Search

In the present study, supercritical solvent impregnation (SSI) has been applied to incorporate thymol into bio-composite polymers as a potential active packaging material. Thymol, a natural component with a proven antimicrobial activity, was successfully impregnated into starch-chitosan (SC) and starch-chitosan-zeolite (SCZ) films using supercritical carbon dioxide (scCO(2)) as a solvent. Experiments were performed at 35 degrees C, pressures of 15.5 and 30 MPa, and an impregnation time in the range of 4-24 h. The highest impregnation yields of SC films with starch to chitosan mass ratios of 1:1 and 1:2 were 10.80% and 6.48%, respectively. The addition of natural zeolite (15-60%) significantly increased the loading capacity of films enabling thymol incorporation in a quantity of 16.7-27.3%. FTIR and SEM analyses were applied for the characterization of the films. Mechanical properties and water vapor permeability of films before and after the impregnation were tested as well. Thymol release kinetics in deionized water was followed and modeled by the Korsmeyer-Peppas and Weibull model. SCZ films with thymol loading of approximately 24% exhibited strong antibacterial activity against E. coli and methicillin-resistant Staphylococcus (S.) aureus (MRSA).

In the present study, supercritical solvent impregnation (SSI) has been applied to incorporate thymol into bio-composite polymers as a potential active packaging material. Thymol, a natural component with a proven antimicrobial activity, was successfully impregnated into starch-chitosan (SC) and starch-chitosan-zeolite (SCZ) films using supercritical carbon dioxide (scCO(2)) as a solvent. Experiments were performed at 35 degrees C, pressures of 15.5 and 30 MPa, and an impregnation time in the range of 4-24 h. The highest impregnation yields of SC films with starch to chitosan mass ratios of 1:1 and 1:2 were 10.80% and 6.48%, respectively. The addition of natural zeolite (15-60%) significantly increased the loading capacity of films enabling thymol incorporation in a quantity of 16.7-27.3%. FTIR and SEM analyses were applied for the characterization of the films. Mechanical properties and water vapor permeability of films before and after the impregnation were tested as well. Thymol release kinetics in deionized water was followed and modeled by the Korsmeyer-Peppas and Weibull model. SCZ films with thymol loading of approximately 24% exhibited strong antibacterial activity against E. coli and methicillin-resistant Staphylococcus (S.) aureus (MRSA).

In the present study, supercritical solvent impregnation (SSI) has been applied to incorporate thymol into bio-composite polymers as a potential active packaging material. Thymol, a natural component with a proven antimicrobial activity, was successfully impregnated into starch-chitosan (SC) and starch-chitosan-zeolite (SCZ) films using supercritical carbon dioxide (scCO(2)) as a solvent. Experiments were performed at 35 degrees C, pressures of 15.5 and 30 MPa, and an impregnation time in the range of 4-24 h. The highest impregnation yields of SC films with starch to chitosan mass ratios of 1:1 and 1:2 were 10.80% and 6.48%, respectively. The addition of natural zeolite (15-60%) significantly increased the loading capacity of films enabling thymol incorporation in a quantity of 16.7-27.3%. FTIR and SEM analyses were applied for the characterization of the films. Mechanical properties and water vapor permeability of films before and after the impregnation were tested as well. Thymol release kinetics in deionized water was followed and modeled by the Korsmeyer-Peppas and Weibull model. SCZ films with thymol loading of approximately 24% exhibited strong antibacterial activity against E. coli and methicillin-resistant Staphylococcus (S.) aureus (MRSA).