap density, and trap layer and trap-free layer thicknesses in the electronic BRS were evaluated. This showed that the degradation in the switching performance could be understood from the decrease and modified distribution of the trap densities in the trap layer. [ABSTRACT FROM AUTHOR]

We report the observation of two resistance switching modes in certain 50 nm x 50 nm crossbar TiO2 memristive devices that have been electroformed with a low-current process. The two switching modes showed opposite switching polarities. The intermediate state was shared by both modes (the ON state of the high-resistance mode or the OFF state of the low-resistance mode) and exhibited a relaxation to a more resistive state, including an initial transient decay. The activation energies of such a decay and ON-switching to the intermediate state were determined to be 50-210 meV and 1.1 eV, respectively. Although they are attributed to the coexistence of charge trapping and ionic motion, the ionic motion dominates in both switching modes. Our results indicate that the two switching modes in our system correspond to different switching layers adjacent to the interfaces at the top and bottom electrodes. [ABSTRACT FROM AUTHOR]