We elucidate here the determining role of Nb interlayer on mechanical properties of Ti/steel clad plate fabricated by vacuum rolling cladding (VRC) as a function of different heating temperatures. A critical analysis on the clad interface via electron probe micro-analyzer, X-ray diffractometer and shear testing were conducted to investigate the influence of TiC, Fe-Nb and TiFe compounds and Nb-Ti solid solution on microstructural evolution and shear properties of Ti/steel clad plate. The inter-diffusion between Ti, C and Fe was effectively restrained by adding the Nb interlayer at heating temperature of 800 °C, and average shear strength of 279 MPa was achieved. With increase of heating temperature, Nb-Ti solid solution was formed at the Ti/Nb interface, which reduced mechanical properties of clad plate at 900 °C. At 1000 °C, TiC and Nb-Fe compounds and Nb-Ti solid solution were formed at the interface, and minimum average shear strength of 152 MPa was achieved. The detailed analysis on the clad interface suggested that ideal shear strength can be obtained through the addition of Nb interlayer and selecting appropriate heating temperature. [ABSTRACT FROM AUTHOR]

In this study, the impact of different surface treatment and degree of vacuum on the interface and mechanical properties of 304/Q345 stainless steel clad plate was investigated. The study indicated that more continuous or aggregated Al2O3 and Si-Mn composite oxides were formed at the interface after brush grinding. However, less inclusions such as Al2O3, MnS and Ca-Mg-Al-Si composite oxides were formed at the interface after pickling treatment. For the vacuum degrees of 10−2 Pa, 1 Pa and 105 Pa, the oxidation reaction became more intense with the decrease in vacuum degree. The interface inclusions were gradually changed from Al2O3 and Si-Mn complex oxides to oxide scale and MnCr2O4 spinel oxide. The interfacial bonding strength of stainless steel clad plate was improved with the increase in degree of vacuum. The bonding strength was 55 MPa at vacuum of 105 Pa, but it was 484 MPa at vacuum of 10−2 Pa, which is far greater than that of the national standard, and an excellent performance was obtained. [ABSTRACT FROM AUTHOR]