CoCrCuFeMnNix (x = 0, 0.5, 1.0, 1.5, 2.0 mol, named as Ni0, Ni0.5, Ni1.0, Ni1.5, and Ni2.0, respectively) high-entropy alloy powders (HEAPs) were prepared via mechanical alloying (MA), and XRD, SEM, EDS, and vacuum annealing were used to study the alloying behavior, phase transition, and thermal stability. The results indicated that the Ni0, Ni0.5, and Ni1.0 HEAPs were alloyed at the initial stage (5–15 h), the metastable BCC + FCC two-phase solid solution structure was formed, and the BCC phase disappeared gradually with the prolonging of ball milling time. Finally, a single FCC structure was formed. Both Ni1.5 and Ni2.0 alloys with high nickel content formed a single FCC structure during the whole mechanical alloying process. The five kinds of HEAPs showed equiaxed particles in dry milling, and the particle size increased with an increase in milling time. After wet milling, they changed into lamellar morphology with thickness less than 1 μm and maximum size less than 20 μm. The composition of each component was close to its nominal composition, and the alloying sequence during ball milling was Cu→Mn→Co→Ni→Fe→Cr. After vacuum annealing at 700~900 °C, the FCC phase in the HEAPs with low Ni content transformed into FCC2 secondary phase, FCC1 primary phase, and a minor σ phase. The thermal stability of HEAPs can be improved by increasing Ni content. [ABSTRACT FROM AUTHOR]

Self-assembled submicron nickel particles were successfully synthesized via the one-step surfactant-assisted solvothermal method. The impact of surfactant and reducing agent stoichiometry is investigated in this manuscript. Different morphologies and structures of Ni particles, including flower-like nanoflakes, hydrangea-like structures, chain structures, sphere-like structures, and hollow structures were prepared through different processing conditions with two parameters such as temperature and time. Based on scanning electron microscopy (SEM), X-ray diffraction (XRD), thermal gravimetric analysis (TGA) and vibrating sample magnetometry (VSM), the submicron nickel particles show good saturation magnetization and excellent thermal stabilities with a possible growth mechanism for the variety of the structure-tuned formation. Importantly, the microwave absorption properties of the submicron nickel particles were studied. The lowest reflection loss of Ni-P9/T200/H15 with a thin layer thickness of 1.7 mm can reach -42.6 dB at 17.3 GHz. [ABSTRACT FROM AUTHOR]